论文信息 - The effect of biological environment on the surface of titanium and plasma-sprayed layer of hydroxylapatite

The effect of biological environment on the surface of titanium and plasma-sprayed layer of hydroxylapatite

The solubility of titanium samples with different surface coatings, i.e., hydroxylapatite (HA) powders, a two-layer coating of ZrO5+HA on a titanium substrate in solution and of tooth implants after long-term functioning in the human organism, was studied. A minimum difference in solubility of titanium samples with different surface finishes (polished or grit blasted) was established. For the HA powders and coatings, the lowest solubility was observed with a coarse-grained HA–B powder and a coating made of that powder. Clinical tests of tooth implants after long implantation times were performed. A titanium implant (implantation 12 y), a titanium implant with a two-layer coating of ZrO5+HA–A (implantation time 4 y) and a titanium implant with a two-layer coating of Al5O3+3% TiO2)+ HA–A (implantation time 6 y) were studied. The results show that the titanium surface and HA–A layers were dissolved. Nevertheless, after 6 y implantation, total removal of HA–A coating from that part of implant set into the bone, was not observed.

[1] C. Klein,et al. Studies of the solubility of different calcium phosphate ceramic particles in vitro. , 1990, Biomaterials.

[2] K. Donath,et al. Interface between bone tissue and implants of solid hydroxyapatite or hydroxyapatite-coated titanium implants. , 1989, Biomaterials.

[3] H. Saalfeld,et al. Solubility behaviour of synthetic hydroxyapatites in aqueous solution: influence of amorphous constituents on pH value. , 1994, Biomaterials.