Performance of thermally damaged fibre reinforced concretes

Abstract Mechanical characteristics of Fibre Reinforced High Performance Concrete (FR-HPC) subjected to high temperatures were experimentally investigated in this paper. Three different concretes were prepared: a normal strength concrete (NSC) and two High Performance Concretes (HPC1 and HPC2). Fibre reinforced concretes were produced by addition of steel or polypropylene fibres in the above mixtures at dosages of 40 kg/m3 and 5 kg/m3, respectively. A total of nine concrete mixtures were produced and fibres were added in six of them. At the age of 120 days specimens were heated to maximum temperatures of 100, 300, 500 and 700 °C. Specimens were then allowed to cool in the furnace and tested for compressive strength, splitting tensile strength, modulus of elasticity and ultrasonic pulse velocity. Reference tests were also performed at air temperature (20 °C). Residual strength of NSC and HPC1 was reduced almost linearly up to 700 °C and 500 °C, respectively whereas the residual strength of HPC2 was sharply reduced up to 300 °C. Explosive spalling was observed on both HPC. Addition of steel fibres increased the residual strength up to 300 °C, but spalling still occurred in HPC1 and HPC2. Such an explosive behavior was not observed when polypropylene fibres were added in the mixtures; however, in this case the residual mechanical characteristics of all concretes were significantly reduced.

[1]  Y. Chen,et al.  Residual stress–strain relationship for concrete after exposure to high temperatures , 2006 .

[2]  G Sanjayan,et al.  SPALLING OF HIGH-STRENGTH SILICA FUME CONCRETE IN FIRE , 1993 .

[3]  A. Neville.  Properties of Concrete , 1968 .

[4]  Ziad Bayasi,et al.  EFFECT OF EXPOSURE TO ELEVATED TEMPERATURE ON POLYPROPYLENE FIBER-REINFORCED CONCRETE , 2002 .

[5]  James R. Lawson,et al.  Effects of elevated temperature exposure on heating characteristics, spalling, and residual properties of high performance concrete , 2001 .

[6]  P. K. Mehta.  Concrete: Structure, Properties, and Materials , 1992 .

[7]  L. Sarvaranta,et al.  Fibre mortar composites under fire conditions: effects of ageing and moisture content of specimens , 1994 .

[8]  Daniel Quenard,et al.  Spalling and pore pressure in HPC at high temperatures , 2000 .

[9]  Kristian Dahl Hertz,et al.  DANISH INVESTIGATIONS ON SILICA FUME CONCRETES AT ELEVATED TEMPERATURES , 1992 .

[10]  Y. N. Chan,et al.  Residual strength and pore structure of high-strength concrete and normal strength concrete after exposure to high temperatures , 1999 .

[11]  Pierre Kalifa,et al.  High-temperature behaviour of HPC with polypropylene fibres: From spalling to microstructure , 2001 .

[12]  A. Noumowé,et al.  High Temperature Effect on High Performance Concrete (70 - 600 C) strength and porosity , 1994, "SP-145: Durability of Concrete -- Proceedings Third CANMET - ACI International Conference, Nice, France 1994".

[13]  R. Feldman,et al.  Differentiation of interlayer and adsorbed water in hydrated portland cement by thermal analysis , 1971 .

[14]  N. Carino,et al.  Effects of Test Conditions and Mixture Proportions on Behavior of High-Strength Concrete Exposed to High Temperatures , 2002 .

[15]  Gabriel A. Khoury,et al.  Compressive strength of concrete at high temperatures: a reassessment , 1992 .

[16]  Venkatesh Kodur,et al.  Optimization of the type and amount of polypropylene fibres for preventing the spalling of lightweight concrete subjected to hydrocarbon fire , 2004 .

[17]  F. Roux.  Concrete at elevated temperature , 1974 .

[18]  Wei-Ming Lin,et al.  Microstructures of Fire-Damaged Concrete , 1996 .