Membrane accelerated stress test development for polymer electrolyte fuel cell durability validated using field and drive cycle testing

Author(s): Mukundan, R; Baker, AM; Kusoglu, A; Beattie, P; Knights, S; Weber, AZ; Borup, RL | Abstract: © The Author(s) 2018. A combined chemical/mechanical accelerated stress test (AST) was developed for proton exchange membrane (PEM) fuel cells based on relative humidity cycling (RHC) between dry and saturated gases at open circuit voltage (OCV). Membrane degradation and failure were investigated using scanning electron microscopy and small- and wide-angle X-ray scattering. Changes to membrane thickness, hydrophilic domain spacing, and crystallinity were observed to be most similar between field-operated cells and OCV RHC ASTs, where local thinning and divot-type defects are the primary failure modes. While RHC in air also reproduces these failure modes, it is not aggressive enough to differentiate between different membrane types in g1,333 hours (55 days) of testing. Conversely, steady-state OCV tests result in significant ionomer morphology changes and global thinning, which do not replicate field degradation and failure modes. It is inferred that during the OCV RHC AST, the decay of the membrane’s mechanical properties is accelerated such that materials can be evaluated in hundreds, instead of thousands, of hours, while replicating the degradation and failure modes of field operation; associated AST protocols are recommended as OCV RHC at 90◦C for 500 hours with wet/dry cycle durations of 30s/45s and 2m/2m for automotive and bus operation, respectively.

[1]  A. Wokaun,et al.  Local Degradation at Membrane Defects in Polymer Electrolyte Fuel Cells , 2013 .

[2]  Matt Crum,et al.  Effective Testing Matrix for Studying Membrane Durability in PEM Fuel Cells: Part 2. Mechanical Durability and Combined Mechanical and Chemical Durability , 2006 .

[3]  S. Holdcroft,et al.  Progression in the Morphology of Fuel Cell Membranes upon Conjoint Chemical and Mechanical Degradation , 2016 .

[4]  Matt Crum,et al.  Effective Testing Matrix for Studying Membrane Durability in PEM Fuel Cells: Part I. Chemical Durability , 2006 .

[5]  A. Weber,et al.  Structure/property relationship of Nafion XL composite membranes , 2016 .

[6]  Erik Kjeang,et al.  Membrane degradation during combined chemical and mechanical accelerated stress testing of polymer electrolyte fuel cells , 2014 .

[7]  Ahmet Kusoglu,et al.  Effect of Mechanical Compression on Chemical Degradation of Nafion Membranes , 2014 .

[8]  A. Weber,et al.  STRUCTURE-TRANSPORT RELATIONSHIP OF PERFLUOROSULFONIC-ACID MEMBRANES IN DIFFERENT CATIONIC FORMS , 2016 .

[9]  R. Borup,et al.  Accelerated Testing of Carbon Corrosion and Membrane Degradation in PEM Fuel Cells , 2013 .

[10]  Ma Hong-cha.  Determination of Inorganic Anions in Drinking Water by Ion Chromatography , 2008 .

[11]  Xiao-Zi Yuan,et al.  Diagnosis of MEA degradation under accelerated relative humidity cycling , 2011 .

[12]  A. Weber,et al.  New Insights into Perfluorinated Sulfonic-Acid Ionomers. , 2017, Chemical reviews.

[13]  Monica Pica,et al.  Physical and chemical modification routes leading to improved mechanical properties of perfluorosulfonic acid membranes for PEM fuel cells , 2013 .

[14]  R. Rajapakse,et al.  Decay in Mechanical Properties of Catalyst Coated Membranes Subjected to Combined Chemical and Mechanical Membrane Degradation , 2015 .

[15]  W. Yoon,et al.  Study of Polymer Electrolyte Membrane Degradation under OCV Hold Using Bilayer MEAs , 2010 .

[16]  Eiji Endoh,et al.  Degradation study of MEA for PEMFCs under low humidity conditions , 2004 .

