Electrical response of amorphous silicon thin-film transistors under mechanical strain

We evaluated amorphous silicon thin-film transistors (TFTs) fabricated on polyimide foil under uniaxial compressive or tensile strain. The strain was induced by bending or stretching. The on- current and hence the electron linear mobility μ depend on strain e as μ=μ0(1+26×e), where tensile strain has a positive sign and the strain is parallel to the TFT source-drain current path. Upon the application of compressive or tensile strain the mobility changes “instantly” and under compression then remains constant for up to 40 h. In tension, the TFTs fail mechanically at a strain of about +0.003 but recover if the strain is released “immediately.”

[1]  W. Spear,et al.  The effects of applied and internal strain on the electronic propertiesof amorphous silicon , 1986 .

[2]  Rona E. Belford.  Uniaxial, tensile-strained Si devices , 2001 .

[3]  Gregory N. Parsons,et al.  Reaction Processes for Low Temperature (<150°C) Plasma Enhanced Deposition of Hydrogenated Amorphous Silicon Thin-Film Transistors on Transparent Plastic Substrates , 1998 .

[4]  R. Gottscho,et al.  TFT Performance - Material Quality Correlation for a-Si:H Deposited at high Rates , 1995 .

[5]  B. G. Brooks,et al.  Disorder and the Optical-Absorption Edge of Hydrogenated Amorphous Silicon , 1981 .

[6]  Sigurd Wagner,et al.  High electron mobility polycrystalline silicon thin-film transistors on steel foil substrates , 1999 .

[7]  Sigurd Wagner,et al.  a-Si:H TFTs made on polyimide foil by PE-CVD at 150 °C , 1998 .

[8]  S. Wagner,et al.  Amorphous silicon thin-film transistors on steel foil substrates , 1996, IEEE Electron Device Letters.

[9]  Sigurd Wagner,et al.  150°C Amorphous Silicon Thin-Film Transistor Technology for Polyimide Substrates , 2001 .

[10]  R. Gottscho,et al.  Correlation between the valence‐ and conduction‐band‐tail energies in hydrogenated amorphous silicon , 1996 .

[11]  Sigurd Wagner,et al.  Electron mobility in amorphous silicon thin-film transistors under compressive strain , 2001 .

[12]  M. Brodsky,et al.  Optical absorption in amorphous Si films at high pressure , 1977 .

[13]  M. Machonkin,et al.  Summary Abstract: Thermomechanical properties of glow discharge deposited silicon and silicon oxide films , 1988 .

[14]  S. Wagner,et al.  Electrographically patterned thin-film silicon transistors , 1996, IEEE Electron Device Letters.

[15]  S. Gates.  Prospects for Active Matrix Displays on Plastic , 1997 .

[16]  Sigurd Wagner,et al.  Failure resistance of amorphous silicon transistors under extreme in-plane strain , 1999 .