Preparation and Properties of Partial-Degradable ZrO2–Chitosan Particles–GelMA Composite Scaffolds

In the field of bone repair, the inorganic–organic composite scaffold is a promising strategy for mimicking the compositions of the natural bone. In addition, as implants for repairing load-bearing sites, an inert permanent bone substitute composites with bioactive degradable ingredients may make full use of the composite scaffold. Herein, the porous zirconia (ZrO2) matrix was prepared via the template replication method, and the partial degradable ZrO2–chitosan particles–GelMA composite scaffolds with different chitosan/GelMA volume ratios were prepared through the vacuum infiltration method. Dynamic light scattering (DLS) and the scanning electron microscope (SEM) were adopted to observe the size of the chitosan particles and the morphologies of the composites scaffold. The mechanical properties, swelling properties, and degradation properties of the composite scaffolds were also characterized by the mechanical properties testing machine and immersion tests. The CCK-8 assay was adopted to test the biocompatibility of the composite scaffold preliminarily. The results show that chitosan particles as small as 60 nm were obtained. In addition, the ratio of chitosan/GelMA can influence the mechanical properties and the swelling and degradation behaviors of the composites scaffold. Furthermore, improved cell proliferation performance was obtained for the composite scaffolds.