The effect of copper content and heat treatment on the stress corrosion characteristics of Ai-6Zn-2Mg-X Cu alloys

E. Starke | M. Marek | B. Sarkar

[1] E. Starke,et al. The effect of copper content and degree of recrystallization on the fatigue resistance of 7XXX type aluminum alloys I. Low cycle corrosion fatigue , 1979 .

[2] E. Starke. Aluminium alloys of the 70's: Scientific solutions to engineering problems. An invited review , 1977 .

[3] P. Doig,et al. The Stress Corrosion Susceptibility of 7075 Al-Zn-Mg-Cu Alloys Tempered from T6 to an Overaged T7X , 1977 .

[4] E. A. Starke,et al. The relationship of microstructure to monotonic and cyclic straining of two age hardening aluminum alloys , 1976 .

[5] M. O. Speidel,et al. Stress corrosion cracking of aluminum alloys , 1975 .

[6] P. Doig,et al. The influence of quenching on the segregation of magnesium to the grain boundaries in an Al-5.9 wt pct Zn-3.2 wt pct Mg alloy , 1975 .

[7] R. Gest,et al. Stress Corrosion and Hydrogen Embrittlement in an Aluminum Alloy , 1974 .

[8] A. Mcevily,et al. Stress corrosion crack velocity and grain boundary precipitates in an Al-Zn-Mg alloy , 1974, Metallurgical and Materials Transactions B.

[9] B. Brown. Stress-corrosion cracking in high strength steels and in titanium and aluminum alloys , 1972 .