Photoconductivity of nitrogen-modified hydrogenated tetrahedral amorphous carbon

The changes in the photoconductivity of hydrogenated tetrahedral amorphous carbon (ta-C:H) with nitrogen incorporation were studied. Low level nitrogen incorporation improves the photoconductivity, by shifting the Fermi level upwards in the band gap. Films with a photosensitivity of about 200 at room temperature under white light illumination of 35 mW/cm2 were obtained; thus is the highest value so far reported for diamond-like carbons. At high temperatures, photoconductivity is controlled by nonradiative recombination through gap states, whereas at low temperatures it occurs by energy-loss hopping in the band tails. Nitrogen addition does not create extra charge defect recombination centers. Low temperature photoconductivity allows the direct determination of the localization radius of the band tail states. This radius varies from 2–3 A in ta-C:H to 9 A in ta-C. This illustrates how hydrogen can increase state localization and the photoluminescence efficiency in amorphous carbons.

[1]  J. Robertson,et al.  Electronic properties of tetrahedral amorphous carbon investigated by scanning tunneling microscopy , 1999 .

[2]  J. Robertson,et al.  Photoconductivity and electronic transport in tetrahedral amorphous carbon and hydrogenated tetrahedral amorphous carbon , 1998 .

[3]  J. Robertson,et al.  Reduction in defect density by annealing in hydrogenated tetrahedral amorphous carbon , 1998 .

[4]  T. Itoh,et al.  Preparation and properties of photoconductive amorphous carbon nitride a-CNx films: the layer-by-layer method , 1998 .

[5]  T. Frauenheim,et al.  p- and n-Type doping in carbon modifications , 1998 .

[6]  John Robertson,et al.  Nature of disorder and localization in amorphous carbon , 1998 .

[7]  J. Robertson,et al.  Electronic properties and doping of hydrogenated tetrahedral amorphous carbon films , 1998 .

[8]  G. Amaratunga,et al.  Nitrogen modification of hydrogenated amorphous carbon films , 1997 .

[9]  Robertson.  Recombination and photoluminescence mechanism in hydrogenated amorphous carbon. , 1996, Physical review. B, Condensed matter.

[10]  L. Ley,et al.  Effective correlation energies for defects in a-C:H from a comparison of photelectron yield and electron spin resonance experiments , 1995 .

[11]  G. Amaratunga,et al.  Electronic density of states in highly tetrahedral amorphous carbon , 1994 .

[12]  G. Amaratunga,et al.  Photoconductivity in highly tetrahedral diamondlike amorphous carbon , 1993 .

[13]  H. Fritzsche,et al.  Some observations on the photoconductivity of amorphous semiconductors , 1992 .

[14]  E. Terukov,et al.  Radiative recombination in a-Si1−xCx:H films , 1991 .

[15]  R. Street,et al.  Hydrogenated amorphous silicon: Index , 1991 .

[16]  Fritzsche,et al.  Electronic transport and recombination in amorphous semiconductors at low temperatures. , 1989, Physical review letters.

[17]  Monroe,et al.  Hopping exponential band tails. , 1985, Physical review letters.

[18]  R. Street,et al.  Effects of doping on transport and deep trapping in hydrogenated amorphous silicon , 1983 .

[19]  R. Collins,et al.  The temperature dependence of photoluminescence in a-Si: H alloys , 1980 .

[20]  Albert Rose,et al.  Concepts in photoconductivity and allied problems , 1963 .