Fresh and hardened properties of self-compacting concrete produced with manufactured sand

Abstract Self-compacting concrete (SCC) is extensively applied in many construction projects due to its excellent fresh and hardened concrete properties. In recent years, manufactured sand (Msand) produced by crushing rock deposits is being identified as a suitable alternative source for river sand in concrete. The main objective of this study is to explore the possibility of using Msand in SCC. In this process, an attempt was made to understand the influence of paste volume and w/p ratio (water to powder ratio) on the properties of self-compacting concrete (SCC) using Msand. The powder and aggregate combinations were optimised by using the particle packing approach, which involves the selection of combinations having maximum packing density. The chemical admixtures (superplasticisers, viscosity modifying agent) were optimised based on simple empirical tests. Fresh concrete tests such as slump flow, T500 and J-ring were performed on SCC; hardened concrete tests were limited to compressive strength. From the results, it was observed that relatively higher paste volume is essential to achieve the required flow for SCC using Msand, as compared to river sand. Low and medium strength (25–60 MPa) SCCs were achieved by using Msand based on the approach adopted in the study. Results showed that it is possible to successfully utilise manufactured sand in producing SCC.

[1]  D. Kantro,et al.  Influence of Water-Reducing Admixtures on Properties of Cement Paste—A Miniature Slump Test , 1980 .

[2]  R. Siddique,et al.  Influence of high temperature on the properties of concretes made with industrial by-products as fine aggregate replacement , 2011 .

[3]  M. Glavind,et al.  PACKING CALCULATIONS APPLIED FOR CONCRETE MIX DESIGN , 1999 .

[4]  Luís Marcelo Tavares,et al.  Comparison of natural and manufactured fine aggregates in cement mortars , 2007 .

[5]  M. Santhanam,et al.  A new empirical test method for the optimisation of viscosity modifying agent dosage in self-compacting concrete , 2010 .

[6]  M. Santhanam,et al.  A STUDY OF THE INTERACTION BETWEEN VISCOSITY MODIFYING AGENT AND HIGH RANGE WATER REDUCER IN SELF COMPACTING CONCRETE , 2006 .

[7]  D. Fowler,et al.  THE EFFECTS OF AGGREGATES CHARACTERISTICS ON THE PERFORMANCE OF PORTLAND CEMENT CONCRETE , 2003 .

[8]  Manu Santhanam,et al.  Experimental investigations on the influence of paste composition and content on the properties of Self-Compacting Concrete , 2009 .

[9]  C. S. Poon,et al.  Properties of self-compacting concrete prepared with recycled glass aggregate , 2009 .

[10]  Edgardo F. Irassar,et al.  High-strength concrete with different fine aggregate , 2002 .

[11]  M. Alexander,et al.  Aggregates in Concrete , 2005 .

[12]  E. Forssberg,et al.  Influence of fine aggregate characteristics on the rheological properties of mortars , 2008 .

[13]  R. McGeary,et al.  Mechanical Packing of Spherical Particles , 1961 .

[14]  S. Subramanian,et al.  Current developments in self-compacting concrete , 2004 .