Fabrication of flower-like Bi2WO6 superstructures as high performance visible-light driven photocatalysts

A novel flower-like Bi2WO6 superstructure was successfully realized by a facile hydrothermal process without any surfactant or template. Based on the evolution of this morphology as a function of hydrothermal time, the formation mechanism was proposed to be as follows: (1) self-aggregation of nanoparticles; (2) formation of crystalline nanoplates by Ostwald ripening; and (3) organization of the in situ-formed nanoplates into spherical superstructures. The pretty flower-like superstructure of Bi2WO6 was retained after calcination at 550 °C for 4 h. Both the uncalcined and calcined Bi2WO6 exhibited excellent visible-light-driven photocatalytic efficiencies for the degradation of Rhodamine B (RhB), up to 84 and 97% within 60 minutes, respectively, which were much higher than those of TiO2 (P-25) and Bi2WO6 sample prepared by solid-state reaction (SSR-Bi2WO6). Close investigation indicated that plenty of pores with different sizes existed in the Bi2WO6 superstructures, which could serve as hierarchical transport paths for small molecules and might greatly improve their photocatalytic activities.

[1]  Gareth W. V. Cave,et al.  Hydrogen-bonded hexamers self-assemble as spherical and tubular superstructures on the sub-micron scale. , 2006, Angewandte Chemie.

[2]  Wenzhong Wang,et al.  Synthesis of octahedral CuS nanocages via a solid–liquid reaction , 2006 .

[3]  B. Kale,et al.  CdIn2S4 Nanotubes and “Marigold” Nanostructures: A Visible‐Light Photocatalyst , 2006 .

[4]  H. Fu,et al.  Photocatalytic properties of nanosized Bi2WO6 catalysts synthesized via a hydrothermal process , 2006 .

[5]  S. Suib,et al.  Hydrothermal Synthesis of Structure‐ and Shape‐Controlled Manganese Oxide Octahedral Molecular Sieve Nanomaterials , 2006 .

[6]  Reji Varghese,et al.  Evolution of nano- to microsized spherical assemblies of a short oligo(p-phenyleneethynylene) into superstructured organogels. , 2006, Angewandte Chemie.

[7]  X. Cao,et al.  Template‐Free Preparation of Hollow Sb2S3 Microspheres as Supports for Ag Nanoparticles and Photocatalytic Properties of the Constructed Metal–Semiconductor Nanostructures , 2006 .

[8]  Haitao Zhang,et al.  Morphology-controllable synthesis and characterization of hierarchical 3D Co1-xMnxO nanostructures. , 2006, The journal of physical chemistry. B.

[9]  S. Fu,et al.  Template-free synthesis and characterization of novel 3D urchin-like α-Fe2O3 superstructures , 2006 .

[10]  Y. Xiong,et al.  Large-scale fabrication of TiO2 hierarchical hollow spheres. , 2006, Inorganic chemistry.

[11]  K. Domen,et al.  Photocatalyst releasing hydrogen from water , 2006, Nature.

[12]  A. Kudo,et al.  Photocatalytic Hydrogen Evolution on ZnS−CuInS2−AgInS2 Solid Solution Photocatalysts with Wide Visible Light Absorption Bands , 2006 .

[13]  Yadong Li,et al.  Use of carbonaceous polysaccharide microspheres as templates for fabricating metal oxide hollow spheres. , 2006, Chemistry.

[14]  Lisha Zhang,et al.  Preparation of Fenton reagent with H2O2 generated by solar light-illuminated nano-Cu2O/MWNTs composites , 2006 .

[15]  F. Yakuphanoglu,et al.  Optical properties of the poly(N-benzylaniline) thin film. , 2006, The journal of physical chemistry. B.

[16]  Y. Qian,et al.  Nucleation−Dissolution−Recrystallization: A New Growth Mechanism for t-Selenium Nanotubes , 2006 .

[17]  Shicheng Zhang,et al.  Visible-light-driven photocatalyst of Bi2WO6 nanoparticles prepared via amorphous complex precursor and photocatalytic properties , 2006 .

[18]  H. Fu,et al.  Visible-light-induced degradation of rhodamine B by nanosized Bi2WO6. , 2005, The journal of physical chemistry. B.

[19]  J. Hupp,et al.  Better Living Through Nanopore Chemistry , 2005, Science.

[20]  D. Xue,et al.  Fabrication of malachite with a hierarchical sphere-like architecture. , 2005, The journal of physical chemistry. B.

[21]  R. Mokaya,et al.  Hollow spheres of crystalline porous metal oxides: A generalized synthesis route via nanocasting with mesoporous carbon hollow shells , 2005 .

[22]  H. Kim,et al.  Photocatalytic nanodiodes for visible-light photocatalysis. , 2005, Angewandte Chemie.

[23]  Yongfa Zhu,et al.  Synthesis of Square Bi2WO6 Nanoplates as High-Activity Visible-Light-Driven Photocatalysts , 2005 .

[24]  Jiaguo Yu,et al.  Hydrothermal preparation and visible-light photocatalytic activity of Bi2WO6 powders , 2005 .

[25]  C. Grey,et al.  Detecting different oxygen-ion jump pathways in Bi2WO6 with 1- and 2-dimensional 17O MAS NMR spectroscopy , 2005 .

