Stress in undoped LPCVD polycrystalline silicon

The effect of processing conditions on stress in undoped LPCVD polycrystalline silicon films was investigated. Films were deposited at temperatures between 605 and 700 degrees C and pressures from 300 to 550 mtorr, with varying silane flow rate and deposition time. Low temperatures produced tensile films, while temperatures greater than about 620 degrees C resulted in compressive stress. Film thickness and deposition pressure also affect the stress rate. By removing film layers with a plasma etch, the stress profile through the film thickness was determined. Tension results when silicon atoms deposit in the amorphous state and subsequently crystallize, but thermal stress, due to differences in expansion coefficient between the film and substrate, is ruled out as significant contributor to the film stress. By superposing the crystallization stress and a compressive intrinsic stress component that decreases with temperature, the observed stress trend is obtained.<<ETX>>

[1]  Martin A. Schmidt,et al.  Characterization of the mechanisms producing bending moments in polysilicon micro-cantilever beams by interferometric deflection measurements , 1988, IEEE Technical Digest on Solid-State Sensor and Actuator Workshop.

[2]  J. Bloem,et al.  Temperature dependence of the growth rate of silicon prepared through chemical vapor deposition from silane , 1982 .

[3]  R. Howe,et al.  Investigation of Texture and Stress in Undoped Polysilicon Films , 1990 .

[4]  D. C. Booth,et al.  Optical properties and structure of amorphous silicon films prepared by CVD , 1979 .

[5]  I. Wu,et al.  In Situ Hrem Observations of Crystallization in LPCVD Amorphous Silicon , 1990 .

[6]  T. Christenson,et al.  Fabrication of micromechanical devices from polysilicon films with smooth surfaces , 1989 .

[7]  D. W. Burns,et al.  Fine-grained polysilicon films with built-in tensile strain , 1988 .

[8]  I. Kiryushin,et al.  Mechanical stresses in low pressure chemically vapour deposited silicon films , 1988 .

[9]  E. Kinsbron,et al.  Crystallization of amorphous silicon films during low pressure chemical vapor deposition , 1983 .

[10]  R. Howe.  Surface micromachining for microsensors and microactuators , 1988 .

[11]  S. Timoshenko,et al.  Analysis of Bi-Metal Thermostats , 1925 .

[12]  R. Gat,et al.  Morphological effects during low pressure chemical vapor deposition and annealing of undoped polycrystalline silicon layers , 1986 .

[13]  R. Howe,et al.  Stress in polycrystalline and amorphous silicon thin films , 1983 .

[14]  I. Kiryushin,et al.  Stresses in thin polycrystalline silicon films , 1988 .

[15]  Takuzo Ogawa,et al.  The Deformation of Polycrystalline‐Silicon Deposited on Oxide‐Covered Single Crystal Silicon Substrates , 1977 .

[16]  B. Loisel,et al.  The Effect of Low Pressure on the Structure of LPCVD Polycrystalline Silicon Films , 1987 .

[17]  J. Adamczewska,et al.  Stress in chemically vapour-deposited silicon films , 1984 .