Effect of heat treatment on age hardening behaviour of electroless nickel–phosphorus coatings

Abstract Electroless nickel–phosphorus (EN) coatings have been widely used in various industries such as oil, gas, electronic, chemical, automotive, aerospace, and mining. The EN coating process is based on a redox reaction in which a reducing agent is oxidised and Ni2+ ions are reduced on the substrate materials. Once the first layer of Ni is deposited, it acts as a catalyst for the process. Consequently, a linear relation between coating thickness and time usually occurs. If the reducing agent is sodium hypophosphite, the deposit obtained will be a nickel–phosphorus alloy. Also, the actual nickel and phosphorous levels in the EN deposit depend on the composition, temperature, and pH of the plating bath used. In this work, three types of EN coatings have been studied: low, medium, and high phosphorus Ni–P alloys. The techniques used were: differential scanning calorimetry (DSC), SEM, and hardness measurements. Heat treatment resulted in precipitation of nickel phosphides, e.g. Ni3P, and nickel crystallites. Thus, the phosphorus content of the coating was reduced. The results of isochronal age hardening showed that the peak age hardening temperature for the three EN coatings occurred at ∼673 K. However, the time to reach peak hardness during isothermal heat treatment at 593 K varied with phosphorus content. Also, it was found that the temperatures at which peak precipitation reactions occur during DSC scan are influenced by phosphorus content.

[1]  R. Parkinson.  Properties and applications of electroless nickel , 2001 .

[2]  P. Ernst,et al.  Porosity of Electroless Nickel Coatings Investigated Using Different Porosity Tests and Their Application , 1997 .

[3]  Peter Leisner,et al.  Porosity Measurements on Coatings , 1997 .

[4]  J. Zahavi,et al.  Properties of electrodeposited NiP-SiC composite coatings , 1996 .

[5]  Don Baudrand,et al.  Electroless plating processes: Developing technologies for electroless nickel, palladium, and gold , 1995 .

[6]  M. Kalantary,et al.  Optimisation of a bath for electroless plating and its use for the production of nickel-phosphorus-silicon carbide coatings , 1993 .

[7]  H. Deng,et al.  Effect of the Substrate Surface Morphology on the Porosity of Electroless Nickel Coatings , 1993 .

[8]  H. Xinmin,et al.  The wear characteristics of Ni-P-SiC composite coatings , 1992 .

[9]  Dong Nyung Lee,et al.  Microstructures and crystallization of electroless Ni-P deposits , 1990 .

[10]  Ralph E. White,et al.  Electrochemical Production and Corrosion Testing of Amorphous Ni‐P , 1988 .

[11]  Dong Nyung Lee,et al.  A study on the microstructure and phase transformation of electroless nickel deposits , 1988 .

[12]  Liu Cheng,et al.  Analysis of nonisothermal transformation kinetics; tempering of iron-carbon and iron-nitrogen martensites , 1988 .

[13]  E. J. Mittemeijer,et al.  Analysis of transformation kinetics by nonisothermal dilatometry , 1986 .

[14]  D. A. Luke.  Nickel-phosphorus electrodeposits , 1986 .

[15]  M. Mahoney,et al.  The effects of thermal history and phosphorus level on the crystallization behavior of electroless nickel , 1985 .

[16]  C. Shipley.  Historical highlights of electroless plating , 1984 .

[17]  K. Sugita,et al.  Composition and Crystallinity of Electroless Nickel , 1984 .

[18]  R. Allen,et al.  The structure of electroless NiP films as a function of composition , 1982 .

[19]  H. L. Rook,et al.  The State-of-the-art of thermal analysis , 1980 .

[20]  D. Turnbull,et al.  Structure Study of an Amorphous Electrodeposited Nickel‐Phosphorus Alloy , 1968 .