Cooperative upconversion and optical gain in ion-beam sputter-deposited Er(x)Y(2-x)SiO(5) waveguides.

Single-phase, polycrystalline Er(x)Y(2-x)SiO(5) thin films were deposited by reactive ion-beam sputter deposition and rapid thermal annealing. Due to the crystalline nature, the silicate thin films provide peak Er(3+) emission cross-section of 0.9 +/- 0.02 x 10(-20) cm(2) that is higher than that in silica. Optical gain, with near 60% inversion, is achieved via optical pumping of a single-mode, ridge-type waveguide with the silicate core with an Er concentration of 1.7 x 10(20) cm(-3). Analysis of pump-power dependence of the optical gain and spontaneous emission intensity of Er(3+) indicate that the gain is limited by cooperative upconversion process, whose coefficient is determined to be (8 +/- 3) x 10(-17) cm(3)/sec.

[1]  Tadamasa Kimura,et al.  Fabrication and characterization of Er silicates on SiO2/Si substrates , 2009 .

[2]  J. Bowers,et al.  Electrically pumped hybrid AlGaInAs-silicon evanescent laser. , 2006, Optics express.

[3]  B. Bae,et al.  Large-scale fabrication of single-phase Er2SiO5 nanocrystal aggregates using Si nanowires , 2006 .

[4]  A. Polman,et al.  Erbium implanted thin film photonic materials , 1997 .

[5]  Maria Miritello,et al.  Efficient Luminescence and Energy Transfer in Erbium Silicate Thin Films , 2007 .

[6]  Mk Meint Smit,et al.  Upconversion in Er-implanted Al2O3 waveguides , 1996 .

[7]  Lorenzo Pavesi,et al.  Optical gain in silicon nanocrystals , 2001 .

[8]  Pieter G. Kik,et al.  Cooperative upconversion as the gain-limiting factor in Er doped miniature Al2O3 optical waveguide amplifiers , 2003 .

[9]  B. Bae,et al.  Er3+ luminescence and cooperative upconversion in ErxY2−xSiO5 nanocrystal aggregates fabricated using Si nanowires , 2008 .

[10]  F. Iacona,et al.  Thermal evolution of Er silicate thin films grown by rf magnetron sputtering , 2008 .

[11]  T. R. Gosnell,et al.  Uniform upconversion in high-concentration Er(3+)-doped soda lime silicate and aluminosilicate glasses. , 1997, Optics letters.

[12]  D. Mccumber,et al.  Einstein Relations Connecting Broadband Emission and Absorption Spectra , 1964 .

[13]  Albert Polman,et al.  Erbium-doped phosphate glass waveguide on silicon with 4.1 dB/cm gain at 1.535 µm , 1997 .

[14]  W. Miniscalco.  Erbium-doped glasses for fiber amplifiers at 1500 nm , 1991 .

[15]  R. C. Kistler,et al.  Optical doping of waveguide materials by MeV Er implantation , 1991 .