Study of the magnetite to maghemite transition using microwave permittivity and permeability measurements

The microwave cavity perturbation (MCP) technique is used to identify the transition from magnetite (Fe3O4) to the meta-stable form of maghemite (γ-Fe2O3). In this study Fe3O4 was annealed at temperatures from 60 to 300 °C to vary the oxidation. Subsequent to annealing, the complex permittivity and magnetic permeability of the iron oxide powders were measured. The transition to γ-Fe2O3 was corroborated with x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS) and vibrating sample magnetometry (VSM). XRD, XPS and VSM implied that the starting powder was consistent with Fe3O4 and the powders annealed at more than 200 °C were transitioning to γ-Fe2O3. The MCP measurements gave large differences in both complex permittivity and magnetic permeability of the two phases in the frequency range of 2.5-10.2 GHz. Magnetic permeability decreased with annealing temperature, though magnetic losses showed frequency dependent behaviour. Complex permittivity measurements showed a large decrease in both dielectric constant and losses at all measurement frequencies, as well as a prominent loss peak centred around the phase transition temperatures. We interpret the loss peak as being a consequence of field effects due to an intermediate multi-phase mixture. Additionally, almost no frequency dependence was observed. The reduction in complex permittivity implies that the Feoct(2+) cations in the lattice provide a significant contribution to polarization at microwave frequencies and the effects of Feoct(3+) are nominal in comparison.. The change in loss can be explained as a combination of the differences in the effective conductivity of the two phases (i.e. Fe3O4 exhibits electron-hopping conduction whereas the presence of vacancies in γ-Fe2O3 nullifies this). This shows that the non-invasive MCP measurements serve as a highly sensitive and versatile method for looking at this phase transition in iron and potentially the effects of oxidation states on the polarization in other iron oxides.

[1]  Magnetic resonance in iron oxide nanoparticles: Quantum features and effect of size , 2007, 0711.0168.

[2]  K. Roh,et al.  A new method for the identification and quantification of magnetite-maghemite mixture using conventional X-ray diffraction technique. , 2012, Talanta.

[3]  K. Gross,et al.  Characterization of Magnetite and Maghemite for Hyperthermia in Cancer Therapy , 2003 .

[4]  A. Porch,et al.  Microwave complex permeability of magnetite using non-demagnetising and demagnetising cavity modes , 2014, 2014 44th European Microwave Conference.

[5]  W. F. Stuart.  Methods in Rock Magnetism and Palaeomagnetism Techniques and Instrumentation , 1983 .

[6]  Q. Pankhurst,et al.  Applications of magnetic nanoparticles in biomedicine , 2003 .

[7]  H. Allen,et al.  Vibrational Spectroscopic Characterization of Hematite, Maghemite, and Magnetite Thin Films Produced by Vapor Deposition , 2010 .

[8]  A. Morrish,et al.  MAGNETITE TO MAGHEMITE TRANSFORMATION IN ULTRAFINE PARTICLES , 1977 .

[9]  Y. Javadzadeh,et al.  Recent Advances in Novel Drug Carrier Systems , 2012 .

[10]  Yu Zhang,et al.  Size dependence of specific power absorption of Fe3O4 particles in AC magnetic field , 2004 .

[11]  R. Kopp,et al.  Ferromagnetic resonance and low-temperature magnetic tests for biogenic magnetite , 2004 .

[12]  Lina Wu,et al.  Magnetite Nanocrystals on Multiwalled Carbon Nanotubes as a Synergistic Microwave Absorber , 2013 .

[13]  Ricardo Grau-Crespo,et al.  Vacancy ordering and electronic structure of γ-Fe2O3 (maghemite): a theoretical investigation , 2010, Journal of physics. Condensed matter : an Institute of Physics journal.

[14]  J. Torrent,et al.  Evidence for a simple pathway to maghemite in Earth and Mars soils , 2002 .

