The cross-plane thermoelectric properties of p-Ge/Si0.5Ge0.5 superlattices

The electrical conductivity, Seebeck coefficients, and thermal conductivities of a range of p-type Ge/Si0.5 Ge 0.5 superlattices designed for thermoelectric generation and grown by low energy plasma enhanced chemical vapor deposition have been measured using a range of microfabricated test structures. For samples with barriers around 0.5 nm in thickness, the measured Seebeck coefficients were comparable to bulk p-SiGe at similar doping levels suggesting the holes see the material as a random bulk alloy rather than a superlattice. The Seebeck coefficients for Ge quantum wells of 2.85 ± 0.85 nm increased up to 533 ± 25 μV/K as the doping was reduced. The thermal conductivities are between 4.5 to 6.0 Wm−1K−1 which are lower than comparably doped bulk Si0.3 Ge 0.7 but higher than undoped Si/Ge superlattices. The highest measured figure of merit ZT was 0.080 ± 0.011 obtained for the widest quantum well studied. Analysis suggests that interface roughness is presently limiting the performance and a reduction in the strain between the quantum wells and barriers has the potential to improve the thermoelectric performance.

[1]  Rama Venkatasubramanian,et al.  Thermal conductivity of Si–Ge superlattices , 1997 .

[2]  M. Dresselhaus,et al.  Experimental Study of the Effect of the Quantum Well Structures on the Thermoelectric Figure of Merit in Si/Si 1- x Ge x System , 1998 .

[3]  Mildred S. Dresselhaus,et al.  Use of quantum‐well superlattices to obtain a high figure of merit from nonconventional thermoelectric materials , 1993 .

[4]  G. Cody,et al.  Thermal Conductivity of Ge-Si Alloys at High Temperatures , 1962 .

[5]  E. Müller,et al.  Low energy plasma enhanced chemical vapor deposition , 2002 .

[6]  Ali Shakouri,et al.  Thermal conductivity of Si/SiGe and SiGe/SiGe superlattices , 2002 .

[7]  R. Venkatasubramanian,et al.  Thin-film thermoelectric devices with high room-temperature figures of merit , 2001, Nature.

[8]  Douglas J. Paul.  8-band k.p modeling of the quantum confined Stark effect in Ge quantum wells on Si substrates , 2008 .

[9]  Douglas J. Paul,et al.  The thermoelectric properties of Ge/SiGe modulation doped superlattices , 2013 .

[10]  Mildred S. Dresselhaus,et al.  Effect of quantum-well structures on the thermoelectric figure of merit. , 1993, Physical review. B, Condensed matter.

[11]  T. Geballe,et al.  Seebeck Effect in Silicon , 1955 .

[12]  Douglas J. Paul,et al.  Nanofabrication of high aspect ratio (∼50:1) sub-10 nm silicon nanowires using inductively coupled plasma etching , 2012 .

[13]  Gang Chen,et al.  Thermal conductivity and ballistic-phonon transport in the cross-plane direction of superlattices , 1998 .

[14]  M. Myronov,et al.  Ohmic contacts to n-type germanium with low specific contact resistivity , 2012 .

[15]  Hohyun Lee,et al.  Enhanced thermoelectric figure-of-merit in nanostructured p-type silicon germanium bulk alloys. , 2008, Nano letters.

[16]  Xie,et al.  Semiconductor surface roughness: Dependence on sign and magnitude of bulk strain. , 1994, Physical review letters.

[17]  J. Watling,et al.  A study of the impact of dislocations on the thermoelectric properties of quantum wells in the Si/SiGe materials system , 2011 .

[18]  Stefano Cecchi,et al.  Ge/SiGe superlattices for thermoelectric energy conversion devices , 2013, Journal of Materials Science.

[19]  E. F. Steigmeier,et al.  Thermal and Electrical Properties of Heavily Doped Ge‐Si Alloys up to 1300°K , 1964 .

[20]  T. Geballe,et al.  Seebeck Effect in Germanium , 1954 .