Composition and heat-treatment dependences of the martensitic transformations in sputter-deposited shape memory Ti-Ni films were investigated by differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). Films were deposited on quartz substrates by sputtering using a target of an equiatomic TiNi alloy. The substrate temperature was kept below 423K during sputtering. The compositions of the films were determined by electron probe micro-analysis using a calibration line prepared from bulk samples of well-established compositions. The as-deposited films were found to be amorphous and to crystallize on heating above 750K. The amorphous films were heat-treated at various temperatures between 673 and 1123K and the transformation behavior of the heat-treated films was examined by DSC and TEM. Obtained results are as follows. (1) During crystallization heat treatment, no precipitation occurs in near-equiatomic Ti-Ni films, whereas Ti 2 Ni particles precipitate in the Ti-rich films and Ti 3 Ni 4 particles do in the Ni-rich films. (2) The B2→R transformation temperature becomes maximum (335K) at the equiatomic composition and decreases with increasing Ni-content with a rate of 96K/at.% Ni for 50.0-50.5 at.% Ni alloys which becomes a single B2 phase when crystallized by holding at 773K. It is constant (335K) in the Ti-rich side range. It also is constant in the Ni-rich range (287K with the films crystallized by holding at 773K). (3) The B2 → B19' transformation temperature becomes maximum at the equiatomic composition and decreases with increasing Ni-context. It is constant in the Ti-richrange.
[1]
W. J. Buehler,et al.
Crystal Structure and a Unique ``Martensitic'' Transition of TiNi
,
1965
.
[2]
G. D. Rieck,et al.
Diffusion in the titanium-nickel system: I. occurrence and growth of the various intermetallic compounds
,
1974
.
[3]
Yoshiyuki Nakata,et al.
Crystal Structure, Composition and Morphology of a Precipitate in an Aged Ti-51 at%Ni Shape Memory Alloy
,
1986
.
[4]
S. Nenno,et al.
Crystal structure and morphology of the metastable X phase in shape memory Ti-Ni alloys
,
1986
.
[5]
Yoshiyuki Nakata,et al.
Thermal Cycling Effects in an Aged Ni-rich Ti–Ni Shape Memory Alloy
,
1987
.
[6]
David A. Stevenson,et al.
Shape‐memory properties in Ni‐Ti sputter‐deposited film
,
1990
.
[7]
S. Miyazaki,et al.
Shape memory thin film of TiNi formed by sputtering
,
1993
.
[8]
Akira Ishida,et al.
Shape memory characteristics of sputter-deposited Ti-Ni thin films
,
1994
.