ZIF-derived in situ nitrogen-doped porous carbons as efficient metal-free electrocatalysts for oxygen reduction reaction

We have successfully prepared nanoporous Carbon-L and -S materials by using ZIF-7 as a precursor and glucose as an additional carbon source. Results indicate that Carbon-L and -S show an appropriate nitrogen content, high surface area, robust pore structure and excellent graphitization degree. The addition of an environmentally friendly carbon source – glucose – not only improves the graphitization degree of samples, but also plays a key role in removing residual Zn metal and zinc compound impurities, which makes the resulting materials metal-free in situ nitrogen-doped porous carbons. By further investigating the electrocatalytic performance of these nitrogen-doped porous carbons for oxygen reduction reaction (ORR), we find that Carbon-L, as a metal-free electrocatalyst, shows excellent electrocatalytic activity (the onset and half-wave potentials are 0.86 and 0.70 V vs. RHE, respectively) and nearly four electron selectivity (the electron transfer number is 3.68 at 0.3 V), which is close to commercial 20% Pt/C. Moreover, when methanol was added, the Pt/C catalyst would be poisoned while the Carbon-L and -S would be unaffected. By exploring the current-time chronoamperometric response in 25 000 s, we found that the duration stability of Carbon-L is much better than the commercial 20% Pt/C. Thus, both Carbon-L and -S exhibit excellent ability to avoid methanol crossover effects, and long-term operation stability superior to the Pt/C catalyst. This work provides a new strategy for in situ synthesis of N-doped porous carbons as metal-free electrocatalysts for ORR in fuel cells.

[1]  Sheng Ye,et al.  Magnetic porous carbons with high adsorption capacity synthesized by a microwave-enhanced high temperature ionothermal method from a Fe-based metal-organic framework , 2013 .

[2]  Z. Shao,et al.  Nitrogen-doped carbon nanotubes derived from Zn–Fe-ZIF nanospheres and their application as efficient oxygen reduction electrocatalysts with in situ generated iron species , 2013 .

[3]  D. Cao,et al.  Covalent organic polymer supported palladium catalysts for CO oxidation. , 2013, Chemical communications.

[4]  Qiang Xu,et al.  Metal–organic frameworks as platforms for clean energy , 2013 .

[5]  Z. Tang,et al.  Molecular architecture of cobalt porphyrin multilayers on reduced graphene oxide sheets for high-performance oxygen reduction reaction. , 2013, Angewandte Chemie.

[6]  Seung Jae Yang,et al.  Preparation and exceptional lithium anodic performance of porous carbon-coated ZnO quantum dots derived from a metal-organic framework. , 2013, Journal of the American Chemical Society.

[7]  Liquan Chen,et al.  Sulfur in hierarchically pore-structured carbon pillars as cathode material for lithium–sulfur batteries , 2013 .

[8]  Zhenyu Liu,et al.  One-step scalable preparation of N-doped nanoporous carbon as a high-performance electrocatalyst for the oxygen reduction reaction , 2013, Nano Research.

[9]  Jinpeng Han,et al.  Sulfur embedded in metal organic framework-derived hierarchically porous carbon nanoplates for high performance lithium–sulfur battery , 2013 .

[10]  Hailiang Wang,et al.  Strongly coupled inorganic-nano-carbon hybrid materials for energy storage. , 2013, Chemical Society reviews.

[11]  Yuichiro Kamachi,et al.  Facile synthesis of nanoporous carbons with controlled particle sizes by direct carbonization of monodispersed ZIF-8 crystals. , 2013, Chemical communications.

[12]  Shaojun Dong,et al.  Recent progress in graphene-based nanomaterials as advanced electrocatalysts towards oxygen reduction reaction. , 2013, Nanoscale.

[13]  D. Cao,et al.  Porous covalent–organic materials: synthesis, clean energy application and design , 2013 .

[14]  R. Banerjee,et al.  Porous-organic-framework-templated nitrogen-rich porous carbon as a more proficient electrocatalyst than Pt/C for the electrochemical reduction of oxygen. , 2013, Chemistry.

[15]  K. Ariga,et al.  A new family of carbon materials: synthesis of MOF-derived nanoporous carbons and their promising applications , 2013 .

[16]  Liangti Qu,et al.  A versatile, ultralight, nitrogen-doped graphene framework. , 2012, Angewandte Chemie.

