A geopolymer mortar for wood and earth structures

Abstract In building construction, because of the hygroscopic nature of wood and earth brick and the low adhesion between these materials, cracks are formed at their interface when they are assembled. Geopolymer binder has been show to create strong bonds between wood and earth brick. Assemblies of wood and extruded earth brick with geopolymer binder were manufacture and tested. Double shear tests at two scales were carried out that provided evidence of good adhesion and information about the influence of the type of brick on shear behavior. The workability of the binder was improved by adding siliceous aggregates. The mortar obtained has an improved compressive strength, ranging from 3 to 8 MPa, depending on the aggregate size. FTIR measurements and thermal analysis were performed to determine the reaction mechanism.

[1]  A. Neville.  Properties of Concrete , 1968 .

[2]  G. Corder,et al.  Costs and carbon emissions for geopolymer pastes in comparison to ordinary portland cement , 2011 .

[3]  B. V. Venkatarama Reddy,et al.  Embodied energy of common and alternative building materials and technologies , 2003 .

[4]  E. Prud'homme.  Rôles du cation alcalin et des renforts minéraux et végétaux sur les mécanismes de formation de géopolymères poreux ou denses , 2011 .

[5]  Séka Simplice Kouassi,et al.  Consolidation mechanism of materials obtained from sodium silicate solution and silica-based aggregates , 2011 .

[6]  J. Deventer,et al.  Geopolymer technology: the current state of the art , 2007 .

[7]  Waltraud M. Kriven,et al.  The effect of alkali and Si/Al ratio on the development of mechanical properties of metakaolin-based geopolymers , 2007 .

[8]  Hugo Houben,et al.  Traité de construction en terre , 1989 .

[9]  Peter Walker,et al.  Properties of some cement stabilised compressed earth blocks and mortars , 1997 .

[10]  R. Hedrich,et al.  Potassium-dependent wood formation in poplar: seasonal aspects and environmental limitations. , 2009, Plant biology.

[11]  M. Holtzer,et al.  FTIR analysis of bentonite in moulding sands , 2008 .

[12]  P. Michaud,et al.  Silica fume as porogent agent in geo-materials at low temperature , 2010 .

[13]  P. Michaud,et al.  Geomaterial Foam to Reinforce Wood , 2010 .

[14]  J. Norton,et al.  Building with earth. , 1997 .

[15]  Ajay Gupta,et al.  Influence of sand grading on the characteristics of mortars and soil–cement block masonry , 2008 .

[16]  J. V. Deventer,et al.  Use of Infrared Spectroscopy to Study Geopolymerization of Heterogeneous Amorphous Aluminosilicates , 2003 .

[17]  Plinio Innocenzi,et al.  Infrared spectroscopy of sol–gel derived silica-based films: a spectra-microstructure overview , 2003 .

[18]  P. Duxson,et al.  Effect of Alkali Cations on Aluminum Incorporation in Geopolymeric Gels , 2005 .

[19]  J. Deventer,et al.  The Role of Inorganic Polymer Technology in the Development of ‘Green Concrete’ , 2007 .

[20]  M. Nocuń,et al.  Specific features of the IR spectra of silicate glasses , 1994 .

[21]  Emmanuel Joussein,et al.  Role of alkaline cations and water content on geomaterial foams: Monitoring during formation , 2011 .

[22]  Amala Paul.  Chemistry of glasses , 1982 .

[23]  P. Walker,et al.  THE COMPRESSIVE STRENGTH OF MODERN EARTH MASONRY , 2009 .

[24]  R. Roy,et al.  PROTON RETENTION IN HEATED 1: 1 CLAYS STUDIED BY INFRARED SPECTROSCOPY, WEIGHT LOSS AND DEUTERIUM UPTAKE , 1961 .

[25]  Ángel Palomo,et al.  Alkali activation of fly ashes. Part 1: Effect of curing conditions on the carbonation of the reaction products , 2005 .