[17]  E. Kjeang,et al.  3D Failure Analysis of Pure Mechanical and Pure Chemical Degradation in Fuel Cell Membranes , 2017 .

[18]  A. Svensson,et al.  Degradation Rates of PEM Fuel Cells Running at Open Circuit Voltage , 2006 .

[19]  Minoru Inaba,et al.  Gas crossover and membrane degradation in polymer electrolyte fuel cells , 2006 .

[20]  Shohji Tsushima,et al.  Degradation Mechanism of PEMFC under Open Circuit Operation , 2006 .

[21]  Rodney L. Borup,et al.  Accelerated Testing Validation , 2011 .

[22]  K. Reifsnider,et al.  Mechanical Endurance of Polymer Electrolyte Membrane and PEM Fuel Cell Durability , 2006 .

[23]  A. Prasad,et al.  Cerium Migration during PEM Fuel Cell Accelerated Stress Testing , 2016 .

[24]  Kazuhiko Shinohara,et al.  Membrane Degradation Behavior during Open-Circuit Voltage Hold Test , 2007 .

[25]  Mahlon Wilson,et al.  Scientific aspects of polymer electrolyte fuel cell durability and degradation. , 2007, Chemical reviews.

[26]  Alexander Wokaun,et al.  Investigation of membrane degradation in polymer electrolyte fuel cells using local gas permeation analysis , 2012 .

[27]  M. Chandesris,et al.  Membrane degradation in PEM fuel cells: From experimental results to semi-empirical degradation laws , 2017 .

[28]  F. de Bruijn,et al.  Review: Durability and Degradation Issues of PEM Fuel Cell Components , 2008 .

[29]  Ahmet Kusoglu,et al.  Electrochemical/mechanical coupling in ion-conducting soft matter. , 2015, The journal of physical chemistry letters.

[30]  Deborah J. Jones,et al.  Current understanding of chemical degradation mechanisms of perfluorosulfonic acid membranes and their mitigation strategies: a review , 2017 .

[31]  S. Knights,et al.  Effect of catalyst layer defects on local membrane degradation in polymer electrolyte fuel cells , 2016 .

[32]  B. Pivovar,et al.  Effect of Relative Humidity on Membrane Degradation Rate and Mechanism in PEM Fuel Cells , 2007 .

[33]  G. G. Wang,et al.  Creep properties of catalyst coated membranes for polymer electrolyte fuel cells , 2015 .

[34]  T. Nejat Veziroğlu,et al.  Polymer electrolyte fuel cell degradation , 2012 .

[35]  W. B. Johnson,et al.  Mechanical response of fuel cell membranes subjected to a hygro-thermal cycle , 2006 .

[36]  H. R. Kunz,et al.  Perfluorinated Sulfonic Acid Membrane and Membrane Electrode Assembly Degradation Correlating Accelerated Stress Testing and Lifetime Testing , 2013 .

[37]  G. G. Wang,et al.  Microstructural and Mechanical Characterization of Catalyst Coated Membranes Subjected to In Situ Hygrothermal Fatigue , 2015 .

[38]  Hiroshi Komiyama,et al.  Influence of Deposition Temperature on the Microstructure of Pb-Ti-Nb-O Thin Films by Metallorganic Chemical Vapor Deposition , 2001 .

[39]  Michael H. Santare,et al.  Numerical Investigation of Mechanical Durability in Polymer Electrolyte Membrane Fuel Cells , 2010 .

[40]  Xiao‐Zi Yuan,et al.  Accelerated durability testing via reactants relative humidity cycling on PEM fuel cells , 2012 .

[41]  H. R. Kunz,et al.  Fuel cell perfluorinated sulfonic acid membrane degradation correlating accelerated stress testing and lifetime. , 2012, Chemical reviews.

[42]  Dai-jun Yang,et al.  Proton exchange membrane fuel cell degradation under close to open-circuit conditions: Part I: In situ diagnosis , 2010 .

[43]  M. Hicks,et al.  Accelerated Testing and Lifetime Modeling for the Development of Durable Fuel Cell MEAs , 2006 .