Efficient Antifungal and Flame-Retardant Properties of ZnO-TiO2-Layered Double-Nanostructures Coated on Bamboo Substrate

A facile method to synthesize ZnO-TiO2-layered double-nanostructures with the average thickness of 20 μm on a bamboo substrate was proposed to improve the antifungal and flame-retardant properties. The cross-linked wurtzite ZnO nanostructures with an average thickness of approximately 0.14 μm were uniformly distributed on the anatase TiO2 surface. The energy-dispersive X-ray spectroscopy (EDS) confirmed that the ZnO-TiO2 coating on bamboo was a layered double nanostructure. During a two-month antifungal test conducted in an outdoor environment, the fungi began to grow after one week on pristine bamboo and three weeks on ZnO-bamboo and TiO2-bamboo. Furthermore, there was an infected area of 100% after four weeks for pristine bamboo and six weeks for ZnO-bamboo, while there was an infected area of 43% after eight weeks for TiO2-bamboo. By comparison, there was no visible fungal growth on ZnO-TiO2-bamboo until the end of the test. The electron spin resonance (ESR) technique has demonstrated that the reactive oxygen species (ROS) of •O2− and •OH were produced from the ZnO-TiO2 surface under visible light irradiation (λ > 420 nm). This large quantity of •O2− compared to •OH is considered to be mainly responsible for the inactivation of fungi. Additionally, the limiting oxygen index has increased from 25.6% to 30.2% after being covered with a ZnO-TiO2 coating, which revealed a significant enhancement of its flame-retardant property.

[1]  Maximilian Bock,et al.  Engineered bamboo for structural applications , 2015, Nonconventional and Vernacular Construction Materials.

[2]  Wenting Sun,et al.  Insight into the Transfer Mechanisms of Photogenerated Carriers for Heterojunction Photocatalysts with the Analogous Positions of Valence Band and Conduction Band: A Case Study of ZnO/TiO2 , 2018, The Journal of Physical Chemistry C.

[3]  Hua-ming Li,et al.  Visible-light-driven Ag/AgBr/ZnFe2O4 composites with excellent photocatalytic activity for E. coli disinfection and organic pollutant degradation. , 2018, Journal of colloid and interface science.

[4]  F. Meng,et al.  Preparation, physical, mechanical, and interfacial morphological properties of engineered bamboo scrimber , 2017 .

[5]  M. Ladisch,et al.  Enhanced Antimicrobial Efficacy of Bimetallic Porous CuO Microspheres Decorated with Ag Nanoparticles. , 2017, ACS applied materials & interfaces.

[6]  F. Stazi,et al.  Nanotechnology on wood: The effect of photocatalytic nanocoatings against Aspergillus niger , 2017 .

[7]  Qingfeng Sun,et al.  Fabrication of nanocrystalline anatase TiO2 in a graphene network as a bamboo coating material with enhanced photocatalytic activity and fire resistance , 2017 .

[8]  P. Laokul,et al.  Preparation, characterizations and photocatalytic activity of a ZnO/TiO2 nanocomposite , 2017 .

[9]  Li Yu,et al.  Sustainability, space and supply chains: the role of bamboo in Anji County, China , 2017 .

[10]  Qi Zhang,et al.  Novel magnetic CoFe2O4/Ag/Ag3VO4 composites: Highly efficient visible light photocatalytic and antibacterial activity , 2016 .

[11]  J. Ji,et al.  Room temperature synthesis of crystalline anatase TiO2 on bamboo timber surface and their short-term antifungal capability under natural weather conditions , 2016 .

[12]  G. Lu,et al.  High specific surface area urchin-like hierarchical ZnO-TiO2 architectures: Hydrothermal synthesis and photocatalytic properties , 2016 .

[13]  Feng Liu,et al.  Synthesis of Ag ion-implanted TiO2 thin films for antibacterial application and photocatalytic performance. , 2015, Journal of hazardous materials.

