Effect of process variables on the grain growth and microstructure of ZnO–Bi2O3 varistors and their nanosize ZnO precursors

The basic building block of the ZnO varistor is the ZnO grain formed as a result of sintering. Nanosized ZnO particles are prepared by carrying out the reaction in the controlled size nanoreactors—the droplets of microemulsions. Chemical doping of the ZnO nanoparticles provides ZnO-based ceramic varistors displaying superior varistor properties. These varistors show a higher value of the nonlinear coefficient, lower leakage current, and higher critical electric field value as compared to those for conventional samples in their log E versus log J curve. The present work has also been aimed at studying the effect of processing variables such as sintering temperature and duration on the microstructure and grain growth of ZnO nanoparticles and ZnO-Bi 2 O 3 ceramics. The activation energy calculated from this data is found to be 175 kJ/mol for pure ZnO. For Bi 2 O 3 -doped ZnO, the activation energy is found to decrease considerably (∼148 kJ/mol). All these advantages are due to greater structural homogeneity, smaller particle size, higher surface area, and higher density of the ZnO nanoparticles which are precursors for ZnO varistors, as compared to coarser particles for making varistors.

[1]  R. B. Poeppel,et al.  Impedance Spectroscopy Study of Sintering in Bi‐Doped ZnO , 1994 .

[2]  V. Dravid,et al.  Microanalytical Determination of ZnO Solidus and Liquidus Boundaries in the ZnO-Bi2O3 System , 1994 .

[3]  L. Overzet,et al.  Negative and positive ions from CF4 and CF4/O2 rf discharges in etching Si , 1993 .

[4]  W. Klimczak,et al.  Dust collector design for pneumatic conveying systems , 1993 .

[5]  D. Shah,et al.  Magnetic properties of barium ferrite synthesized using a microemulsion mediated process , 1992 .

[6]  Long Wu,et al.  Effects of processing and valence states of metal oxides on electrical properties of ZnO varistors , 1992 .

[7]  R. W. Siegel Nanophase Materials Assembled from Atomic Clusters , 1990 .

[8]  T. Gupta Application of Zinc Oxide Varistors , 1990 .

[9]  D. Hennings,et al.  Grain Size Control in Low‐Voltage Varistors , 1990 .

[10]  L. C. Jonghe,et al.  Low-temperature sintering of zinc oxide varistors , 1990 .

[11]  R. Bradt,et al.  Grain Growth in Sintered ZnO and ZnO-Bi2O3 Ceramics , 1990 .

[12]  S. Haile,et al.  Aqueous Precipitation of Spherical Zinc Oxide Powders for Varistor Applications , 1989 .

[13]  D. Shah,et al.  A light scattering study on the droplet size and interdroplet interaction in microemulsions of AOT—oil—water system , 1988 .

[14]  PREPARATION OF BaCO3, PARTICLES IN IONIC W/O MICROEMULSIONS , 1988 .

[15]  G. Iyengar,et al.  Influence of Process Variables on Microstructure and V‐I Characteristics of Multicomponent ZnO‐Based Nonlinear Resistors , 1987 .

[16]  Noboru Amiji,et al.  Homogeneity of Zinc Oxide Varistors , 1986 .

[17]  R. M. Spriggs,et al.  Grain Growth in Fully Dense ZnO , 1970 .

[18]  J. Burke,et al.  Ultrafine-Grain ceramics , 1970 .

[19]  G. C. Nicholson Grain Growth in Zinc Oxide , 1965 .