Effect of various mixing ratios on antibacterial properties and hardness of endodontic sealers.

Most chemically cured two-component dental materials, including endodontic sealers, are marketed with mixing instructions but with no strict mixing ratios. The present study evaluated the antibacterial properties and hardness of three endodontic sealers: Roth's cement (RC), CRCS, and AH26, mixed to four controlled consistencies within the range of the manufacturer recommendations. Using Enterococcus faecalis as the test microorganism, antibacterial activity was evaluated by agar diffusion and direct contact test. Surface hardness of sealers with the same consistency was evaluated on week-old specimens by the Knoop Hardness Number tester. In the agar diffusion test, light consistency of RC showed larger zones of inhibition than heavier consistency, whereas no significant differences were found with AH26 or CRCS. In the direct contact test, RC and CRCS exhibited complete inhibition of bacterial growth at all consistencies, whereas AH26 with the heavier consistencies did not inhibit bacterial growth at 24 h samples. The hardness of AH26 and CRCS was significantly lower with lighter consistencies. It is concluded that endodontic sealers possess different antibacterial and physical properties according to their mixing consistencies.

[1]  Z. Fuss,et al.  Antibacterial activity of calcium hydroxide-containing endodontic sealers on Enterococcus faecalis in vitro. , 1997, International endodontic journal.

[2]  Z. Fuss,et al.  In vitro antibacterial activity of a glass ionomer endodontic sealer. , 1997, Journal of endodontics.

[3]  Z. Fuss,et al.  Assessment of antibacterial activity of endodontic sealers by a direct contact test. , 1996, Endodontics & dental traumatology.

[4]  G. Sundqvist,et al.  Ecology of the root canal flora. , 1992, Journal of endodontics.

[5]  M. T. Jiménez de Anta,et al.  Antimicrobial activity of seven root canal sealers. Results of agar diffusion and agar dilution tests. , 1992, Oral surgery, oral medicine, and oral pathology.

[6]  D. Morse,et al.  The antimicrobial effect of various endodontic sealers. , 1990, Oral surgery, oral medicine, and oral pathology.

[7]  M. Tagger,et al.  Release of calcium and hydroxyl ions from set endodontic sealers containing calcium hydroxide. , 1988, Journal of endodontics.

[8]  D. Ørstavik,et al.  In vitro Infection and of Dentinal Tubules , 1987 .

[9]  W. Hume,et al.  The pharmacologic and toxicological properties of zinc oxide-eugenol. , 1986, Journal of the American Dental Association.

[10]  C. Wilson,et al.  Antibacterial activity of dental restorative materials. , 1985, International endodontic journal.

[11]  J L Ferracane,et al.  Correlation between hardness and degree of conversion during the setting reaction of unfilled dental restorative resins. , 1985, Dental materials : official publication of the Academy of Dental Materials.

[12]  D. Ørstavik.  Antibacterial properties of root canal sealers, cements and pastes. , 1981 .

[13]  L. Grossman.  Antimicrobial effect of root canal cements. , 1980, Journal of endodontics.

[14]  A. Caputo,et al.  Antimicrobial action of dental cements. , 1980, The Journal of prosthetic dentistry.

[15]  R. G. Craig.  Restorative dental materials , 1971 .

[16]  R. Phillips,et al.  Properties of cements mixed from liquids with altered water content. , 1970, The Journal of prosthetic dentistry.

[17]  H. Stanley,et al.  THE EFFECTS OF SURGICAL EXPOSURES OF DENTAL PULPS IN GERM-FREE AND CONVENTIONAL LABORATORY RATS. , 1965, Oral surgery, oral medicine, and oral pathology.