Bioactive titanium: effect of sodium removal on the bone-bonding ability of bioactive titanium prepared by alkali and heat treatment.

As reported previously, bioactive titanium is prepared by simple alkali and heat treatment, and can bond to living bone directly. The purpose of this study was to accelerate the bioactivity of bioactive titanium in vivo. In in vitro study, sodium removal by hot water immersion enhanced the apatite-forming ability of bioactive titanium in simulated body fluid dramatically. The specific anatase structure of titania gel was effective for apatite formation in vitro. In the current study, we investigated the in vivo effect of sodium removal on the bone-bonding strength of bioactive titanium. Sodium-free bioactive titanium plates were prepared by immersion in an aqueous solution of 5 M NaOH at 60 degrees C for 24 h, followed by immersion in distilled water at 40 degrees C for 48 h before heating them at 600 degrees C for 1 h. Three kinds of titanium plates were inserted into rabbit tibiae, including untreated cp-Ti, conventional alkali- and heat-treated Ti, and sodium-free alkali- and heat-treated Ti. In vivo bioactive performance was examined mechanically and histologically after 4, 8, 16, and 24 weeks. Sodium removal enhanced the bone-bonding strength of bioactive titanium at 4 and 8 weeks postoperatively; however, its bone-bonding strength was inferior to that of conventional alkali- and heat-treated titanium at 16 and 24 weeks. Histological examinations after the detaching test revealed breakage of the treated layer in the sodium-free alkali- and heat-treated titanium group. In conclusion, sodium removal accelerated the in vivo bioactivity of bioactive titanium and achieved faster bone-bonding because of its anatase surface structure, but the loss of the surface's graded structure due to the complete removal of sodium decreased the adhesive strength of the treated layer to the titanium substrate. Further investigations are required to determine the optimum conditions for preparation of bioactive titanium.

[1]  Lester Dk.  Microscopic studies of human press fit titanium hip prostheses. , 1997 .

[2]  H. M. Kim,et al.  Preparation of bioactive Ti and its alloys via simple chemical surface treatment. , 1996, Journal of biomedical materials research.

[3]  K. Kawanabe,et al.  Apatite layer-coated titanium for use as bone bonding implants. , 1997, Biomaterials.

[4]  S. McNally,et al.  The results at nine to twelve years of the use of a hydroxyapatite-coated femoral stem. , 2000, The Journal of bone and joint surgery. British volume.

[5]  H. M. Kim,et al.  Bonding strength of bonelike apatite layer to Ti metal substrate. , 1997, Journal of biomedical materials research.

[6]  Tadashi Kokubo,et al.  Spontaneous Formation of Bonelike Apatite Layer on Chemically Treated Titanium Metals , 1996 .

[7]  K. Baba,et al.  Spectroscopic studies of three osseointegrated implants. , 1998, Journal of dentistry.

[8]  K. de Groot,et al.  Calcium phosphate formation within sol-gel prepared titania in vitro and in vivo. , 1993, Journal of biomedical materials research.

[9]  S. Toksvig-Larsen,et al.  A Comparison of Hydroxyapatite-Coated, Titanium-Coated, and Uncoated Tapered External-Fixation Pins. An in Vivo Study in Sheep* , 1998, The Journal of bone and joint surgery. American volume.

[10]  A. Yee,et al.  A randomized trial of hydroxyapatite coated prostheses in total hip arthroplasty. , 1999, Clinical orthopaedics and related research.

[11]  H. M. Kim,et al.  Graded surface structure of bioactive titanium prepared by chemical treatment. , 1999, Journal of biomedical materials research.

[12]  R. Craig,et al.  Strategies to affect bone remodeling: Osteointegration , 1993, Journal of bone and mineral research : the official journal of the American Society for Bone and Mineral Research.

[13]  H. M. Kim,et al.  Bonding of chemically treated titanium implants to bone. , 1997, Journal of biomedical materials research.

[14]  R. Geesink,et al.  Six-year results of hydroxyapatite-coated total hip replacement. , 1995, The Journal of bone and joint surgery. British volume.

[15]  K Nakanishi,et al.  The role of hydrated silica, titania, and alumina in inducing apatite on implants. , 1994, Journal of biomedical materials research.

[16]  Joshua J. Jacobs,et al.  Corrosion of metal orthopaedic implants. , 1998, The Journal of bone and joint surgery. American volume.

[17]  T. Goto,et al.  Bone-bonding behavior of plasma-sprayed coatings of BioglassR, AW-glass ceramic, and tricalcium phosphate on titanium alloy. , 1996, Journal of biomedical materials research.

[18]  T. Goto,et al.  Bone bonding behavior of titanium and its alloys when coated with titanium oxide (TiO2) and titanium silicate (Ti5Si3). , 1996, Journal of biomedical materials research.

[19]  H. M. Kim,et al.  The effect of heat treatment on bone-bonding ability of alkali-treated titanium. , 1999, Biomaterials.

[20]  H. M. Kim,et al.  Formation of a bioactive graded surface structure on Ti-15Mo-5Zr-3Al alloy by chemical treatment. , 2000, Biomaterials.

[21]  K. Suzuki,et al.  Effects of surface roughness of titanium implants on bone remodeling activity of femur in rabbits. , 1997, Bone.

[22]  S. Steinemann.  Metal implants and surface reactions. , 1996, Injury.

[23]  H. M. Kim,et al.  Enhancement of bone-bonding strengths of titanium alloy implants by alkali and heat treatments. , 1999, Journal of biomedical materials research.

[24]  P Ducheyne,et al.  Bioactive ceramics: the effect of surface reactivity on bone formation and bone cell function. , 1999, Biomaterials.