Microstructure and mechanical properties of nickel based superalloy IN718 produced by rapid prototyping with electron beam melting (EBM)

Abstract A nickel alloy of a composition similar to that of the nickel based superalloy Inconel alloy 718 (IN718) was produced with the electron beam melting (EBM) process developed by Arcam AB. The microstructures of the as processed and heat treated material are similar to that of conventionally produced IN718, except that the EBM material showed some porosity and the δ phase did not dissolve during the solution heat treatment because the temperature of 1000°C apparently was too low. Mechanical testing of the layer structured material, parallel and perpendicular to the built layers, revealed sufficient strength in both directions. However, it showed only limited elongation when tested perpendicular to the built layers due to local agglomerations of pores. Otherwise, data for the hardness, Young’s modulus, 0·2% yield tensile strength and ultimate tensile strength match those recommended for IN718.

[1]  M. Sundararaman,et al.  The influence of aging on the serrated yielding phenomena in a nickel-base superalloy , 2008 .

[2]  Mark Whittaker,et al.  Shaped metal deposition of a nickel alloy for aero engine applications , 2008 .

[3]  Liu Wei,et al.  Delta phase precipitation in Inconel 718 , 2004 .

[4]  M. L. Griffith,et al.  Understanding the Microstructure and Properties of Components Fabricated by Laser Engineered Net Shaping (LENS) , 2000 .

[5]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[6]  W. Kurz,et al.  SINGLE-CRYSTAL LASER DEPOSITION OF SUPERALLOYS: PROCESSING-MICROSTRUCTURE MAPS , 2001 .

[7]  R. Fischer,et al.  Investigations of MX and γ′/γ″ precipitates in the nickel-based superalloy 718 produced by electron beam melting , 2008 .

[8]  Weidong Huang,et al.  Study on microstructure and mechanical properties of laser rapid forming Inconel 718 , 2008 .

[9]  F. Petzoldt,et al.  Effect of production parameters on the properties of IN 718 superalloy by three-dimensional printing , 2008 .

[10]  Srikumar Banerjee,et al.  Precipitation of the δ-Ni3Nb phase in two nickel base superalloys , 1988 .

[11]  M. Weaver,et al.  Activation energy calculations for discontinuous yielding in Inconel 718SPF , 2001 .

[12]  R. A. Stevens,et al.  The dependence of creep rate on microstructure in a γ′ strengthened superalloy , 1981 .

[13]  M. Weaver,et al.  Effects of Precipitation on Serrated Yielding in Inconel 718 , 2001 .

[14]  R. F. Jones,et al.  Characterization and Thermomechanical Processing of Sprayformed Allvac 720 Alloy , 2000 .

[15]  P. Blackwell,et al.  The mechanical and microstructural characteristics of laser-deposited IN718 , 2005 .

[16]  K. Osakada,et al.  Rapid Manufacturing of Metal Components by Laser Forming , 2006 .