ff ects of Annealing Temperature on the Structural Properties of ZrB 2 Films Deposited via Pulsed DC Magnetron Sputtering

Zirconium diboride (ZrB2) thin films were deposited on a Si(100) substrate using pulsed direct current (dc) magnetron sputtering and then annealed in high vacuum. In addition, we discussed the effects of the vacuum annealing temperature in the range of 750 to 870 ◦C with flowing N2 on the physical properties of ZrB2 films. The structural properties of ZrB2 films were investigated with X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS). The XRD patterns indicated that the ZrB2 films annealed at various temperatures exhibited a highly preferred orientation along the [0001] direction and that the residual stress could be relaxed by increasing the annealing temperature at 870 ◦C in a vacuum. The surface morphology was smooth, and the surface roughness slightly decreased with increasing annealing temperature. Cross-sectional TEM images of the ZrB2/Si(100) film annealed at 870 ◦C reveals the films were highly oriented in the direction of the c-axis of the Si substrate and the film structure was nearly stoichiometric in composition. The XPS results show the film surfaces slightly contain oxygen, which corresponds to the binding energy of Zr–O. Therefore, the obtained ZrB2 film seems to be quite suitable as a buffer layer for III-nitride growth.

[1]  V. Shestakov,et al.  Synthesis of Zirconium Diboride Films and ZrB2/BCxNy Heterostructures , 2018, Inorganic Materials.

[2]  L. Hultman,et al.  Chemical bonding in epitaxial ZrB2 studied by X-ray spectroscopy , 2018, 1801.08663.

[3]  Jens Birch,et al.  Magnetron Sputter Epitaxy of High-Quality GaN Nanorods on Functional and Cost-Effective Templates/Substrates , 2017 .

[4]  E. Janzén,et al.  Stoichiometric, epitaxial ZrB2 thin films with low oxygen-content deposited by magnetron sputtering from a compound target: Effects of deposition temperature and sputtering power , 2015 .

[5]  D. Frankel,et al.  Growth, structure, and high temperature stability of zirconium diboride thin films , 2015 .

[6]  E. Janzén,et al.  Direct current magnetron sputtered ZrB2 thin films on 4H-SiC(0001) and Si(100) , 2014 .

[7]  L. Hultman,et al.  ZrB2 thin films grown by high power impulse magnetron sputtering from a compound target , 2012 .

[8]  Yue Zhang,et al.  Oxidation of zirconium diboride–silicon carbide ceramics under an oxygen partial pressure of 200 Pa: Formation of zircon , 2010 .

[9]  Q. Zeng,et al.  Crystal structure and elastic properties of ZrB compared with ZrB2: A first-principles study , 2010 .

[10]  D. Alfano,et al.  Microstructural characterization of ZrB2-SiC based UHTC tested in the MESOX plasma facility , 2010 .

[11]  T. Aizawa,et al.  The 2 2 oxidized layer on ZrB 2(0 0 0 1) , 2009 .

[12]  S. Bera,et al.  Growth of single-crystalline zirconium diboride thin film on sapphire , 2009 .

[13]  A. Vantomme,et al.  High-temperature AlN interlayer for crack-free AlGaN growth on GaN , 2008 .

[14]  G. Janssen,et al.  Stress and strain in polycrystalline thin films , 2007 .

[15]  J. Tolle,et al.  Effect of nitridation on the growth of GaN on ZrB2(0001)∕Si(111) by molecular-beam epitaxy , 2006 .

[16]  T. Kimoto,et al.  Characterization of ZrB2(0001) surface prepared by ex situ HF solution treatment toward applications as a substrate for GaN growth , 2006 .

[17]  T. Aizawa,et al.  Surface core-level shift and electronic structure on transition-metal diboride (0001) surfaces , 2005 .

[18]  B. Vincent Crist,et al.  The elements and native oxides , 2004 .

[19]  Kazuyoshi Iida,et al.  Violet and UV light‐emitting diodes grown on ZrB2 substrate , 2003 .

[20]  S. Kamiyama,et al.  Growth of GaN on ZrB2 substrate by metal-organic vapor phase epitaxy , 2003 .

[21]  John R Abelson,et al.  Remote-plasma chemical vapor deposition of conformal ZrB2 films at low temperature: A promising diffusion barrier for ultralarge scale integrated electronics , 2002 .

[22]  H. Matsunami,et al.  Zirconium Diboride (0001) as an Electrically Conductive Lattice-Matched Substrate for Gallium Nitride , 2001 .

[23]  Y. Paderno,et al.  Analysis of a Zirconium Diboride Single Crystal, ZrB2 (0001), by XPS , 2000 .

[24]  M. Korsukova,et al.  Preparation of HfB2 and ZrB2 single crystals by the floating-zone method , 1998 .

[25]  Theeradetch Detchprohm,et al.  Relaxation Process of the Thermal Strain in the GaN/α-Al2O3 Heterostructure and Determination of the Intrinsic Lattice Constants of GaN Free from the Strain , 1992 .

[26]  A. L. Patterson.  The Scherrer Formula for X-Ray Particle Size Determination , 1939 .