Atomic-scale compositional characterization of a nanocrystalline AlCrCuFeNiZn high-entropy alloy usi

Abstract We have studied a nanocrystalline AlCrCuFeNiZn high-entropy alloy synthesized by ball milling followed by hot compaction at 600 °C for 15 min at 650 MPa. X-ray diffraction reveals that the mechanically alloyed powder consists of a solid-solution body-centered cubic (bcc) matrix containing 12 vol.% face-centered cubic (fcc) phase. After hot compaction, it consists of 60 vol.% bcc and 40 vol.% fcc. Composition analysis by atom probe tomography shows that the material is not a homogeneous fcc–bcc solid solution but instead a composite of bcc structured Ni–Al-, Cr–Fe- and Fe–Cr-based regions and of fcc Cu–Zn-based regions. The Cu–Zn-rich phase has 30 at.% Zn α-brass composition. It segregates predominantly along grain boundaries thereby stabilizing the nanocrystalline microstructure and preventing grain growth. The Cr- and Fe-rich bcc regions were presumably formed by spinodal decomposition of a Cr–Fe phase that was inherited from the hot compacted state. The Ni–Al phase remains stable even after hot compaction and forms the dominant bcc matrix phase. The crystallite sizes are in the range of 20–30 nm as determined by transmission electron microscopy. The hot compacted alloy exhibited very high hardness of 870 ± 10 HV. The results reveal that phase decomposition rather than homogeneous mixing is prevalent in this alloy. Hence, our current observations fail to justify the present high-entropy alloy design concept. Therefore, a strategy guided more by structure and thermodynamics for designing high-entropy alloys is encouraged as a pathway towards exploiting the solid-solution and stability idea inherent in this concept.

[1]  J. Banhart,et al.  Effect of decomposition of the Cr-Fe-Co rich phase of AlCoCrCuFeNi high entropy alloy on magnetic properties. , 2011, Ultramicroscopy.

[2]  Jien-Wei Yeh,et al.  High-Entropy Alloys – A New Era of Exploitation , 2007 .

[3]  Akira Takeuchi,et al.  Classification of Bulk Metallic Glasses by Atomic Size Difference, Heat of Mixing and Period of Constituent Elements and Its Application to Characterization of the Main Alloying Element , 2005 .

[4]  Yuan-Sheng Huang,et al.  On the elemental effect of AlCoCrCuFeNi high-entropy alloy system , 2007 .

[5]  W. Hume-Rothery,et al.  Atomic diameters, atomic volumes and solid solubility relations in alloys , 1966 .

[6]  J. Yeh,et al.  Microstructure characterization of AlxCoCrCuFeNi high-entropy alloy system with multiprincipal elements , 2005 .

[7]  Swastik Mondal,et al.  Investigation of phases in Al23Co15Cr23Cu8Fe15Ni16 and Al8Co17Cr17Cu8Fe17Ni33 high entropy alloys and comparison with equilibrium phases predicted by Thermo-Calc , 2013 .

[8]  D. Raabe,et al.  Mechanical alloying and amorphization in Cu–Nb–Ag in situ composite wires studied by transmission electron microscopy and atom probe tomography , 2009 .

[9]  H. Bei,et al.  Relative effects of enthalpy and entropy on the phase stability of equiatomic high-entropy alloys , 2013 .

[10]  B. Cullity,et al.  Elements of X-ray diffraction , 1957 .

[11]  B. Murty,et al.  Alloying behavior in multi-component AlCoCrCuFe and NiCoCrCuFe high entropy alloys , 2012 .

[12]  B. S. Murty,et al.  Synthesis and characterization of nanocrystalline AlFeTiCrZnCu high entropy solid solution by mechanical alloying , 2008 .

[13]  W. Hume-rothery.  Comments on papers resulting from Hume-Rothery's Note—1965 , 1967 .

[14]  D. Raabe,et al.  Metallic composites processed via extreme deformation: Toward the limits of strength in bulk materials , 2010 .

[15]  D. Raabe,et al.  Microstructure and electromagnetic properties of heavily cold worked Cu-20 wt.%Nb wires , 1995 .

[16]  T. Chin,et al.  Formation of simple crystal structures in Cu-Co-Ni-Cr-Al-Fe-Ti-V alloys with multiprincipal metallic elements , 2004 .

[17]  B. S. Murty,et al.  Processing and properties of nanocrystalline CuNiCoZnAlTi high entropy alloys by mechanical alloying , 2010 .

[18]  J. Benedict,et al.  A Procedure for Cross Sectioning Specific Semiconductor Devices for Both SEM and TEM Analysis , 1990 .

[19]  H. Baker,et al.  Alloy phase diagrams , 1992 .

[20]  D. Raabe,et al.  Microstructure and mechanical properties of a cast and wire-drawn ternary Cu–Ag–Nb in situ composite , 1998 .

[21]  B. S. Murty,et al.  Decomposition in multi-component AlCoCrCuFeNi high-entropy alloy , 2011 .

[22]  D Lawrence,et al.  In situ site-specific specimen preparation for atom probe tomography. , 2007, Ultramicroscopy.

[23]  D. Raabe,et al.  Using ab initio calculations in designing bcc Mg–Li alloys for ultra-lightweight applications , 2009 .

[24]  D. Raabe,et al.  Atomic-scale mechanisms of deformation-induced cementite decomposition in pearlite , 2011 .

[25]  J. Benedict,et al.  Recent Developments in the use of the Tripod Polisher for TEM Specimen Preparation , 1991 .

[26]  D. Raabe,et al.  Theory-guided bottom-up design of β-titanium alloys as biomaterials based on first principles calculations: Theory and experiments , 2007 .

[27]  J. Yeh,et al.  Mechanical performance of the AlxCoCrCuFeNi high-entropy alloy system with multiprincipal elements , 2005 .

[28]  Yong Zhang,et al.  Solid Solution Formation Criteria for High Entropy Alloys , 2007 .

[29]  D. Raabe,et al.  Atom probe tomography characterization of heavily cold drawn pearlitic steel wire. , 2011, Ultramicroscopy.

[30]  C. Kittel.  Introduction to solid state physics , 1954 .

[31]  J. Schneider,et al.  Elastic properties of face-centred cubic Fe-Mn-C studied by nanoindentation and ab initio calculations , 2012 .

[32]  C. Liu,et al.  Effect of valence electron concentration on stability of fcc or bcc phase in high entropy alloys , 2011 .

[33]  K. Easterling,et al.  Phase Transformations in Metals and Alloys , 2021 .

[34]  Michael K Miller,et al.  Atom Probe Field Ion Microscopy , 1996 .

[35]  J. Yeh,et al.  Competition between elements during mechanical alloying in an octonary multi-principal-element alloy system , 2009 .

[36]  P. Liaw,et al.  Solid‐Solution Phase Formation Rules for Multi‐component Alloys , 2008 .