Effect of Curing Water Availability and Composition on Cement Hydration

Curing can help concrete reach its full strength and durability potential. The effect of sealing the concrete with plastic or formwork, use of a liquid curing compound, wet curing, and internal curing with saturated lightweight aggregates on the cement degree of hydration (DOH) development with time was examined using isothermal calorimetry. Curing water amount, curing water ionic concentration, and sample thickness were varied. Finally, curing application timing was studied by comparing strength development of concrete cylinders sealed, placed in a moist room after 24 hours sealed, and immersed in a water bath immediately after finishing. Increasing the height of curing water decreased the height of heat of hydration rate peaks. Curing water ionic concentration affected the setting time and heat of hydration rate peak heights. Strength results show delayed curing can result in significant strength loss because of the difficulty for water to penetrate the already-hardened concrete.

[1]  E. Lachowski,et al.  Clinker Mineral Hydration at Reduced Relative Humidities , 1999 .

[2]  Gilles Chanvillard,et al.  Determining the apparent activation energy of concrete Ea: numerical simulations of the heat of hydration of cement , 2002 .

[3]  K. Folliard,et al.  Heat of Hydration Models for Cementitious Materials , 2005 .

[4]  Tommy Nantung,et al.  Volume change and cracking in internally cured mixtures made with saturated lightweight aggregate under sealed and unsealed conditions , 2009 .

[5]  P Klieger,et al.  EARLY HIGH-STRENGTH CONCRETE FOR PRESTRESSING , 1969 .

[6]  Walter H. Price,et al.  Factors influencing concrete strength , 1950, Materiales de Construcción.

[7]  T. Powers,et al.  A DISCUSSION OF CEMENT HYDRATION IN RELATION TO THE CURING OF CONCRETE , 1948 .

[8]  B. Duthoit,et al.  Conception of an isothermal calorimeter for concrete— Determination of the apparent activation energy , 2002 .

[9]  P. Freiesleben Hansen,et al.  AUTOGENOUS DEFORMATION AND CHANGE OF THE RELATIVE HUMIDITY IN SILICA FUME-MODIFIED CEMENT PASTE , 1996 .

[10]  D. Bentz,et al.  Curing, Hydration, and Microstructure of Cement Paste , 2006 .

[11]  B. Duthoit,et al.  Determination of apparent activation energy of concrete by isothermal calorimetry , 2000 .

[12]  Hans W. Reinhardt,et al.  A New Generation of High Performance Concrete: Concrete with Autogenous Curing , 1997 .

[13]  K. Kovler,et al.  Novel Techniques for Concrete Curing , 2005 .

[14]  Luc Taerwe,et al.  Degree of hydration-based description of mechanical properties of early age concrete , 1996 .

[15]  T. L. Brownyard,et al.  Studies of the Physical Properties of Hardened Portland Cement Paste , 1946 .

[16]  Pietro Lura,et al.  Mixture Proportioning for Internal Curing , 2005 .

[17]  Verbeck,et al.  Chemistry of Hydration of Portland Cement , 2022 .

[18]  F. Winnefeld,et al.  Simultaneous measurements of heat of hydration and chemical shrinkage on hardening cement pastes , 2010 .

[19]  Ines Jaouadi.  Étude numérique et expérimentale du retrait endogène de la pâte de ciment au jeune âge , 2008 .

[20]  O. Jensen,et al.  Water-entrained cement-based materials: II. Experimental observations , 2002 .

[21]  Zachary C. Grasley.  Measuring and Modeling the Time-Dependent Response of Cementitious Materials to Internal Stresses , 2006 .

[22]  Per Freiesleben Hansen,et al.  Water-entrained cement-based materials , 2001 .

[23]  B. Mather.  "Self-Curing Concrete, Why Not?" , 2004, SP-223: Investigating Concrete-Selected Works of Bryant and Katharine Mather.

[24]  L. Wadsö.  Operational issues in isothermal calorimetry , 2010 .