Temperature and composition dependence of Young's modulus in polycrystalline B2 Ni−Al

Young's modulus (E) for ten specimens of ordered polycrystalline Ni-Al has been measured using PUCOT (Piezoelectric Ultrasonic Composite Oscillator Technique). The modulus has been determined in the composition range 43.94 to 52.70 atomic percent Al and temperature interval 300 to 1300 K. Anomalous dependence on composition and temperature has been found, where the modulus does not always decrease linearly with temperature and does not show the expected maximum near the stoichiometric composition. Nonetheless, these materials show remarkable stiffness, where the modulus clusters near 230 GPa at ambient temperature and decreases to about 180 GPa at 1300 K in this composition range.

A. Wolfenden | Harmouche

[1] A. Wolfenden,et al. Temperature and composition dependence of young's modulus for ordered B2 polycrystalline CoAl and FeAl , 1986 .

[2] E. Henig,et al. Influence of supersaturated thermal vacancies on the elastic constants of β2-NiAl , 1980 .

[3] H. Warlimont,et al. Young's modulus of β2‐NiAl alloys , 1979 .

[4] H. Warlimont,et al. The elastic behaviour of β2-NiAl alloys , 1977 .

[5] A. Wolfenden,et al. Mechanical damping in leaded and in lead-free alpha brass , 1977 .

[6] W. Robinson,et al. The Piezoelectric Method of Determining Mechanical Damping at Frequencies of 30 to 200 KHz , 1974, IEEE Transactions on Sonics and Ultrasonics.