The Effect of Insertion Species on Nanostructured Open Framework Hexacyanoferrate Battery Electrodes

Recent battery research has focused on the high power and energy density needed for portable electronics and vehicles, but the requirements for grid-scale energy storage are different, with emphasis on low cost, long cycle life, and safety. 1,2 Open framework materials with the Prussian Blue crystal structure offer the high power capability, ultra-long cycle life, and scalable, low cost synthesis and operation that are necessary for storage systems to integrate transient energy sources, such as wind and solar, with the electrical grid. We have demonstrated that two open framework materials, copper hexacyanoferrate and nickel hexacyanoferrate, can reversibly intercalate lithium, sodium, potassium, and ammonium ions at high rates. These materials can achieve capacities of up to 60 mAh/g. The porous, nanoparticulate morphology of these materials, synthesized by the use of simple and inexpensive methods, results in remarkable rate capabilities: e.g. copper hexacyanoferrate retains 84% of its maximum capacity during potassium cycling at a very high (41.7C) rate, while nickel hexacyanoferrate retains 66% of its maximum capacity while cycling either sodium or potassium at this same rate. These materials show excellent stability during the cycling of sodium and potassium, with minimal capacity loss after 500 cycles.

[1]  G. Soloveichik Battery technologies for large-scale stationary energy storage. , 2011, Annual review of chemical and biomolecular engineering.

[2]  Jun Liu,et al.  Electrochemical energy storage for green grid. , 2011, Chemical reviews.

[3]  P. He,et al.  Raising the cycling stability of aqueous lithium-ion batteries by eliminating oxygen in the electrolyte. , 2010, Nature chemistry.

[4]  Yi Cui,et al.  Recent results on aqueous electrolyte cells , 2010 .

[5]  J. Whitacre,et al.  Na4Mn9O18 as a positive electrode material for an aqueous electrolyte sodium-ion energy storage device , 2010 .

[6]  Gerbrand Ceder,et al.  Response to "unsupported claims of ultrafast charging of Li-ion batteries" , 2009 .

[7]  Jian Ma,et al.  Operational Impacts of Wind Generation on California Power Systems , 2009, IEEE Transactions on Power Systems.

[8]  Byoungwoo Kang,et al.  Battery materials for ultrafast charging and discharging , 2009, Nature.

[9]  Yi Cui,et al.  Electrochemical behavior of LiCoO2 as aqueous lithium-ion battery electrodes , 2009 .

[10]  R. Huggins Advanced Batteries: Materials Science Aspects , 2008 .

[11]  J. Tarascon,et al.  Mixed-valence li/fe-based metal-organic frameworks with both reversible redox and sorption properties. , 2007, Angewandte Chemie.

[12]  Craig M. Brown,et al.  Hydrogen storage in a microporous metal-organic framework with exposed Mn2+ coordination sites. , 2006, Journal of the American Chemical Society.

[13]  G. Aromí,et al.  Synthesis of 3d metallic single-molecule magnets , 2006 .

[14]  J. Long,et al.  Hydrogen storage in the dehydrated prussian blue analogues M3[Co(CN)6]2 (M = Mn, Fe, Co, Ni, Cu, Zn). , 2005, Journal of the American Chemical Society.

[15]  J. Eto,et al.  Understanding the cost of power interruptions to U.S. electricity consumers , 2004 .

[16]  J.P. Barton,et al.  Energy storage and its use with intermittent renewable energy , 2004, IEEE Transactions on Energy Conversion.

[17]  Michael O'Keeffe,et al.  Hydrogen Storage in Microporous Metal-Organic Frameworks , 2003, Science.

[18]  Bruno Scrosati,et al.  Fast Ion Transport in Solids , 1993 .

[19]  D. Stilwell,et al.  Electrochemical studies of the factors influencing the cycle stability of Prussian Blue films , 1992 .

[20]  J. O. Berg,et al.  Application of Stokes' law to ions in aqueous solution , 1990 .

[21]  E. Grabner,et al.  A secondary cell based on thin layers of zeolite-like nickel hexacyanometallates , 1989 .

[22]  John O. Thomas,et al.  THE PADDLE-WHEEL MODEL FOR ION CONDUCTION IN SOME SOLID PHASES , 1989 .

[23]  A secondary battery composed of multilayer Prussian Blue and its reaction characteristics , 1988 .

[24]  J. McCargar,et al.  Thermodynamics of mixed-valence intercalation reactions: the electrochemical reduction of Prussian blue , 1988 .

[25]  K. Honda,et al.  Prussian Blue Containing Nafion Composite Film as Rechargeable Battery , 1987 .

[26]  E. Grabner,et al.  Hexacyanoferrate layers as electrodes for secondary cells , 1987 .

[27]  I. Uchida,et al.  Electrochemistry of polynuclear transition metal cyanides: Prussian blue and its analogues , 1986 .

[28]  V. Neff Some Performance Characteristics of a Prussian Blue Battery , 1985 .

[29]  A. Bocarsly,et al.  Reaction of Nickel Electrode Surfaces with Anionic Metal-Cyanide Complexes: Formation of Precipitated Surfaces , 1984 .

[30]  T. Kuwana,et al.  Electrochemical and Spectroscopic Studies of Metal Hexacyanometalate Films I . Cupric Hexacyanoferrate , 1983 .

[31]  A. Bocarsly,et al.  Effects of surface structure on electrode charge transfer properties. Induction of ion selectivity at the chemically derivatized interface , 1982 .

[32]  Kingo Itaya,et al.  Spectroelectrochemistry and electrochemical preparation method of Prussian blue modified electrodes , 1982 .

[33]  A. J. Mark,et al.  Thermodynamics and kinetics of the electrochemical insertion of lithium into tungsten bronzes , 1981 .

[34]  Peter Fischer,et al.  Neutron diffraction study of Prussian Blue, Fe4[Fe(CN)6]3.xH2O. Location of water molecules and long-range magnetic order , 1980 .

[35]  Vernon D. Neff,et al.  Electrochemical Oxidation and Reduction of Thin Films of Prussian Blue , 1978 .

[36]  D. Schwarzenbach,et al.  The crystal structure of Prussian Blue: Fe4[Fe(CN)6]3.xH2O , 1977 .

[37]  Peter Day,et al.  Mixed Valence Chemistry-A Survey and Classification , 1968 .