[17]  Zheng Hu,et al.  Nitrogen‐Doped Carbon Nanocages as Efficient Metal‐Free Electrocatalysts for Oxygen Reduction Reaction , 2012, Advanced materials.

[18]  Dan Zhao,et al.  Iron imidazolate framework as precursor for electrocatalysts in polymer electrolyte membrane fuel cells , 2012 .

[19]  G. Shi,et al.  Graphene based catalysts , 2012 .

[20]  R. Banerjee,et al.  Control of porosity by using isoreticular zeolitic imidazolate frameworks (IRZIFs) as a template for porous carbon synthesis. , 2012, Chemistry.

[21]  Jyoti Jog,et al.  MOF derived porous carbon–Fe3O4 nanocomposite as a high performance, recyclable environmental superadsorbent , 2012 .

[22]  Liang Jiang,et al.  Mesoporous graphitic carbon nanodisks fabricated via catalytic carbonization of coordination polymers. , 2012, Chemical communications.

[23]  D. Cao,et al.  Synthesis of luminescent covalent-organic polymers for detecting nitroaromatic explosives and small organic molecules. , 2012, Macromolecular rapid communications.

[24]  K. Ariga,et al.  Nanoporous carbons through direct carbonization of a zeolitic imidazolate framework for supercapacitor electrodes. , 2012, Chemical communications.

[25]  Mark K. Debe,et al.  Electrocatalyst approaches and challenges for automotive fuel cells , 2012, Nature.

[26]  Wenming Qiao,et al.  Synthesis of 3D hierarchical porous carbon as electrode material for electric double layer capacitors , 2012 .

[27]  Katsuhiko Ariga,et al.  Direct carbonization of Al-based porous coordination polymer for synthesis of nanoporous carbon. , 2012, Journal of the American Chemical Society.

[28]  Yern Seung Kim,et al.  MOF-Derived Hierarchically Porous Carbon with Exceptional Porosity and Hydrogen Storage Capacity , 2012 .

[29]  R. Mokaya,et al.  Preparation and hydrogen storage capacity of templated and activated carbons nanocast from commercially available zeolitic imidazolate framework , 2012 .

[30]  A. Filoramo,et al.  Catalytic activity of cobalt and iron phthalocyanines or porphyrins supported on different carbon nanotubes towards oxygen reduction reaction , 2011 .

[31]  Tom Regier,et al.  Co₃O₄ nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. , 2011, Nature materials.

[32]  Juan Herranz,et al.  Iron-based cathode catalyst with enhanced power density in polymer electrolyte membrane fuel cells. , 2011, Nature communications.

[33]  J. Baek,et al.  Polyelectrolyte-functionalized graphene as metal-free electrocatalysts for oxygen reduction. , 2011, ACS nano.

[34]  Tomoki Akita,et al.  From metal-organic framework to nanoporous carbon: toward a very high surface area and hydrogen uptake. , 2011, Journal of the American Chemical Society.

[35]  Klaus Müllen,et al.  Graphene-based carbon nitride nanosheets as efficient metal-free electrocatalysts for oxygen reduction reactions. , 2011, Angewandte Chemie.

[36]  Gang Wu,et al.  High-Performance Electrocatalysts for Oxygen Reduction Derived from Polyaniline, Iron, and Cobalt , 2011, Science.

[37]  D. Cao,et al.  Zeolitic imidazolate framework-8 as a luminescent material for the sensing of metal ions and small molecules , 2011 .

[38]  Bruno Jousselme,et al.  Low-platinum and platinum-free catalysts for the oxygen reduction reaction at fuel cell cathodes , 2011 .

[39]  Ann V. Call,et al.  Cobalt imidazolate framework as precursor for oxygen reduction reaction electrocatalysts. , 2011, Chemistry.

[40]  Wenchuan Wang,et al.  Metal-organic frameworks with incorporated carbon nanotubes: improving carbon dioxide and methane storage capacities by lithium doping. , 2011, Angewandte Chemie.

[41]  Qiang Zhang,et al.  Highly efficient metal-free growth of nitrogen-doped single-walled carbon nanotubes on plasma-etched substrates for oxygen reduction. , 2010, Journal of the American Chemical Society.

