A pilot study of a simple photon migration model for predicting depth of cure in dental composite.

OBJECTIVES The purpose of this study was to build a photo migration model to calculate the radiant exposure (irradiancextime) in dental composite and to relate the radiant exposure with extent of cure using polymer kinetics models. METHODS A composite (Z100, Shade A2) cylinder (21 mm diameter by 15 mm deep) was cured with a tungsten-halogen lamp emitting 600 mW/cm2, 1 mm above the composite for 60s. For each of the 2x1 mm grids along the longitudinal cross section (diameter versus depth), the degree of conversion (DC) and hardness (KHN) were measured to construct the curing extent distribution. The inverse adding-doubling method was used to characterize the optical properties of the composite for the Monte Carlo model simulating the photon propagation within the composite cylinder. The calculated radiant exposure (H) distribution along the cross section was related to the curing extent DC/DC(max) distribution and fitted with two polymer curing kinetics models, the exponential model DC=DC(max)[1-exp((ln0.5)H/H(dc)(50%))] and Racz's model [Formula: see text] , where H(dc)(50%) is a fitting parameter representing the threshold for 50% of the maximum curing level. RESULTS AND SIGNIFICANCE The absorption and scattering coefficients of uncured composite were higher than that of cured composite at wavelengths between 420 and 520 nm. A roughly hemi-spheric distribution of radiant exposure in the Monte Carlo simulation result was comparable with the curing profiles determined by both DC and KHN. The relationship between DC (or KHN) and H agreed with the Racz model (r2=0.95) and the exponential model (r2=0.93). The H(dc)(50%) was 1.5(0.1), equal for the two models (P<0.05). The estimated radiant exposure threshold for 80% of the maximum curing level was between 3.8 and 8.8 J/cm2. The simulation results verify that the radiant exposure extends to a greater depth and width for composite with lower absorption and scattering coefficients. Given the optical properties and the geometry of the composite, and the spectrum and the geometry of the light source, the Monte Carlo simulation can accurately describe the radiant exposure distribution in a composite material to predict the extent of cure.

[1]  K. Jandt,et al.  High power light emitting diode (LED) arrays versus halogen light polymerization of oral biomaterials: Barcol hardness, compressive strength and radiometric properties. , 2002, Biomaterials.

[2]  J. Rabek,et al.  Kinetic studies of a new photoinitiator hybrid system based on camphorquinone-N-phenylglicyne derivatives for laser polymerization of dental restorative and stereolithographic (3D) formulations , 1996 .

[3]  Statistical estimation of resin composite polymerization sufficiency using microhardness. , 2004, Dental materials : official publication of the Academy of Dental Materials.

[4]  D. Watts.  Dental Restorative Materials , 2006 .

[5]  W. Johnston,et al.  A mathematical model for post-irradiation hardening of photoactivated composite resins. , 1985, Dental materials : official publication of the Academy of Dental Materials.

[6]  The application of magnetic resonance microimaging to the visible light curing of dental resins. Part 2. Dynamic imaging by the FLASH-MOVIE pulse sequence. , 2001, Dental materials : official publication of the Academy of Dental Materials.

[7]  J. Ferracane,et al.  Wear and Marginal Breakdown of Composites with Various Degrees of Cure , 1997, Journal of dental research.

[8]  B. Abedian,et al.  Cure kinetics of light-activated polymers , 1998 .

[9]  N. Melikechi,et al.  The effect of irradiation wavelength bandwidth and spot size on the scraping depth and temperature rise in composite exposed to an argon laser or a conventional quartz-tungsten-halogen source. , 2002, Dental materials : official publication of the Academy of Dental Materials.

[10]  M. Miyazaki,et al.  Effect of light exposure on fracture toughness and flexural strength of light-cured composites. , 1996, Dental materials : official publication of the Academy of Dental Materials.

[11]  L Wang,et al.  MCML--Monte Carlo modeling of light transport in multi-layered tissues. , 1995, Computer methods and programs in biomedicine.

