p-GaN surface treatments for metal contacts

The chemical bonding and electronic properties of wet, chemically treated p-GaN surfaces were studied using synchrotron radiation photoemission spectroscopy. Chlorine-based chemical bonding was identified on the conventional HCl-treated p-GaN surface, which is associated with a shift of the surface Fermi level toward the conduction band edge by ∼0.9 eV with respect to the thermally cleaned surface. Compared to the HCl-treated surface, the surface Fermi level on the KOH-treated surface lies about ∼1.0 eV closer to the valence band edge, resulting in a much smaller surface barrier height to p-type materials than the HCl-treated surface. The smaller surface barrier height to p-GaN after KOH treatment can lead to a lower contact resistivity and can play an important role in lowering the metal contact resistivity to p-GaN.

[1]  J. Weyher,et al.  Chemical polishing of bulk and epitaxial GaN , 1997 .

[2]  H. Morkoç,et al.  Low resistance ohmic contacts on wide band‐gap GaN , 1994 .

[3]  Theodore D. Moustakas,et al.  Metal contacts to gallium nitride , 1993 .

[4]  C. D. Thurmond,et al.  Heteroepitaxial Thermal Gradient Solution Growth of GaN , 1972 .

[5]  I. Lindau,et al.  Atomic subshell photoionization cross sections and asymmetry parameters: 1 ⩽ Z ⩽ 103 , 1985 .

[6]  Shuji Nakamura,et al.  InGaN multi‐quantum‐well structure laser diodes grown on MgAl2O4 substrates , 1996 .

[7]  A. Wickenden,et al.  The dependence of the structure and electronic properties of wurtzite GaN surfaces on the method of preparation , 1998 .

[8]  Franz J. Himpsel,et al.  Chemical bonding and electronic properties of SeS2-treated GaAs(100) , 1999 .

[9]  F. Himpsel,et al.  The oxidation of GaAs(110): A reevaluation , 1984 .

[10]  Taeil Kim,et al.  Effect of surface treatment by KOH solution on ohmic contact formation of p-type GaN , 1999 .

[11]  H. Morkoç,et al.  Very low resistance multilayer Ohmic contact to n‐GaN , 1996 .

[12]  T. Kozawa,et al.  Schottky barriers and contact resistances on p‐type GaN , 1996 .

[13]  C. Kunz,et al.  Determination of partial subshell cross-sections and electron mean free path in solids with the photoemission set-up at the FLIPPER monochromator , 1983 .

[14]  Surface and interface analysis at 3rd generation light sources , 1995 .

[15]  Masa-aki Suzuki,et al.  Low-resistance Ta/Ti ohmic contacts for p-type GaN , 1998 .

[16]  S. Nakamura,et al.  Candela‐class high‐brightness InGaN/AlGaN double‐heterostructure blue‐light‐emitting diodes , 1994 .

[17]  Eicke R. Weber,et al.  The advanced unified defect model for Schottky barrier formation , 1988 .

[18]  Masayoshi Koike,et al.  Effects of surface treatments and metal work functions on electrical properties at p-GaN/metal interfaces , 1997 .

[19]  Kelvin G. Lynn,et al.  Ohmic contact formation mechanism of nonalloyed Pd contacts to p-type GaN observed by positron annihilation spectroscopy , 1999 .