[42]  G. Goenaga,et al.  New Approaches to Non-PGM Electrocatalysts Using Porous Framework Materials , 2010 .

[43]  Huanlei Wang,et al.  Porous carbons prepared by using metal–organic framework as the precursor for supercapacitors , 2010 .

[44]  Seizo Miyata,et al.  Pt-free cathode catalysts prepared via multi-step pyrolysis of Fe phthalocyanine and phenolic resin for fuel cells. , 2010, Chemical communications.

[45]  B. Smit,et al.  Doping of alkali, alkaline-earth, and transition metals in covalent-organic frameworks for enhancing CO2 capture by first-principles calculations and molecular simulations. , 2010, ACS nano.

[46]  Fangyi Liang,et al.  Zeolitic imidazolate framework ZIF-7 based molecular sieve membrane for hydrogen separation , 2010 .

[47]  K. Müllen,et al.  Nitrogen-doped ordered mesoporous graphitic arrays with high electrocatalytic activity for oxygen reduction. , 2010, Angewandte Chemie.

[48]  Y. Liu,et al.  Nitrogen-doped graphene as efficient metal-free electrocatalyst for oxygen reduction in fuel cells. , 2010, ACS nano.

[49]  Xin-bo Zhang,et al.  Metal–organic framework (MOF) as a template for syntheses of nanoporous carbons as electrode materials for supercapacitor , 2010 .

[50]  W. Schuhmann,et al.  Electrocatalytic Activity and Stability of Nitrogen-Containing Carbon Nanotubes in the Oxygen Reduction Reaction , 2009 .

[51]  Wenchuan Wang,et al.  Lithium-doped 3D covalent organic frameworks: high-capacity hydrogen storage materials. , 2009, Angewandte Chemie.

[52]  Younan Xia,et al.  Pd-Pt Bimetallic Nanodendrites with High Activity for Oxygen Reduction , 2009, Science.

[53]  N. Xia,et al.  Worm-like mesoporous carbon synthesized from metal―organic coordination polymers for supercapacitors , 2009 .

[54]  Frédéric Jaouen,et al.  Iron-Based Catalysts with Improved Oxygen Reduction Activity in Polymer Electrolyte Fuel Cells , 2009, Science.

[55]  F. Du,et al.  Nitrogen-Doped Carbon Nanotube Arrays with High Electrocatalytic Activity for Oxygen Reduction , 2009, Science.

[56]  D. Su,et al.  Dynamic surface rearrangement and thermal stability of nitrogen functional groups on carbon nanotubes. , 2008, Chemical communications.

[57]  T. Akita,et al.  Metal-organic framework as a template for porous carbon synthesis. , 2008, Journal of the American Chemical Society.

[58]  Yuyan Shao,et al.  Nitrogen-doped carbon nanostructures and their composites as catalytic materials for proton exchange membrane fuel cell , 2008 .

[59]  M. Mavrikakis,et al.  Platinum Monolayer Fuel Cell Electrocatalysts , 2007 .

[60]  Siyu Ye,et al.  Recent advances in activity and durability enhancement of Pt/C catalytic cathode in PEMFC: Part II: Degradation mechanism and durability enhancement of carbon supported platinum catalyst , 2007 .

[61]  Michael O’Keeffe,et al.  Exceptional chemical and thermal stability of zeolitic imidazolate frameworks , 2006, Proceedings of the National Academy of Sciences.

[62]  Bin Wang,et al.  Recent development of non-platinum catalysts for oxygen reduction reaction , 2005 .

[63]  C. Ewels,et al.  Nitrogen doping in carbon nanotubes. , 2005, Journal of nanoscience and nanotechnology.

[64]  P. Bruce,et al.  Nanostructured materials for advanced energy conversion and storage devices , 2005, Nature materials.

[65]  M. Winter,et al.  What are batteries, fuel cells, and supercapacitors? , 2004, Chemical reviews.

[66]  M. D. Rooij,et al.  Electrochemical Methods: Fundamentals and Applications , 2003 .

[67]  Solarthermal and Solar Quasi-Electrolytic Processing and Separations: Zinc from Zinc Oxide as an Example , 1999 .

[68]  D. Guay,et al.  Influence of Nitrogen‐Containing Precursors on the Electrocatalytic Activity of Heat‐Treated Fe ( OH ) 2 on Carbon Black for O 2 Reduction , 1998 .