Microstructure and Magnetic Properties of Microwave Sintered Ni0.5Zn0.5Fe2O4 Ferrite

Ni0.5Zn0.5)Fe2O4 ferrite has been sintered via microwave irradiation. The structural, component and magnetic properties of NiZn ferrite was determined by SEM, X-ray powder diffraction (XRD) and automatic hysteresis loop magnetometer. Results showed that the material sintered by microwave energy at 1220°C for 20min had a high purity (Ni0.5Zn0.5)Fe2O4 phase. The sample obtained magnetic properties of intrinsic coercivity 222A/m, saturation magnetization 332mT, initial permeability 0.20mH/m and maximum permeability 0.58mH/m. Compared with conventional sintering method, microwave sintering of NiZn ferrite is more efficient and reducing soaking time.

[1] W. Marsden. I and J , 2012 .

[2] T. Santos,et al. Simulating the electromagnetic field in microwave ovens , 2011, 2011 SBMO/IEEE MTT-S International Microwave and Optoelectronics Conference (IMOC 2011).

[3] J. Xiao,et al. Advanced soft magnetic materials for high frequency and high power application , 2011, 2011 Twenty-Sixth Annual IEEE Applied Power Electronics Conference and Exposition (APEC).

[4] Morteza Oghbaei,et al. Microwave versus Conventional Sintering: A Review of Fundamentals, Advantages and Applications , 2010 .

[5] Z. Ling,et al. Sintering behavior and electromagnetic properties of Fe-deficient NiZn ferrites , 2008 .

[6] T. Marcelo,et al. MW sinter processing emerges as efficient and green technology , 2008 .

[7] Y. Matsuo,et al. High performance NiZn ferrite , 2001 .

[8] Rustum Roy,et al. Full sintering of powdered-metal bodies in a microwave field , 1999, Nature.

[9] M. Sugimoto. The Past, Present, and Future of Ferrites , 1999 .

[10] D. Stoppels. Developments in soft magnetic power ferrites , 1996 .

[11] G. Roussy,et al. Temperature runaway of microwave irradiated materials , 1987 .