Experimental and Numerical Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

In the paper corrosion-induced crack initiation and propagation are investigated experimentally and numerically, with particular emphasis on quantifying the proportion of corrosion products that are dissipated within the concrete pores and cracks, thus reducing the pressure exerted by corrosion products on the surrounding concrete. Initially, experimental data on crack initiation and propagation obtained from accelerated corrosion tests of reinforced concrete slabs are presented. A comparison of finite-element model results and experimental data is used to estimate the amount of corrosion products penetrating into concrete pores and cracks, which is an essential parameter for prediction of corrosion initiation and propagation. It was found that the amount of corrosion products penetrating into the concrete pores before crack initiation is larger than that obtained by other researchers. The paper also showed that corrosion products do not fully fill corrosion-induced cracks in concrete immediately after their initiation as the cracks are being filled gradually over time and the thicker the concrete cover the longer it will take to fully fill a crack.

[1]  A. Bentur.  Steel corrosion in concrete , 1997 .

[2]  Masayasu Ohtsu,et al.  Analysis of crack propagation and crackinitiation due to corrosion of reinforcement , 1997 .

[3]  X. H. Wang,et al.  Modelling effects of corrosion on cover cracking and bond in reinforced concrete , 2004 .

[4]  Comite Euro-International du Beton,et al.  CEB-FIP Model Code 1990 , 1993 .

[5]  M Maage,et al.  SERVICE LIFE PREDICTION OF EXISTING CONCRETE STRUCTURES EXPOSED TO MARINE ENVIRONMENT , 1996 .

[7]  L. Wood,et al.  Concrete Uniaxial Tensile Strength and Cylinder Splitting Test , 2003 .

[8]  Stavroula J. Pantazopoulou,et al.  Modeling Cover-Cracking due to Reinforcement Corrosion in RC Structures , 2001 .

[9]  Andrés A. Torres-Acosta,et al.  Residual Life of Corroding Reinforced Concrete Structures in Marine Environment , 2003 .

[10]  Z. Bažant.  Closure of "Physical Model for Steel Corrosion in Concrete Sea Structures—Application" , 1980 .

[11]  Rasheeduzzafar,et al.  CORROSION CRACKING IN RELATION TO BAR DIAMETER, COVER, AND CONCRETE QUALITY , 1992 .

[12]  C. Andrade,et al.  Factors controlling cracking of concrete affected by reinforcement corrosion , 1998 .

[13]  Modeling of concrete cracking due to corrosion of embedded reinforcement , 1999 .

[14]  M. S. Elgarf,et al.  Bond characteristics of corrding reinforcement in concrete beams , 1999 .

[15]  Kapilesh Bhargava,et al.  Model for cover cracking due to rebar corrosion in RC structures , 2006 .

[16]  Thierry Vidal,et al.  ANALYZING CRACK WIDTH TO PREDICT CORROSION IN REINFORCED CONCRETE , 2004 .

[17]  Cruz Alonso,et al.  Cover cracking as a function of bar corrosion: Part I-Experimental test , 1993 .

[18]  S. J. Williamson,et al.  Pressure required to cause cover cracking of concrete due to reinforcement corrosion , 2000 .

[19]  Palle Thoft-Christensen.  Service Life Definitions based on Corrosion Crack Width , 2005 .

[20]  Hirozo Mihashi,et al.  Cover cracking of reinforced concrete beams due to corrosion of steel , 2007 .

[21]  J. Rodriguez,et al.  Corrosion of Reinforcement and Service Life of Concrete Structures , 1996 .

[22]  Cruz Alonso,et al.  Cover cracking as a function of rebar corrosion: Part 2—Numerical model , 1993 .

[23]  Khaled Soudki,et al.  A model for prediction of time from corrosion initiation to corrosion cracking , 2007 .

[24]  A. Hillerborg,et al.  Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements , 1976 .

[25]  A. Neville.  Properties of Concrete , 1968 .

[26]  Masayasu Ohtsu,et al.  Mechanisms of crack propagation due to corrosion of reinforcement in concrete by AE-SiGMA and BEM , 2003 .

[27]  M. Berra,et al.  Steel-concrete bond deterioration due to corrosion: finite-element analysis for different confinement levels , 2003 .

[28]  Koichi Maekawa,et al.  Simulation of Coupled Corrosive Product Formation, Migration into Crack and Propagation in Reinforced Concrete Sections , 2005 .

[29]  J. G. Cabrera,et al.  Deterioration of concrete due to reinforcement steel corrosion , 1996 .

[30]  V. Saouma,et al.  Numerical Simulation of Reinforced Concrete Deterioration: Part 2—Steel Corrosion and Concrete Cracking , 1999 .

[31]  S. Kulendran,et al.  Finite Element Modeling of Corrosion Damage in Concrete Structures , 1992 .

[32]  J. Padovan,et al.  FE MODELING OF EXPANSIVE OXIDE INDUCED FRACTURE OF REBAR REINFORCED CONCRETE , 1997 .

[33]  Dimitri V. Val,et al.  Effect of Different Limit States on Life-Cycle Cost of RC Structures in Corrosive Environment , 2005 .

[34]  Tim Topper,et al.  Long-Term Performance of Corrosion-Damaged Reinforced Concrete Beams , 2005 .

[35]  Mark G. Stewart,et al.  Corrosion-Induced Cracking: Experimental Data and Predictive Models , 2005 .

[36]  Christopher K.Y. Leung,et al.  Modeling of concrete cracking induced by steel expansion , 2001 .

[37]  K. Lundgren,et al.  Modelling the effect of corrosion on bond in reinforced concrete , 2002 .

[38]  Richard E. Weyers,et al.  MODELING THE TIME-TO-CORROSION CRACKING IN CHLORIDE CONTAMINATED REINFORCED CONCRETE STRUCTURES , 1998 .

[39]  Andrew Chan,et al.  Finite element analysis of the effects of radial expansion of corroded reinforcement , 2006 .