Oxidation behavior of stainless steels 304 and 316 under the Venus atmospheric surface conditions

Abstract In general support of planetary exploration missions, the chemical, structural and microstructural behavior of stainless steels 304 and 316 was probed after exposure to a gas mixture with temperature, pressure, and composition mimicking the Venus lower atmosphere. Exposures were carried out in the Glenn Extreme Environments Rig (GEER) chamber with the Venusian gas mixture (96.5% CO2, 3.5% N2, 30 ppm H2O, 150 ppm SO2, 28 ppm CO, 15 ppm OCS, 3 ppm H2S, 0.5 ppm HCl and 5 ppb HF) at 9.2 × 106 Pa and 740 K for a duration of 10, 21, and 42 days. Stainless steel 304 and 316 samples were characterized before and after the experiment by gravimetric analysis, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and cross-section electron microscopy analysis. All samples exposed to the Venusian atmosphere formed double-layered scales in which the outer layer is mainly magnetite (Fe3O4) and the inner layer is mainly spinel (Fe3-xCrxO4). Nickel sulfide and oxide formed at the interface of stainless steel 304. Nickel sulfide also formed in the inner and outer layer of the stainless steel 316 scale. Chromium carbide was only detected by Auger analysis at the interface of the unpolished side of the stainless steel 304 coupon sample. Stainless steel 304 with its smoother surface (780.62 nm total roughness on the polished side and 3.57 μm on the unpolished side) and slightly higher chromium and slightly lower nickel content, exhibited slower kinetics of oxidation (3.1 ± 0.5 × 10−3 mg cm−2 day−1) than stainless steel 316 (0.05 ± 0.07 mg cm−2 day−1) with its rougher surface (4.78 μm total roughness on both sides). The slightly higher molybdenum content in stainless steel 316 was also responsible for increasing its kinetics of oxidation because of the formation of molybdenum sulfide. Our thermodynamic calculations of the phase assemblage containing the Venus gas mixture and the stainless steel samples predicted hematite Cr2O3(s), Fe2O3(s), CrS(l), Cr2S3(l), NiS(l), FeS(l), CrO(l), H2(g), HCl(g), HF(g), NH3(g) and H2S(g) as the thermodynamically stable phases formed at the Venus atmospheric conditions.

[1]  N. J. Cory,et al.  The location of hydrogen in the kinetics of oxidation of ferrous alloys by superheated steam , 1988 .

[2]  H. Kyung,et al.  Microstructural evolution of duplex grain structure and interpretation of the mechanism for NiO scales grown on pure Ni- and Cr-doped substrates during high temperature oxidation , 2000 .

[3]  Gunnar Eriksson,et al.  FactSage thermochemical software and databases , 2002 .

[4]  W. Quadakkers,et al.  Steam oxidation of ferritic steels – laboratory test kinetic data , 2005 .

[5]  J. Robertson The mechanism of high temperature aqueous corrosion of stainless steels , 1991 .

[6]  F. Balbaud-Célérier,et al.  Oxidation mechanism of a Fe–9Cr–1Mo steel by liquid Pb–Bi eutectic alloy (Part I) , 2008 .

[7]  J. Robertson,et al.  Criteria for formation of single layer, duplex, and breakaway scales on steels , 1988 .

[8]  G. Y. Lai,et al.  High Temperature Corrosion of Engineering Alloys , 1990 .

[9]  G. Was,et al.  Oxidation of ferritic–martensitic alloys T91, HCM12A and HT-9 in supercritical water , 2007 .

[10]  D. Young High Temperature Oxidation and Corrosion of Metals , 2008 .

[11]  S. Bosonnet,et al.  Oxidation mechanism of an Fe–9Cr–1Mo steel by liquid Pb–Bi eutectic alloy at 470 °C (Part II) , 2008 .

[12]  P. Kofstad On the formation of porosity and microchannels in growing scales , 1985 .

[13]  Marie-Aline Van Ende,et al.  FactSage thermochemical software and databases, 2010–2016 , 2016 .

[14]  G. Moine,et al.  Corrosion Behavior Of Different Metallic Materials In Supercritical CO2At 550°C And 250 Bars , 2010 .

[15]  Yasuyoshi Kato Advanced High Temperature Gas-Cooled Reactor Systems , 2010 .

[16]  Mark H. Anderson,et al.  Corrosion of austenitic and ferritic-martensitic steels exposed to supercritical carbon dioxide , 2011 .

[17]  Fu-hui Wang,et al.  The Effect of Surface Finish on the Scaling Behavior of Stainless Steel in Steam and Supercritical Water , 2013, Oxidation of Metals.

[18]  G. B. Gibbs,et al.  The influence of metal lattice vacancies on the oxidation of high temperature materials , 1977 .

[19]  M. Warzée,et al.  Effect of Surface Treatment on the Corrosion of Stainless Steels in High‐Temperature Water and Steam , 1965 .

[20]  A. Atkinson,et al.  Transport of Nickel and Oxygen during the Oxidation of Nickel and Dilute Nickel/Chromium Alloy , 1988 .

[21]  J. Keiser,et al.  The Effect of Temperature and Pressure on Supercritical CO2 Compatibility of Conventional Structural Alloys , 2016 .

[22]  S. Nešić,et al.  Effect Of Water Content On The Corrosion Behavior Of Carbon Steel In Supercritical Co2 Phase With Impurities , 2011 .

[23]  R. Hales,et al.  The role of metal lattice vacancies in the hightemperature oxidation of nickel , 1972 .

[24]  A. Brückman The mechanism of transport of matter through the scales during oxidation of metals and alloys , 1967 .

[25]  L. Tomlinson,et al.  Hydrogen emission during the steam oxidation of ferritic steels: Kinetics and mechanism , 1989 .

[26]  J. Romański,et al.  On the mechanism of sulphide scale formation on iron , 1965 .

[27]  M. Anderson,et al.  Corrosion of austenitic alloys in high temperature supercritical carbon dioxide , 2012 .