论文信息 - Comparison of the corrosion behavior of austenitic and ferritic/martensitic steels exposed to static liquid Pb-Bi at 450 and 550 °C

Comparison of the corrosion behavior of austenitic and ferritic/martensitic steels exposed to static liquid Pb-Bi at 450 and 550 °C

Abstract Static corrosion tests of various steels were conducted in oxygen-saturated liquid Pb–Bi eutectic at 450 °C and 550 °C for 3000 h to study the effects of temperature and alloying elements on corrosion behavior in liquid Pb–Bi. Corrosion depth decreases at 450 °C with increasing Cr content in steels regardless of ferritic/martensitic steels or austenitic steels. Appreciable dissolution of Ni and Cr does not occur in the three austenitic steels at 450 °C. Corrosion depth of ferritic/martensitic steels also decreases at 550 °C with increasing Cr content in steels whereas corrosion depth of austenitic steels, JPCA and 316SS becomes larger due to ferritization caused by dissolution of Ni at 550 °C than that of ferritic/martensitic steels. An austenitic stainless steel containing about 5%Si exhibits fine corrosion resistance at 550 °C because the protective Si oxide film is formed and prevents dissolution of Ni and Cr.

[1] Thomas J McManamy,et al. Overview of the Spallation Neutron Source (SNS) with emphasis on target systems , 2003 .

[2] C. Fazio,et al. Compatibility tests of steels in flowing liquid lead–bismuth , 2001 .

[3] G. Benamati,et al. Compatibility tests on steels in molten lead and lead-bismuth , 2001 .

[4] Frank Zimmermann,et al. Results of steel corrosion tests in flowing liquid Pb/Bi at 420-600 °C after 2000 h , 2002 .

[5] Carlo Rubbia,et al. Conceptual design of a fast neutron operated high power energy amplifier , 1995 .

[6] Frank Zimmermann,et al. Investigation on oxygen controlled liquid lead corrosion of surface treated steels , 2000 .

[7] T. Ogawa,et al. Review of research and development of accelerator-driven system in Japan for transmutation of long-lived nuclides , 2001 .

[8] G. Benamati,et al. Temperature effect on the corrosion mechanism of austenitic and martensitic steels in lead–bismuth , 2002 .

[9] S. Saito,et al. Corrosion–erosion test of SS316 in flowing Pb–Bi , 2003 .

[10] S. Saito,et al. Corrosion studies in liquid Pb–Bi alloy at JAERI: R & D program and first experimental results , 2002 .

[11] J. R. Weeks,et al. Lead, bismuth, tin and their alloys as nuclear coolants☆ , 1971 .

[12] A. Rusanov,et al. Corrosion behavior of steels in flowing lead–bismuth , 2001 .

[13] J. Robertson,et al. Healing layer formation in Fe–Cr–Si ferritic steels , 1989 .