Investigation of White Layers Formed in Conventional and Cryogenic Hard Turning of Steels

Although hard turning of steels has become an accepted industrial practice reducing the extent of grinding, many surface integrity aspects of hard turning require clarification. The striking result of hard turning is the tendency for forming white (non-etching) and dark (overtempered) layers at machined surface. White layers are often associated with residual tensile stresses leading to reduced fatigue strength and poor wear resistance. It has been reported that certain steel compositions, machining conditions, and tools enhance white layers, but no consensus was reached on the nature of white layer and the role of environmental factors. This study examines the impact of cryogenic, liquid nitrogen spray cooling, tool and work materials, as well as machining speed on white layer formation. Results are evaluated using XRD, SEM, EDS, AES, residual stress measurement and microhardness profiling. It is concluded that white layers are a purely thermomechanical phenomenon involving dissolution of lowalloy carbides into austenitic matrix, and catastrophic flow of that 1phase material resulting in its nano-scale refinement. The depth and extent of the refinement are controlled by cooling, with the cryogenic nitrogen reducing white layer thickness, loss of hardness, and improving residual stress distribution.

[1]  W. König,et al.  Residual Stresses — Measurement and Causes in Machining Processes , 1982 .

[2]  W. Konig,et al.  Machining hard materials with geometrically defined cutting edges , 1990 .

[3]  W. König,et al.  Turning versus grinding: a comparison of surface integrity aspects and attainable accuracies , 1993 .

[4]  W. Konig,et al.  Top-quality components not only by grinding , 1994 .

[5]  M. C. Shaw,et al.  Heat-Affected Zones in Grinding Steel , 1994 .

[6]  Z. Y. Wang,et al.  Cryogenic PCBN turning of ceramic (Si3N4) , 1996 .

[7]  Zhao Xingzhong,et al.  Wear mechanisms of Ti(C, N) ceramic in sliding contact with stainless steel , 1997 .

[8]  Christopher J. Evans,et al.  White Layers and Thermal Modeling of Hard Turned Surfaces , 1997, Manufacturing Science and Engineering: Volume 2.

[9]  Christopher J. Evans,et al.  Finish Hard Turning of Powder Metallurgy M50 Steel | NIST , 1997 .

[10]  Z. Y. Wang,et al.  Wear of CBN tool in turning of silicon nitride with cryogenic cooling , 1997 .

[11]  M. A. Fleming,et al.  PCBN HARD TURNING AND WORKPIECE SURFACE INTEGRITY , 1998 .

[12]  Y. K. Chou,et al.  Process Effects on White Layer Formation in Hard Turning | NIST , 1998 .

[13]  Turning and Grinding of Hard Alloys , 1999 .

[14]  Fukuo Hashimoto,et al.  Surface Integrity Generated by Precision Hard Turning , 1999 .

[15]  Shreyes N. Melkote,et al.  Effect of Cutting-Edge Geometry and Workpiece Hardness on Surface Residual Stresses in Finish Hard Turning of AISI 52100 Steel , 1999, Manufacturing Science and Engineering.

[16]  Shane Y. Hong,et al.  Economical and ecological cryogenic machining of AISI 304 austenitic stainless steel , 2000 .

[17]  Shreyes N. Melkote,et al.  Effect of Tool Edge Geometry on Workpiece Subsurface Deformation and Through-Thickness Residual Stresses for Hard Turning of AISI 52100 Steel , 2000 .

[18]  Z. Y. Wang,et al.  Cryogenic machining of hard-to-cut materials , 2000 .

[19]  C. Richard Liu,et al.  Experimental study on the performance of superfinish hard turned surfaces in rolling contact , 2000 .

[20]  N. R. Dhar,et al.  The influence of cryogenic cooling on tool wear, dimensional accuracy and surface finish in turning AISI 1040 and E4340C steels , 2001 .

[21]  N. R. Dhar,et al.  Beneficial effects of cryogenic cooling over dry and wet machining on tool wear and surface finish in turning AISI 1060 steel , 2001 .

[22]  R. Valiev,et al.  Nanostructure Formation and Mechanical Alloying in the Wheel/Rail Contact Area of High Speed Trains in Comparison with Other Synthesis Routes , 2001 .

[23]  R. Valiev,et al.  Nanostructure Formation and Mechanical Alloying in the Wheel/Rail Contact Area of High Speed Trains in Comparison with Other Synthesis Routes , 2001 .

[24]  Shane Y. Hong,et al.  Cooling approaches and cutting temperatures in cryogenic machining of Ti-6Al-4V , 2001 .

[25]  Mohamed A. Elbestawi,et al.  HIGH STRAIN RATE SHEAR EVALUATION AND CHARACTERIZATION OF AISI D2 TOOL STEEL IN ITS HARDENED STATE , 2001 .

[26]  K. Tsuchiya,et al.  Formation of Nanocrystalline Ferrite through Rolling and Ball Milling , 2001 .

[27]  Shane Y. Hong,et al.  New cooling approach and tool life improvement in cryogenic machining of titanium alloy Ti-6Al-4V , 2001 .

[28]  T. I. El-Wardany,et al.  PHYSICS-BASED SIMULATION OF HIGH SPEED MACHINING , 2002 .

[29]  N. R. Dhar,et al.  The effects of cryogenic cooling on chips and cutting forces in turning AISI 1040 and AISI 4320 steels , 2002 .

[30]  T. Kurfess,et al.  TOOL LIFE, WEAR RATES, AND SURFACE QUALITY IN HARD TURNING , 2002 .

[31]  Y. Kevin Chou,et al.  Surface hardening of AISI 4340 steel by machining: a preliminary investigation , 2002 .

[32]  G. Byrne,et al.  Chip Formation, Acoustic Emission and Surface White Layers in Hard Machining , 2002 .

[33]  A. Hamrol,et al.  Turning and grinding as a source of microstructural changes in the surface layer of hardened steel , 2003 .

[34]  R. Ghosh,et al.  Cryogenic Machining With Brittle Tools and Effects on Tool Life , 2003 .

[35]  Applications of Ceramic Cutting Tools in Machining of Hardness Material , 2005 .