Stress-assisted hydrogen diffusion analysis was performed on arc-shaped tension specimen (C-specimen) fabricated from Type 21-6-9 stainless steel. Two-dimensional finite element method was applied for the determination of elastic-plastic crack front stress fields, which was later coupled with hydrogen diffusion analyses. The extension of Fick's rule was used as the governing equation for the diffusion analysis. The distributions of hydrogen concentration were compared under various Internal Hydrogen Embrittlement (IHE) and Hydrogen Environment Embrittlement (HEE) conditions. Without any external hydrogen pressure in IHE conditions, the increment of hydrogen concentration driven by the gradient of hydrostatic stress was offset by the out-gasing driven by gradient of hydrogen concentration at the crack front region. As the hydrogen pressure increases, the hydrogen concentration at the crack front region becomes dominant and show peak value around the crack tip. Compared with the results of IHE cases, the hydrogen concentrations in HEE conditions could reach the level of steady state in a relatively short time which is attributed to the high solubility and diffusivity of the material at high temperature.Copyright © 2006 by ASME
[1]
M. Pechersky,et al.
On the Effect of Hydrogen on the Fracture Toughness of Steel
,
2005
.
[2]
M. J. Pechersky,et al.
C-Specimen Fracture Toughness Testing: Effect of Side Grooves and η Factor
,
2004
.
[3]
J. E. Perez Ipiña,et al.
In situ crack growth observation and fracture toughness measurement of hydrogen charged Zircaloy-4
,
2003
.
[4]
D. Symons.
A comparison of internal hydrogen embrittlement and hydrogen environment embrittlement of X-750
,
2001
.
[5]
G. Pressouyre,et al.
Current solutions to hydrogen problems in steels : proceedings of the First International Conference on Current Solutions to Hydrogen Problems in Steels, Washington DC, November 1-5, 1982
,
1982
.
[6]
H. W. Liu.
Stress-Corrosion Cracking and the Interaction Between Crack-Tip Stress Field and Solute Atoms
,
1970
.