[15]  G. Hearne,et al.  Pressure response of vacancy ordered maghemite (γ-Fe2O3) and high pressure transformed hematite (α-Fe2O3) , 2012 .

[16]  Mingyuan Gao,et al.  One‐Pot Reaction to Synthesize Biocompatible Magnetite Nanoparticles , 2005 .

[17]  G. Burns,et al.  Infrared- and Raman-active phonons of magnetite, maghemite, and hematite: a computer simulation and spectroscopic study. , 2005, The journal of physical chemistry. B.

[18]  D. Morgan,et al.  Spin state of iron in Fe3O4 magnetite and h-Fe3O4 , 2013 .

[19]  Sebastiano D'Amico,et al.  Earthquake Research and Analysis - Seismology, Seismotectonic and Earthquake Geology , 2012 .

[20]  T. Swaddle,et al.  Kinetics of the magnetite–maghemite–hematite transformation, with special reference to hydrothermal systems , 1980 .

[21]  Soumen Mandal,et al.  Microwave determination of sp2 carbon fraction in nanodiamond powders , 2015 .

[22]  P Lunkenheimer,et al.  Response of disordered matter to electromagnetic fields. , 2003, Physical review letters.

[23]  Dalva Lúcia Araújo de Faria,et al.  Raman microspectroscopy of some iron oxides and oxyhydroxides , 1997 .

[24]  Sahrim Ahmad,et al.  Magnetic and microwave absorbing properties of magnetite-thermoplastic natural rubber nanocomposites , 2010 .

[25]  T. Fukuchi.  ESR Techniques for the Detection of Seismic Frictional Heat , 2012 .

[26]  M. A. Gilleo.  Superexchange Interaction Energy for Fe3+-O2--Fe3+ Linkages , 1958 .

[27]  A. Rosencwaig.  Double exchange and electron hopping in magnetite , 1969 .

[28]  L. A. García-Cerda,et al.  Synthesis and characterization of maghemite nanoparticles for hyperthermia applications , 2015 .

[29]  G. C. Allen,et al.  X-Ray photoelectron spectroscopy of iron–oxygen systems , 1974 .

[30]  Christine C. Dantas,et al.  Dependence of microwave absorption properties on ferrite volume fraction in MnZn ferrite/rubber radar absorbing materials , 2011, 1105.5969.

[31]  M. Dekkers,et al.  The lepidocrocite–maghemite–haematite reaction chain—I. Acquisition of chemical remanent magnetization by maghemite, its magnetic properties and thermal stability , 2005 .

[32]  A. K. Jonscher,et al.  The ‘universal’ dielectric response , 1977, Nature.

[33]  A. Dinesen,et al.  The Thermal Conversion of Lepidocrocite (γ-FeOOH) Revisited , 2001 .

[34]  C. Serna,et al.  Maghemite (γ-Fe2O3): A Versatile Magnetic Colloidal Material , 2004 .

[35]  Huifang Xu,et al.  Characteristics and genesis of maghemite in Chinese loess and paleosols: Mechanism for magnetic susceptibility enhancement in paleosols , 2005 .

[36]  J. Zussman,et al.  Non-silicates : oxides, hydroxides and sulphides , 2011 .

[37]  Hui‐Ming Cheng,et al.  Microwave Electromagnetic Characteristics of a Microcoiled Carbon Fibers/paraffin Wax Composite in Ku Band , 2002 .

[38]  M. Aggag,et al.  Magnetic nanoparticle-induced hyperthermia treatment under magnetic resonance imaging. , 2011, Magnetic resonance imaging.

[39]  Ben Zhong Tang,et al.  Processible Nanostructured Materials with Electrical Conductivity and Magnetic Susceptibility: Preparation and Properties of Maghemite/Polyaniline Nanocomposite Films , 1999 .

[40]  O. Shebanova,et al.  Raman study of magnetite (Fe3O4): laser‐induced thermal effects and oxidation , 2003 .