[14]  Qingfeng Sun,et al.  Fabrication of superhydrophobic bamboo timber based on an anatase TiO2 film for acid rain protection and flame retardancy , 2015 .

[15]  P. Mohanty,et al.  ZnO nanowire-immobilized paper matrices for visible light-induced antibacterial activity against Escherichia coli , 2015 .

[16]  Danzhen Li,et al.  Construction of ZnO/TiO2 photonic crystal heterostructures for enhanced photocatalytic properties , 2015 .

[17]  Jianfeng Chen,et al.  Visible-light-responsive TiO2-coated ZnO:I nanorod array films with enhanced photoelectrochemical and photocatalytic performance. , 2015, ACS applied materials & interfaces.

[18]  Xianxu Zhan,et al.  A robust, anti-acid, and high-temperature–humidity-resistant superhydrophobic surface of wood based on a modified TiO2 film by fluoroalkyl silane , 2015 .

[19]  Yun Lu,et al.  Superhydrophobic conductive wood with oil repellency obtained by coating with silver nanoparticles modified by fluoroalkyl silane , 2015 .

[20]  Chang Ming Li,et al.  Fabrication of CeO2 nanoparticle-modified silk for UV protection and antibacterial applications. , 2014, Journal of colloid and interface science.

[21]  De-jun Wang,et al.  Construction of a branched ZnO–TiO2 nanorod array heterostructure for enhancing the photovoltaic properties in quantum dot-sensitized solar cells , 2014 .

[22]  J. Matos,et al.  Performance of activated carbons in consecutive phenol photooxidation cycles , 2014 .

[23]  Hongzhi Wang,et al.  All-nanoparticle self-assembly ZnO/TiO₂ heterojunction thin films with remarkably enhanced photoelectrochemical activity. , 2014, ACS applied materials & interfaces.

[24]  Xianai Huang,et al.  A novel process to improve yield and mechanical performance of bamboo fiber reinforced composite via mechanical treatments , 2014 .

[25]  Ž. Lukšienė,et al.  Antibacterial and antifungal activity of photoactivated ZnO nanoparticles in suspension. , 2013, Journal of photochemistry and photobiology. B, Biology.

[26]  Xinyong Li,et al.  Fabrication of Ag/Ag3PO4/TiO2 heterostructure photoelectrodes for efficient decomposition of 2-chlorophenol under visible light irradiation , 2013 .

[27]  Bin Zhao,et al.  A highly efficient TiO2@ZnO n-p-n heterojunction nanorod photocatalyst. , 2013, Nanoscale.

[28]  Fang‐Xing Xiao.  Construction of highly ordered ZnO-TiO2 nanotube arrays (ZnO/TNTs) heterostructure for photocatalytic application. , 2012, ACS applied materials & interfaces.

[29]  C. S. Verma,et al.  Development of layered laminate bamboo composite and their mechanical properties , 2012 .

[30]  Xiangke Wang,et al.  Enhanced photocatalytic degradation of methylene blue under visible irradiation on graphene@TiO2 dyade structure , 2012 .

[31]  S. Mohajerzadeh,et al.  Investigating the antifungal activity of TiO2 nanoparticles deposited on branched carbon nanotube arrays , 2011 .

[32]  A. Gedanken,et al.  Antifungal activity of ZnO nanoparticles—the role of ROS mediated cell injury , 2011, Nanotechnology.

[33]  Sapna Sharma,et al.  Synthesis of ZnO nanoparticles and study of their antibacterial and antifungal properties , 2010 .

[34]  O. Akhavan,et al.  Lasting antibacterial activities of Ag-TiO2/Ag/a-TiO2 nanocomposite thin film photocatalysts under solar light irradiation. , 2009, Journal of colloid and interface science.

[35]  Liyi Shi,et al.  Zn-doped TiO2 nanoparticles with high photocatalytic activity synthesized by hydrogen–oxygen diffusion flame , 2008 .