ON-state reliability of GaN-on-Si Schottky Barrier Diodes: Si3N4 vs. Al2O3/SiO2 GET dielectric

The degradation of Schottky Barrier Diodes (SBDs) with a Gated Edge Termination (GET) under on-state stress conditions is studied for a 650 V GaN-on-Si technology. Reliability metric techniques previously used in MOS-HEMTs are applied in this work due to a similar MIS gate stack architecture in GET-SBDs. Here, the density of traps is analyzed in GET structures where the dielectric is either Si3N4 (nitride-based) or a stack of Al2O3/SiO2 (oxide-based). Statistical analysis across two wafers indicates some systematic differences in turn-on voltage degradation depending on wafer location, likely caused by process-related variations. Under 1000 s stress time and ON-state voltage, the number of trapped charges in nitride-based dielectric devices keeps increasing. This suggests an ongoing dielectric degradation. On the other hand, Al2O3/SiO2 dielectric devices with an Al-based interfacial layer (IL) exhibit less process-induced variability across the wafer along with a lower density of trapped charges compared with nitride-based dielectric diodes under the same stress conditions suggesting better reliability and process improvement.

[1]  Sandeep R. Bahl,et al.  A Generalized Approach to Determine the Switching Lifetime of a GaN FET , 2020, 2020 IEEE International Reliability Physics Symposium (IRPS).

[2]  Dirk Wellekens,et al.  Au-Free AlGaN/GaN Power Diode on 8-in Si Substrate With Gated Edge Termination , 2013, IEEE Electron Device Letters.

[3]  L. Trojman,et al.  On recoverable behavior of PBTI in AlGaN/GaN MOS-HEMT , 2017 .

[4]  Kazushige Horio,et al.  Numerical Analysis of Breakdown Voltage Enhancement in AlGaN/GaN HEMTs With a High-$k$ Passivation Layer , 2014, IEEE Transactions on Electron Devices.

[5]  R. Degraeve,et al.  Insight Into N/PBTI Mechanisms in Sub-1-nm-EOT Devices , 2012, IEEE Transactions on Electron Devices.

[6]  S. Decoutere,et al.  Reliability Improvements in AlGaN/GaN Schottky Barrier Diodes With a Gated Edge Termination , 2018, IEEE Transactions on Electron Devices.

[7]  D. Pogany,et al.  Enhancement of Vth drift for repetitive gate stress pulses due to charge feedback effect in GaN MIS-HEMTs , 2014, 2014 IEEE International Reliability Physics Symposium.

[8]  Lester F. Eastman,et al.  Two-dimensional electron gases induced by spontaneous and piezoelectric polarization charges in N- and Ga-face AlGaN/GaN heterostructures , 1999 .

[9]  J. Croon,et al.  Extensive Investigation of Time-Dependent Breakdown of GaN-HEMTs Submitted to OFF-State Stress , 2015, IEEE Transactions on Electron Devices.

[10]  D. Pogany,et al.  Comprehensive Study of the Complex Dynamics of Forward Bias-Induced Threshold Voltage Drifts in GaN Based MIS-HEMTs by Stress/Recovery Experiments , 2014, IEEE Transactions on Electron Devices.

[11]  Steven A. Ringel,et al.  Interface trap characterization of atomic layer deposition Al2O3/GaN metal-insulator-semiconductor capacitors using optically and thermally based deep level spectroscopies , 2013 .

[12]  T. Grasser,et al.  The “permanent” component of NBTI revisited: Saturation, degradation-reversal, and annealing , 2016, 2016 IEEE International Reliability Physics Symposium (IRPS).

[13]  Guido Groeseneken,et al.  Toward Understanding Positive Bias Temperature Instability in Fully Recessed-Gate GaN MISFETs , 2016, IEEE Transactions on Electron Devices.

[14]  S. Decoutere,et al.  Reliability in GaN-based devices for power applications , 2018, 2018 IEEE Third Ecuador Technical Chapters Meeting (ETCM).

[15]  S. Decoutere,et al.  Statistical Analysis of the Impact of Anode Recess on the Electrical Characteristics of AlGaN/GaN Schottky Diodes With Gated Edge Termination , 2016, IEEE Transactions on Electron Devices.