[26]  Xianzhi Fu,et al.  Photocatalytic activity of a hierarchically macro/mesoporous titania. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[27]  H. Zeng,et al.  Formation of colloidal CuO nanocrystallites and their spherical aggregation and reductive transformation to hollow Cu2O nanospheres. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[28]  A. Sra,et al.  Spontaneous Hierarchical Assembly of Rhodium Nanoparticles into Spherical Aggregates and Superlattices , 2005 .

[29]  Bin Liu,et al.  Fabrication of ZnO "dandelions" via a modified Kirkendall process. , 2004, Journal of the American Chemical Society.

[30]  H. Zeng,et al.  Self-generation of tiered surfactant superstructures for one-pot synthesis of Co3O4 nanocubes and their close- and non-close-packed organizations. , 2004, Langmuir : the ACS journal of surfaces and colloids.

[31]  Jinhua Ye,et al.  Efficient photocatalytic decomposition of organic contaminants over CaBi2O4 under visible-light irradiation. , 2004, Angewandte Chemie.

[32]  B. Liu,et al.  Mesoscale organization of CuO nanoribbons: formation of "dandelions". , 2004, Journal of the American Chemical Society.

[33]  Hua Chun Zeng,et al.  Preparation of Hollow Anatase TiO2 Nanospheres via Ostwald Ripening. , 2004, The journal of physical chemistry. B.

[34]  C. Brinker,et al.  Controlled synthesis of 2-D and 3-D dendritic platinum nanostructures. , 2004, Journal of the American Chemical Society.

[35]  Chad A Mirkin,et al.  Self-Assembly of Mesoscopic Metal-Polymer Amphiphiles , 2004, Science.

[36]  Jinhua Ye,et al.  Photocatalytic Decomposition of Organic Contaminants by Bi2WO6 Under Visible Light Irradiation , 2004 .

[37]  Peidong Yang,et al.  Nanotechnology: Wires on water , 2003, Nature.

[38]  Eduardo Enciso,et al.  Micro/nano-structural properties of imprinted macroporous titania and zirconia , 2003 .

[39]  Dongmok Whang,et al.  Large-scale hierarchical organization of nanowire arrays for integrated nanosystems , 2003 .

[40]  Z. Niu,et al.  Templated synthesis of inorganic hollow spheres with a tunable cavity size onto core-shell gel particles. , 2003, Angewandte Chemie.

[41]  Debra R Rolison,et al.  Catalytic Nanoarchitectures--the Importance of Nothing and the Unimportance of Periodicity , 2003, Science.

[42]  A. Bell.  The Impact of Nanoscience on Heterogeneous Catalysis , 2003, Science.

[43]  K. Philippot,et al.  Organometallic Synthesis of Size‐Controlled Polycrystalline Ruthenium Nanoparticles in the Presence of Alcohols , 2003 .

[44]  Younan Xia,et al.  Shape-Controlled Synthesis of Gold and Silver Nanoparticles , 2002, Science.

[45]  Seung‐Man Yang,et al.  Packings of uniform microspheres with ordered macropores fabricated by double templating. , 2002, Journal of the American Chemical Society.

[46]  A. R. Bausch,et al.  Colloidosomes: Selectively Permeable Capsules Composed of Colloidal Particles , 2002, Science.

[47]  M. Antonietti,et al.  Biomimetic crystallization of calcium carbonate spherules with controlled surface structures and sizes by double-hydrophilic block copolymers , 2002 .

[48]  Chuncheng Chen,et al.  Photodegradation of Sulforhodamine-B Dye in Platinized Titania Dispersions under Visible Light Irradiation: Influence of Platinum as a Functional Co-catalyst , 2002 .

[49]  R. Asahi,et al.  Visible-Light Photocatalysis in Nitrogen-Doped Titanium Oxides , 2001, Science.

[50]  F. Caruso,et al.  Magnetic Nanocomposite Particles and Hollow Spheres Constructed by a Sequential Layering Approach , 2001 .

[51]  K. Sakurai,et al.  Novel Vesicular Aggregates of Crown-Appended Cholesterol Derivatives Which Act as Gelators of Organic Solvents and as Templates for Silica Transcription , 2000 .

[52]  Göltner.  Porous Solids from Rigid Colloidal Templates: Morphogenesis. , 1999, Angewandte Chemie.

[53]  T. Pinnavaia,et al.  Textural Mesoporosity and the Catalytic Activity of Mesoporous Molecular Sieves with Wormhole Framework Structures , 1999 .

[54]  Arthur J. Olson,et al.  Development of a New Type of Protease Inhibitors, Efficacious against FIV and HIV Variants , 1999 .

[55]  G. Mairesse,et al.  Oxide ion conductivity in Bi2W1−xMExO6−x/2 (ME = Nb, Ta) , 1996 .

[56]  S. Martin,et al.  Environmental Applications of Semiconductor Photocatalysis , 1995 .

[57]  Detlef W. Bahnemann,et al.  Preparation and characterization of quantum-size titanium dioxide , 1988 .

[58]  Michael A. Butler,et al.  Photoelectrolysis and physical properties of the semiconducting electrode WO2 , 1977 .