Numerical investigation on the fracture failure of a railway axle

Abstract Railway axles are designed to be highly reliable so as to ensure even more than 30 years of service. Even though they are periodically inspected by scheduled Non Destructive Testing (NDT) inspections to detect the potential initiation of cracks, failures with disastrous consequences for railway vehicles and human beings can occur. This paper reports an investigation concerning the failure of an axle of a passenger coach due to fatigue crack propagation. Calculations indicated that the need for reliable NDT inspection methods is of crucial importance for the upfront detection of potentially critical cracks. The presented investigation was useful to support the application of the crack propagation simulation for the determination of reliable axle NDT inspection intervals so as to prevent future accidents.

[1]  E. Wolf.  Fatigue crack closure under cyclic tension , 1970 .

[2]  Uwe Zerbst,et al.  An investigation on the influence of rotary bending and press fitting on stress intensity factors and fatigue crack growth in railway axles , 2008 .

[3]  Michele Carboni,et al.  Application of fatigue crack growth algorithms to railway axles and comparison of two steel grades , 2004 .

[4]  F. Erdogan,et al.  On the Crack Extension in Plates Under Plane Loading and Transverse Shear , 1963 .

[5]  W. Elber.  The Significance of Fatigue Crack Closure , 1971 .

[6]  Uwe Zerbst,et al.  The development of a damage tolerance concept for railway components and its demonstration for a railway axle , 2005 .

[7]  G. Dhondt,et al.  Dual boundary element method and finite element method for mixed‐mode crack propagation simulations in a cracked hollow shaft , 2018 .

[8]  Roberto Guglielmo Citarella,et al.  Multiple Crack Propagation with Dual Boundary Element Method in Stiffened and Reinforced Full Scale Aeronautic Panels , 2013 .

[9]  Roberto Guglielmo Citarella,et al.  Efficient FEM-DBEM coupled approach for crack propagation simulations , 2017 .

[10]  M. H. Aliabadi,et al.  Mixed-mode J-integral method for analysis of 3D fracture problems using BEM , 1993 .

[11]  W. J. Mills,et al.  Review and synthesis of stress intensity factor solutions applicable to cracks in bolts , 1988 .

[12]  Michele Carboni.  Reliability of Non-destructive Testing in the Railway Field: Common Practice and New Trends , 2019 .

[13]  Roberto Guglielmo Citarella,et al.  Assessment of Crack Growth from a Cold Worked Hole by Coupled FEM-DBEM Approach , 2013 .

[14]  B. J. Carter,et al.  The M-Integral for Computing Stress Intensity Factors in Generally Anisotropic Materials , 2005 .

[15]  Roberto Guglielmo Citarella,et al.  Combined static-cyclic multi-axial crack propagation in cruciform specimens , 2019, International Journal of Fatigue.

[16]  J. Newman.  A crack opening stress equation for fatigue crack growth , 1984 .

[17]  R. Esposito,et al.  Deterministic fatigue crack-growth simulations for a railway axle by Dual Boundary Element Method , 2021, IOP Conference Series: Materials Science and Engineering.

[18]  G. C. Sih,et al.  A fracture criterion for three-dimensional crack problems , 1974 .

[19]  Roberto Guglielmo Citarella,et al.  Fatigue life assessment in lateral support element of a magnet for nuclear fusion experiment "Wendelstein 7-X" , 2017 .

[20]  Venanzio Giannella,et al.  Stochastic approach to fatigue crack-growth simulation for a railway axle under input data variability , 2021 .

[21]  Stefano Beretta,et al.  Probabilistic fatigue assessment for railway axles and derivation of a simple format for damage calculations , 2016 .

[22]  Michele Carboni,et al.  Experiments and stochastic model for propagation lifetime of railway axles , 2006 .

[23]  Roberto Guglielmo Citarella,et al.  FEM simulation of a crack propagation in a round bar under combined tension and torsion fatigue loading , 2014 .

[24]  V. Giannella,et al.  Multi-axial fatigue numerical crack propagation in cruciform specimens , 2019, Frattura ed Integrità Strutturale.

[25]  Roberto Guglielmo Citarella,et al.  Coupled FEM-DBEM method to assess crack growth in magnet system of Wendelstein 7-X , 2013 .

[26]  Guido Dhondt,et al.  General behaviour of collapsed 8‐node 2‐D and 20‐node 3‐D isoparametric elements , 1993 .

[27]  Michele Carboni,et al.  A CRITICAL ANALYSIS OF ULTRASONIC ECHOES COMING FROM NATURAL AND ARTIFICIAL FLAWS AND ITS IMPLICATIONS IN THE DERIVATION OF “PROBABILITY OF DETECTION” CURVES , 2012 .

[28]  Roberto Guglielmo Citarella,et al.  Surface crack modelling in an engine compressor disc , 2019, Theoretical and Applied Fracture Mechanics.

[29]  Luboš Náhlík,et al.  Residual fatigue lifetime estimation of railway axles for various loading spectra , 2016 .

[30]  Fatigue crack-growth predictions for a railway axle under material data variability , 2021 .