Wear resistance of experimental titanium alloys for dental applications.

The present study evaluated microstructure, microhardness and wear resistance of experimental titanium alloys containing zirconium and tantalum. Alloys were melted in arc melting furnace according to the following compositions: Ti-5Zr, Ti-5Ta and Ti-5Ta-5Zr (%wt). Hemispheres and disks were obtained from wax patterns that were invested and cast by plasma. Microstructures were evaluated using optical microscopy and X-ray diffraction (XRD) analysis and also Vickers microhardness was measured. Hemispherical samples and disks were used for 2-body wear tests, performed by repeated grinding of the samples. Wear resistance was assessed as height loss after 40,000 cycles. The data were compared using ANOVA and post-hoc Tukey test. Ti-5Zr presented a Widmanstätten structure and the identified phases were α and α' while Ti-5Ta and Ti-5Ta-5Zr presented α, β, α' and α" phases, but the former presented a lamellar structure, and the other, acicular. The microhardness of Ti-5Zr was significantly greater than other materials and cp Ti presented wear resistance significantly lower than experimental alloys. It was concluded that wear resistance was improved when adding Ta and Zr to titanium and Zr increased microhardness of Ti-5Zr alloy.

[1]  S. R. Biaggio,et al.  Electrochemical studies on zirconium and its biocompatible alloys Ti-50Zr at.% and Zr-2.5Nb wt.% in simulated physiologic media. , 2005, Journal of biomedical materials research. Part A.

[2]  S. Heintze.  How to qualify and validate wear simulation devices and methods. , 2006, Dental materials : official publication of the Academy of Dental Materials.

[3]  S. R. Seagle,et al.  Considerations in processing titanium , 1999 .

[4]  G. Texier,et al.  Development of a β-type Ti–12Mo–5Ta alloy for biomedical applications: cytocompatibility and metallurgical aspects , 2004, Journal of materials science. Materials in medicine.

[5]  T Hosoi,et al.  Wear resistance of experimental Ti-Cu alloys. , 2003, Biomaterials.

[6]  Hsueh-Chuan Hsu,et al.  Structure, mechanical properties, and grindability of dental Ti–Zr alloys , 2008, Journal of materials science. Materials in medicine.

[7]  P. Schmidlin,et al.  Attritional wear and abrasive surface alterations of composite resin materials in vitro. , 2002, Journal of dentistry.

[8]  R. Legeros,et al.  An evaluation of wear when enamel is opposed by various ceramic materials and gold. , 2006, The Journal of prosthetic dentistry.

[9]  S. Hanatani,et al.  Present status of titanium removable dentures--a review of the literature. , 2008, Journal of oral rehabilitation.

[10]  E P Lautenschlager,et al.  Titanium and titanium alloys as dental materials. , 1993, International dental journal.

[11]  P. Lambrechts,et al.  An in vitro wear study of posterior denture tooth materials on human enamel. , 2001, Journal of oral rehabilitation.

[12]  M. Koike,et al.  Modeling wear of cast Ti alloys. , 2007, Acta biomaterialia.

[13]  Chikahiro Ohkubo,et al.  In vitro wear resistance of three types of composite resin denture teeth. , 2005, The Journal of prosthetic dentistry.

[14]  V. Rousson,et al.  A comparison of three different methods for the quantification of the in vitro wear of dental materials. , 2006, Dental materials : official publication of the Academy of Dental Materials.

[15]  T. Okabe,et al.  The Use of Titanium in Dentistry , 1995 .

[16]  C. Ju,et al.  Structure-property relationship of cast Ti-Nb alloys. , 2002, Journal of oral rehabilitation.

[17]  M. Bonnaure-Mallet,et al.  Evaluation of the biocompatibility of titanium-tantalum alloy versus titanium. , 1998, Journal of biomedical materials research.

[18]  Chikahiro Ohkubo,et al.  In vitro wear assessment of titanium alloy teeth. , 2002, Journal of prosthodontics : official journal of the American College of Prosthodontists.

[19]  Xin Hu,et al.  Study of the surface wear resistance and biological properties of the Ti–Zr–Nb–Sn alloy for dental restoration , 2010, Biomedical materials.

[20]  H. Rack,et al.  Titanium alloys in total joint replacement--a materials science perspective. , 1998, Biomaterials.

[21]  R. Ribeiro,et al.  Effect of repeated torque/mechanical loading cycles on two different abutment types in implants with internal tapered connections: an in vitro study. , 2009, Clinical oral implants research.

[22]  C. Ju,et al.  Structure and properties of cast binary Ti-Mo alloys. , 1999, Biomaterials.

[23]  Y. Oda,et al.  Mechanical properties of cast Ti-6Al-4V-XCu alloys. , 2004, Journal of oral rehabilitation.

[24]  H. Doi,et al.  Influence of aging heat treatment on mechanical properties of biomedical Ti–Zr based ternary alloys containing niobium , 1998, Journal of materials science. Materials in medicine.

[25]  E. Eisenbarth,et al.  Biocompatibility of β-stabilizing elements of titanium alloys , 2004 .

[26]  Masafumi Kikuchi,et al.  Mechanical properties and microstructures of cast Ti-Cu alloys. , 2003, Dental materials : official publication of the Academy of Dental Materials.

[27]  T Hosoi,et al.  The machinability of cast titanium and Ti-6Al-4V. , 2000, Biomaterials.