High internal phase emulsion templating as a route to well-defined porous polymers

Abstract The use of high internal phase emulsions (HIPEs) as templates to create highly porous materials (PolyHIPEs) is described. Polymerisation occurs around emulsion droplets, which create voids in the final material. The void fraction is very high and can reach levels of 0.99. Varying the emulsion composition can control features of the morphology of the resulting porous materials, such as the void diameter and degree of interconnection. Other parameters can also be varied, for example surface area can be increased from 3 to around 700 m 2  g −1 . Rubbery materials can be produced from hydrophobic elsatomers and PolyHIPEs with high thermo-oxidative stability are prepared from high performance materials such as poly(ether sulfone). The highly porous materials so produced are finding applications in areas such as solid supported organic chemistry, sensors, cell culturing and tissue engineering.

[1]  D. Sherrington,et al.  High internal phase emulsions (HIPEs) — Structure, properties and use in polymer preparation , 1996 .

[2]  N. Cameron,et al.  Tissue engineering matrixes by emulsion templating , 2002 .

[3]  J. M. Williams,et al.  Emulsion stability and rigid foams from styrene or divinylbenzene water-in-oil emulsions , 1990 .

[4]  P. Becher,et al.  Encyclopedia of emulsion technology , 1983 .

[5]  N. Cameron,et al.  Enhanced neurite outgrowth by human neurons grown on solid three-dimensional scaffolds. , 2004, Biochemical and biophysical research communications.

[6]  Neil R. Cameron,et al.  Preparation and glass transition temperatures of elastomeric PolyHIPE materials , 1997 .

[7]  J. Duke,et al.  Functionalized polymer foams as metal ion chelating agents with rapid complexation kinetics , 1998 .

[8]  D. Sherrington,et al.  Immobilization of flavin on highly porous polymeric disks: Three routes to a catalytically active membrane , 1992 .

[9]  H. Deleuze,et al.  Thiol Addition to the Pendant Vinylbenzene Groups of (Vinyl)polystyrene PolyHIPE Via a Batch and a Cross‐Flow Method , 2001 .

[10]  D. Sherrington,et al.  PolyHipe: A new polymeric support for heterogeneous catalytic reactions: Kinetics of hydration of cyclohexene in two- and three-phase systems over a strongly acidic sulfonated polyhipe , 2000 .

[11]  A. Cooper,et al.  Synthesis of porous emulsion-templated polymers using high internal phase CO2-in-water emulsions. , 2003, Journal of the American Chemical Society.

[12]  A. Cooper.  Porous Materials and Supercritical Fluids , 2003 .

[13]  O. Mondain-Monval,et al.  Preparation and functionalization of (vinyl)polystyrene polyHIPE®.: Short routes to binding functional groups through a dimethylene spacer , 2000 .

[14]  D. A. Wrobleski,et al.  Spatial distribution of the phases in water-in-oil emulsions. Open and closed microcellular foams from cross-linked polystyrene , 1988 .

[15]  A. Barbetta,et al.  Morphology and Surface Area of Emulsion-Derived (PolyHIPE) Solid Foams Prepared with Oil-Phase Soluble Porogenic Solvents: Three-Component Surfactant System , 2004 .

[16]  P. Krajnc,et al.  Monolithic scavenger resins by amine functionalizations of poly(4-vinylbenzyl chloride-co-divinylbenzene) PolyHIPE materials. , 2002, Organic letters.

[17]  K. J. Lissant.  Emulsions and Emulsion Technology. Part 1 , 1974 .

[18]  P. Krajnc,et al.  Aryl acrylate based high‐internal‐phase emulsions as precursors for reactive monolithic polymer supports , 2005 .

[19]  R. Wakeman,et al.  Self-supported porous channel filtration modules : preparation, properties and performance : Advanced materials , 1995 .

[20]  F. Švec,et al.  Monolithic materials : preparation, properties and applications , 2003 .

[21]  D. Sherrington,et al.  Synthesis and characterization of poly(aryl ether sulfone) PolyHIPE materials , 1997 .

[22]  N. Cameron,et al.  Emulsion-Derived Foams (PolyHIPEs) Containing Poly(ε-caprolactone) as Matrixes for Tissue Engineering , 2001 .

[23]  A. Barbetta,et al.  High internal phase emulsions (HIPEs) containing divinylbenzene and 4-vinylbenzyl chloride and the morphology of the resulting PolyHIPE materials , 2000 .

[24]  A. Barbetta,et al.  The influence of porogen type on the porosity,surface area and morphology of poly(divinylbenzene) PolyHIPE foams , 2000 .

[25]  D. Sherrington,et al.  Non-aqueous high internal phase emulsions. Preparation and stability , 1996 .

[26]  David C. Sherrington,et al.  Synthesis and ultrastructural studies of styrene-divinylbenzene Polyhipe polymers , 1991 .

[27]  A. Barbetta,et al.  Morphology and Surface Area of Emulsion-Derived (PolyHIPE) Solid Foams Prepared with Oil-Phase Soluble Porogenic Solvents: Span 80 as Surfactant , 2004 .

[28]  D. Sherrington,et al.  Chemical modification of monolithic poly(styrene–divinylbenzene) polyHIPE® materials , 1996 .

[29]  D. P. Gregory,et al.  Study of the formation of the open-cellular morphology of poly(styrene/divinylbenzene) polyHIPE materials by cryo-SEM , 1996 .

[30]  J. M. Barton.  Relation of glass transition temperature to molecular structure of addition copolymers , 2007 .

[31]  D. Sherrington,et al.  Design and application of a new rigid support for high efficiency continuous-flow peptide synthesis , 1989 .

[32]  D. Sherrington,et al.  Syntheses and Separations Using Functional Polymers , 1988 .

[33]  A. Cooper,et al.  Emulsion Templating Using High Internal Phase Supercritical Fluid Emulsions , 2001 .

[34]  B. Benicewicz,et al.  Open-celled polymeric foam monoliths for heavy metal separations study , 1998 .