Fabrication of porous carbonate apatite granules using microfiber and its histological evaluations in rabbit calvarial bone defects.

Carbonate apatite (CO3 Ap) granules are known to show good osteoconductivity and replaced to new bone. On the other hand, it is well known that a porous structure allows bone tissue to penetrate its pores, and the optimal pore size for bone ingrowth is dependent on the composition and structure of the scaffold material. Therefore, the aim of this study was to fabricate various porous CO3 Ap granules through a two-step dissolution-precipitation reaction using CaSO4 as a precursor and 30-, 50-, 120-, and 205-μm diameter microfibers as porogen and to find the optimal pore size of CO3 Ap. Porous CO3 Ap granules were successfully fabricated with pore size 8.2-18.7% smaller than the size of the original fiber porogen. Two weeks after the reconstruction of rabbit calvarial bone defects using porous CO3 Ap granules, the largest amount of mature bone was seen to be formed inside the pores of CO3 Ap (120) [porous CO3 Ap granules made using 120-μm microfiber] followed by CO3 Ap (50) and CO3 Ap (30). At 4 and 8 weeks, no statistically significant difference was observed based on the pore size, even though largest amount of mature bone was formed in case of CO3 Ap (120). It is concluded, therefore, that the optimal pore size of the CO3 Ap is that of CO3 Ap (120), which is 85 μm. This article is protected by copyright. All rights reserved.