Real time contact resistance measurement to determine when microwelds start to form during ultrasonic wire bonding

We prove that we can, using contact resistance as a tool, determine the instant when the bonding process starts, i.e. microwelds start to form during ultrasonic bonding. This knowledge permits us to reduce the uncertainty in the estimated bonded area by 5-18%. We proved our claim by combining a real-time contact resistance measurement, aborted ultrasound bonding, and classical SEM analysis of the bonded surfaces. We measured and analyzed, using a 4-wire Kelvin cross setup, the contact resistance of [email protected] by diameter AlSi(1%) wires bonded to a gold pad. The microweld area of 69 bonds was determined. We focused on inferring exactly when do the microwelds start to form. Post hoc analysis showed a linear correlation between the total microweld area and the time elapsed since the initial contact resistance drop. This work may help minimizing the sonication impact which may allow working with thin bond wires and fragile substrates.

[1]  Siu Wing Or,et al.  Ultrasonic wire-bond quality monitoring using piezoelectric sensor , 1998 .

[2]  Herbert Reichl,et al.  Ultrasonic friction power during Al wire wedge-wedge bonding , 2009 .

[3]  Herbert Reichl,et al.  The ultrasonic wedge/wedge bonding process investigated using in situ real-time amplitudes from laser vibrometer and integrated force sensor , 2010 .

[4]  G. Harman,et al.  The Microelectronic Wire Bond Pull Test-How to use It, How to Abuse It , 1978 .

[5]  Ivan Kassamakov,et al.  Scanning white light interferometry in quality control of single-point tape automated bonding , 2007 .

[6]  G. Harman,et al.  The Ultrasonic Welding Mechanism as Applied to Aluminum-and Gold-Wire Bonding in Microelectronics , 1977 .

[7]  L. W. Linholm,et al.  A direct measurement of interfacial contact resistance , 1982, IEEE Electron Device Letters.

[8]  Effect of ultrasonic power on wedge bonding strength and interface microstructure , 2007 .

[9]  G. Harman.  Wire Bonding in Microelectronics: Materials, Processes, Reliability, and Yield , 1997 .

[10]  H. H. Berger,et al.  Contact Resistance and Contact Resistivity , 1972 .

[11]  M. Brokelmann,et al.  PiQC - a process integrated quality control for nondestructive evaluation of ultrasonic wire bonds , 2008, 2008 IEEE Ultrasonics Symposium.

[12]  H. Reichl,et al.  Analysis of the friction processes in ultrasonic wedge/wedge-bonding , 2009 .

[13]  Frode Strisland,et al.  Wire-bond failure mechanisms in plastic encapsulated microcircuits and ceramic hybrids at high temperatures , 2004, Microelectron. Reliab..