[12]  J. Ferracane,et al.  Contraction Stress Related to Degree of Conversion and Reaction Kinetics , 2002 .

[13]  S. Grobler,et al.  The effect of different power densities and method of exposure on the marginal adaptation of four light-cured dental restorative materials. , 2003, Biomaterials.

[14]  S. Kanagasabay.  Safety with Lasers and Other Optical Sources—A Comprehensive Handbook , 1981 .

[15]  R. Sakaguchi,et al.  Reduced light energy density decreases post-gel contraction while maintaining degree of conversion in composites , 1998 .

[16]  K. Söderholm,et al.  How light irradiance and curing time affect monomer conversion in light-cured resin composites. , 2003, European journal of oral sciences.

[17]  K. Jandt,et al.  Photoinitiator dependent composite depth of cure and Knoop hardness with halogen and LED light curing units. , 2003, Biomaterials.

[18]  K. Jandt,et al.  Light-emitting diode (LED) polymerisation of dental composites: flexural properties and polymerisation potential. , 2000, Biomaterials.

[19]  S. A. Prahl,et al.  A Monte Carlo model of light propagation in tissue , 1989, Other Conferences.

[20]  B. Darvell,et al.  Polymerization of resin composite restorative materials: exposure reciprocity. , 2003, Dental materials : official publication of the Academy of Dental Materials.

[21]  N. Metropolis,et al.  The Monte Carlo method. , 1949 .

[22]  B. Lim,et al.  Effect of surface conditions on the color of dental resin composites. , 2002, Journal of biomedical materials research.

[23]  C. Bowman,et al.  The Effects of Light Intensity, Temperature, and Comonomer Composition on the Polymerization Behavior of Dimethacrylate Dental Resins , 1999, Journal of dental research.

[24]  C. Davidson,et al.  Energy dependent polymerization of resin-based composite. , 2002, Dental materials : official publication of the Academy of Dental Materials.

[25]  E. H. Linfoot.  Principles of Optics , 1961 .

[26]  M. Okazaki,et al.  ESR study of camphorquinone/amine photoinitiator systems using blue light-emitting diodes. , 2003, Biomaterials.

[27]  J. C. Hamilton,et al.  Effect of variable light intensity on composite shrinkage. , 2000, The Journal of prosthetic dentistry.

[28]  B. Hooper.  Optical-thermal response of laser-irradiated tissue , 1996 .

[29]  J L Ferracane,et al.  Correlation between hardness and degree of conversion during the setting reaction of unfilled dental restorative resins. , 1985, Dental materials : official publication of the Academy of Dental Materials.

[30]  W. Cook.  Spectral Distributions of Dental Photopolymerization Sources , 1982, Journal of dental research.

[31]  A. Welch,et al.  Determining the optical properties of turbid mediaby using the adding-doubling method. , 1993, Applied optics.

[32]  M. Okazaki,et al.  Studies on optical properties of two commercial visible-light-cured composite resins by diffuse reflectance measurements. , 1999, Journal of oral rehabilitation.

[33]  W. Cook.  Factors Affecting the Depth of Cure of UV -polymerized Composites , 1980, Journal of dental research.

[34]  A. Versluis,et al.  Fracture toughness and microhardness of a composite: do they correlate? , 2003, Journal of dentistry.

[35]  Maxwell H. Anderson,et al.  Annual Review of selected dental literature: report of the Committee on Scientific Investigation of the American Academy of Restorative Dentistry. , 2013, The Journal of prosthetic dentistry.

[36]  S. Jacques,et al.  Light distributions in artery tissue: Monte Carlo simulations for finite‐diameter laser beams , 1989, Lasers in surgery and medicine.

[37]  Akira Ishimaru,et al.  Wave propagation and scattering in random media , 1997 .

[38]  K. Jandt,et al.  Depth of cure and compressive strength of dental composites cured with blue light emitting diodes (LEDs). , 2000, Dental materials : official publication of the Academy of Dental Materials.

[39]  B. Wilson,et al.  A Monte Carlo model for the absorption and flux distributions of light in tissue. , 1983, Medical physics.