Sol–gel deposited nickel oxide films for electrochromic applications

Abstract The electrochromic (EC) behavior, the microstructure, and the morphology of sol–gel deposited nickel oxide (NiOx) coatings were investigated. The films were produced by spin and dip-coating techniques on indium tin oxide (ITO)/glass and Corning glass (2947) substrates. The coating solutions were prepared by reacting nickel(II) 2-ethylhexanoate as the precursor, and isopropanol as the solvent. NiOx was heat treated at 350 °C for 1 h. The surface morphology, crystal structure, and EC characteristics of the coatings were investigated by scanning electron microscopy (SEM), electron dispersive spectroscopy (EDS), atomic force spectroscopy (AFM), X-ray diffractometry (XRD), and cyclic voltammetry (CV). SEM and AFM images revealed that the surface morphology and surface characteristics of the spin- and dip-coated films on both types of substrate were different. XRD spectra revealed that both films were amorphous, either on ITO or Corning glass substrates. CV showed a reversible electrochemical insertion or extraction of the K+ ions, cycled in 1 M KOH electrolyte, in both type of film. The crystal structure of the cycled films was found to be XRD amorphous. Spectroelectrochemistry demonstrated that dip-coated films were more stable up to 1000 coloration–bleaching cycles, whereas spin-coated films gradually degraded after 500 cycles.

[1]  P. Bukovec,et al.  Preparation and structural investigations of electrochromic nanosized NiOx films made via the sol-gel route , 2003 .

[2]  J. Purans,et al.  XAS, XRD, AFM and Raman studies of nickel tungstate electrochromic thin films , 2001 .

[3]  Steven J. Visco,et al.  Supported Electrolyte Thin Film Synthesis of Solid Oxide Fuel Cells , 2003 .

[4]  Claes G. Granqvist,et al.  Handbook of inorganic electrochromic materials , 1995 .

[5]  C. Lampert,et al.  Electrochromic characterization of sol-gel deposited coatings , 1998 .

[6]  C. E. Tracy,et al.  Electrochromic Properties of Sputtered Ni Oxide Thin Films in Acidic KCl + H2SO4 Aqueous Solutions , 2006 .

[7]  B. Orel,et al.  Sol-gel derived hydrated nickel oxide electrochromic films: Optical, spectroelectrochemical and structural properties , 1997 .

[8]  H. Sakaguchi,et al.  Nanometer scale-electrochromic modification of NiO films using a novel technique of scanning near-field optical microscopy , 2003 .

[9]  Enric Bertran,et al.  Electrochromic behaviour of nickel oxide thin films deposited by thermal evaporation , 2001 .

[10]  P. Bukovec,et al.  The role of thermal analysis in optimization of the electrochromic effect of nickel oxide thin films, prepared by the sol-gel method. Part I , 2003 .

[11]  P. Sharma,et al.  Synthesis, characterization and electrochromic properties of NiOxHy thin film prepared by a sol–gel method , 1998 .

[12]  Qi Zhang,et al.  Nickel oxide sol-gel films from nickel diacetate for electrochromic applications , 2003 .

[13]  Zhibo Zhang,et al.  Preparation of Nickel Oxide Films by Sol-Gel Process , 1993 .