Effect of phosphorus on the formation of retained austenite and mechanical properties in Si-containing low-carbon steel sheet

The effect of phosphorus and silicon on the formation of retained austenite has been investigated in a low-carbon steel cold rolled, intercritically annealed, and isothermally held in a temperature range of bainitic transformation followed by air cooling. The steel sheet containing phosphorus after final heat-treatment consisted of ferrite, retained austenite, and bainite or martensite. Phosphorus, especially in the presence of silicon, in steel was useful to assist the formation of retained austenite. Mechanical properties, such as tensile strength, uniform elongation, and the combination of tensile strength/ductility, were improved when phosphorus was increased up to 0.07 pct in 0.5 pct Si steel. This could be attributed to the strain-induced transformation of retained austenite during tensile deformation. Furthermore, two types of retained austenite were observed in P-containing steel. One is larger than about 1 μm in size and usually exists adjacent to bainite; the other one is of submicron size and usually exists in a ferrite matrix. High phosphorus content promotes the formation of stable (small size) austenites which are considered to be stabilized mainly by their small size effect and have a different formation mechanism from the coarser retained austenite in the lower P steels. The retained austenites of submicron size showed mechanical stability even after 10 pct deformation, suggesting that these small austenites have little effect on ductility. The 0.07 pct P-0.5 pct Si-1.5 pct Mn-0.12 pct C steel showed a high strength of 730 MPa and a total elongation of 36 pct.

[1]  H. Era,et al.  Effect of manganese on the recrystallization texture of P-containing low-carbon steel sheet , 1987 .

[2]  W. C. Leslie,et al.  Precipitation of carbides in low-carbon Fe-AI-C alloys , 1978 .

[3]  N. C. Goel,et al.  The influence of starting microstructure on the retention and mechanical stability of austenite in an intercritically annealed-low alloy dual-phase steel , 1987 .

[4]  I. Lindgren,et al.  Role of vanadium in dual-phase steels , 1981 .

[5]  G. Bégin,et al.  A study of the peculiarities of austenite during the formation of bainite , 1971 .

[6]  O. N. Mohanty,et al.  TEM study of carbide precipitation in a phosphorus-bearing low-carbon steel , 1982 .

[7]  A. Kelly,et al.  Strengthening methods in crystals , 1971 .

[8]  E. Bain,et al.  Alloying elements in steel , 1966 .

[9]  I. Tamura On the TRIP Steel , 1970 .

[10]  F. B. Pickering,et al.  Physical metallurgy and the design of steels , 1978 .

[11]  H. K. D. H. Bhadeshia,et al.  Bainite in silicon steels: New composition–property approach Part 1 , 1983 .

[12]  H. Conrad,et al.  Effect of electric current pulses on the recrystallization of copper , 1983 .

[13]  O. N. Mohanty,et al.  Magnetic aging characteristics of a phosphorous-bearing low carbon steel , 1981 .

[14]  H. Bhadeshia,et al.  The bainite transformation in a silicon steel , 1979 .

[15]  O. Matsumura,et al.  Enhancement of Elongation by Retained Austenite in Intercritical Annealed 0.4C-1.5Si-O.8Mn Steel , 1987 .

[16]  G. Speich,et al.  Formation of Austenite During Intercritical Annealing of Dual-Phase Steels , 1981 .

[17]  A. Sachdev,et al.  Influence of cooling rate on the microstructure and retained austenite in an intercritically annealed vanadium containing HSLA steel , 1982 .