论文信息 - Structure, properties and application of a novel low-glossed waterborne polyurethane

Structure, properties and application of a novel low-glossed waterborne polyurethane

Abstract Waterborne polyurethane (WPU) with low gloss was prepared successfully and used as surface modifier to adjust the gloss of leather. The structure and morphology of the WPU films were characterized by Fourier transform infrared spectrometer (FTIR), Atomic force microscope (AFM) and Scanning electron microscope (SEM). Then the factors affecting the gloss, light transmittance and water absorption of WPU films including varieties and amount of chain extenders, nNCO/nOH molar ratio and 2-[(2-aminoethyl)amino]ethyl sulfonic acid sodium content.etc were studied. Results showed that the WPU film possessed a broad particle size distribution combined with a relatively large particle size. This kind of novel WPU would be widely used in polyvinyl chloride, polyurethane synthetic leather surface.

[1] Hongyan Wang,et al. Synthesis and characterization of core-shell LIPN-fluorine-containing polyacrylate latex , 2007 .

[2] G. Tang,et al. Effect of Particle Size Distribution of Calcined Diatomites on the Extinction Performance , 2011 .

[3] Zhang Zhe. Principle and Synthesis of Leather Matting Finishing Agent , 2007 .

[4] Xingyuan Zhang,et al. Effect of the hard segment on the properties of UV curable waterborne blocked polyurethanes , 2008 .

[5] K. Kim,et al. Synthesis and characterizations of waterborne polyurethane–silica hybrids using sol–gel process , 2007 .

[6] C. Cao,et al. Blood compatibility of polyurethane immobilized with acrylic acid and plasma grafting sulfonic acid , 2004, Journal of materials science. Materials in medicine.

[7] Zhengxing Qin,et al. Preparation and characterization of the waterborne polyurethane modified with nanosilica , 2009 .

[8] T. Fletcher. A simple model to describe relationships between gloss behaviour, matting agent concentration and the rheology of matted paints and coatings , 2002 .