Metal contact recombination in monoPoly™ solar cells with screen-printed & fire-through contacts

Abstract We present a detailed analysis of the contact properties with screen printed fire-through (FT) metal pastes on phosphorus doped (n+) polysilicon (poly-Si) layers. Two different pastes are evaluated for their contact resistivity and contact recombination on n+ doped poly-Si and on n+ doped c-Si. We present excellent contact resistivity (ρc) values ~ 1.5 mΩ-cm2 measured by the transfer length method (TLM) for metal contacts with doped poly-Si layer. The recombination at the metallized contacts is evaluated by analyzing the photoluminescence of the samples together with the Griddler software. In this work, we report ultra-low saturation current density values of 35 fA/cm2 under the metal contacts. We demonstrate that solar cells with a rear passivated contact show an average + 16 mV improvement in cell open circuit voltage as compared to the standard cells when using well-suited rear metal pastes. Efficiency of 21.8% is reported for cells printed with the best performing paste on large-area (244.3 cm2) commercially available n-type Czochralski grown Si wafers.

[1]  S. Wenham,et al.  Edge isolation of solar cells using laser doping , 2015 .

[2]  Ralf Preu,et al.  Recombination at Metal-Emitter Interfaces of Front Contact Technologies for Highly Efficient Silicon Solar Cells , 2011 .

[3]  S. Glunz,et al.  n-Type Si solar cells with passivating electron contact: Identifying sources for efficiency limitations by wafer thickness and resistivity variation , 2017 .

[4]  Vinodh Shanmugam,et al.  Influence of random pyramid surface texture on silver screen-printed contact formation for monocrystalline silicon wafer solar cells , 2015 .

[5]  Yuehua Wu,et al.  Study of screen printed metallization for polysilicon based passivating contacts , 2017 .

[6]  Vinodh Shanmugam,et al.  Towards 22% efficient screen-printed bifacial n-type silicon solar cells , 2018, Solar Energy Materials and Solar Cells.

[7]  Jan-Dirk Kähler,et al.  Parasitic Absorption in Polycrystalline Si-layers for Carrier-selective Front Junctions , 2016 .

[8]  A. Cuevas,et al.  Phosphorus-diffused polysilicon contacts for solar cells , 2015 .

[9]  R. M. Swanson,et al.  A 720 mV open circuit voltage SiOx:c‐Si:SiOx double heterostructure solar cell , 1985 .

[10]  W. Kern.  The Evolution of Silicon Wafer Cleaning Technology , 1990 .

[11]  E. C. Campos.  Screen Printed Silver Contacting Interface in Industrial Crystalline Silicon Solar Cells , 2013 .

[12]  A. Gabor,et al.  Detailed investigation of TLM contact resistance measurements on crystalline silicon solar cells , 2017 .

[13]  S. Glunz,et al.  Passivated rear contacts for high-efficiency n-type Si solar cells providing high interface passivation quality and excellent transport characteristics , 2014 .

[14]  D. Kray.  Modeling, geometric optimization and isolation of the edge region in silicon solar cells , 2010 .

[15]  E. Wefringhaus,et al.  Influence of Surface Topography on the Glass Coverage in the Contact Formation of Silver Screen-Printed Si Solar Cells , 2013, IEEE Journal of Photovoltaics.

[16]  Ingrid G. Romijn,et al.  n-Type polysilicon passivating contact for industrial bifacial n-type solar cells , 2016 .

[17]  Hee‐eun Song,et al.  Structural evolution of tunneling oxide passivating contact upon thermal annealing , 2017, Scientific Reports.

[18]  P. Altermatt,et al.  The effect of sample edge recombination on the averaged injection-dependent carrier lifetime in silicon , 2012 .

[19]  E. Bugiel,et al.  Working principle of carrier selective poly-Si/c-Si junctions: Is tunnelling the whole story? , 2016 .

[20]  M. Ernst,et al.  Passivated contacts to laser doped p+ and n+ regions , 2015 .

[21]  M. Abbott,et al.  Investigation of edge recombination effects in silicon solar cell structures using photoluminescence , 2006 .

[22]  A. Rohatgi,et al.  Tunnel oxide passivated rear contact for large area n -type front junction silicon solar cells providing excellent carrier selectivity , 2016 .

[23]  Evan Franklin,et al.  Phosphorus diffused LPCVD polysilicon passivated contacts with in-situ low pressure oxidation , 2018, Solar Energy Materials and Solar Cells.

[24]  A. Aberle,et al.  monoPoly™ cells: Large-area crystalline silicon solar cells with fire-through screen printed contact to doped polysilicon surfaces , 2018, Solar Energy Materials and Solar Cells.

[25]  New measurement method for the investigation of space charge region recombination losses induced by the metallization of silicon solar cells , 2011 .

[26]  Evaluation of recombination processes using the local ideality factor of carrier lifetime measurements , 2013 .

[27]  A. Stassen,et al.  Electrical and Microstructural Analysis of Contact Formation on Lightly Doped Phosphorus Emitters Using Thick-Film Ag Screen Printing Pastes , 2014, IEEE Journal of Photovoltaics.

[28]  Frank Feldmann,et al.  The application of poly-Si/SiOx contacts as passivated top/rear contacts in Si solar cells , 2017 .

[29]  Vinodh Shanmugam,et al.  Impact of the phosphorus emitter doping profile on metal contact recombination of silicon wafer solar cells , 2016 .

[30]  D. Biro,et al.  Impact of screen printing silver paste components on the space charge region recombination losses of industrial silicon solar cells , 2012 .

[31]  D. Inns.  Understanding Metal Induced Recombination Losses in Silicon Solar Cells with Screen Printed Silver Contacts , 2016 .

[32]  J. Luchies,et al.  Metallisation of Boron‐Doped Polysilicon Layers by Screen Printed Silver Pastes , 2017 .

[33]  Vinodh Shanmugam,et al.  Determination of metal contact recombination parameters for silicon wafer solar cells by photoluminescence imaging , 2015 .

[34]  Vinodh Shanmugam,et al.  Quantifying edge and peripheral recombination losses in industrial silicon solar cells , 2015, IEEE Transactions on Electron Devices.

[35]  M. Werner,et al.  Tunnel oxide passivated carrier-selective contacts based on ultra-thin SiO2 layers grown by photo-oxidation or wet-chemical oxidation in ozonized water , 2015, 2015 IEEE 42nd Photovoltaic Specialist Conference (PVSC).

[36]  J. Luchies,et al.  Material properties of LPCVD processed n-type polysilicon passivating contacts and its application in PERPoly industrial bifacial solar cells , 2017 .

[37]  Y. Chabal.  Fundamental aspects of silicon oxidation , 2001 .