Finite element simulation of ultra low cycle fatigue cracking in steel structures

Abstract This paper proposes a new method of simulating ductile fracture in steel structures under large amplitude cyclic straining experienced in earthquakes. The method is developed based on an existing micromechanical model originally proposed for predicting crack initiation in ultra-low cycle fatigue, ULCF. It involves a step-by-step simulation of material degradation within the framework of conventional nonlinear FEM. The method is validated through simulating fracture in a structural detail (column-to-base plate connection) for which several cyclic tests has been previously conducted. It is found that the method can successfully predict the cracking site, its propagation path, the number of cycles corresponding to crack initiation, and also final fracture.

[1]  G. Deierlein,et al.  Cyclic Void Growth Model to Assess Ductile Fracture Initiation in Structural Steels due to Ultra Low Cycle Fatigue , 2007 .

[2]  Amit Kanvinde,et al.  Micromechanical simulation of earthquake-induced fracture in steel structures , 2004 .

[3]  Dawn E. Lehman,et al.  Seismic Performance Assessment of Concentrically Braced Steel Frames , 2012 .

[4]  G. Meschke,et al.  A hybrid modeling concept for ultra low cycle fatigue of metallic structures based on micropore damage and unit cell models , 2010 .

[5]  Masatoshi Kuroda,et al.  Extremely low cycle fatigue life prediction based on a new cumulative fatigue damage model , 2002 .

[6]  T. Wierzbicki,et al.  Ductile fracture initiation and propagation modeling using damage plasticity theory , 2008 .

[7]  L. Xue.  A unified expression for low cycle fatigue and extremely low cycle fatigue and its implication for monotonic loading , 2008 .

[8]  F. A. McClintock,et al.  A Criterion for Ductile Fracture by the Growth of Holes , 1968 .

[9]  D. M. Tracey,et al.  On the ductile enlargement of voids in triaxial stress fields , 1969 .

[10]  Kuniaki Minami,et al.  A prediction model for extremely low cycle fatigue strength of structural steel , 2007 .

[11]  Andrew T. Myers,et al.  Testing and probabilistic simulation of ductile fracture initiation in structural steel components and weldments , 2009 .

[12]  Yuli Huang,et al.  Simulating the inelastic seismic behavior of steel braced frames including the effects of low-cycle fatigue , 2009 .

[13]  Steve Lambert,et al.  Analysis of ductile tearing of pipeline-steel in single edge notch tension specimens , 2003 .

[15]  Gregory G. Deierlein,et al.  Prediction of Ductile Fracture in Steel Connections Using SMCS Criterion , 2006 .

[16]  J. Hancock,et al.  On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states , 1976 .

[17]  Sheri Sheppard,et al.  The Relationship Between Constraint and Ductile Fracture Initiation as Defined by Micromechanical Analyses , 1995 .