A new electrochemically graded hydroxyapatite coating for osteosynthetic implants promotes implant osteointegration in a rat model.

Hydroxyapatite (HAP) is widely used as an osteoconductive coating for orthopedic implants. So far standard coating methods like plasma spraying produce a relatively thick coating layer (>30 microm). In addition, the chemical structure of the HAP may be altered because of the heating throughout the coating process. This may have negative effects on the coating stability, implant fixation, and induction of bone formation. The relatively thick layer may detach from the implant with the risk of wear debris. In the present study the potential of a newly developed HAP coating of implants on osteointegration was investigated in a rat model. The coating method, based on an electrochemical process, is applied in a graded manner and results in a biodegradable HAP coating with a thickness of approximately 2 mum. Coated versus uncoated titanium Kirschner wires (1.4-mm diameter) were inserted into the medullary cavity of the right femora of 5-month old female Sprague Dawley rats (n=36) in a retrograde fashion. Throughout an experimental period of 2 months the osteointegration was traced radiologically. After this time the animals were sacrificed and the implant integration was tested biomechanically with the use of a push-out test. To analyze the bone-implant interface, histological sections (80 mum) were investigated with an image analyzing system. The biomechanical testing revealed a significantly higher implant fixation in the group treated with the HAP-coated implant (shear strength: 27.8 +/- 6.7 MPa) compared to control (shear strength: 8.08 +/- 3.4 MPa). The histological analyses demonstrated a better ingrowth of the implants in the HAP group with significantly more direct bone-implant contacts compared to the control group. The results demonstrate that the HAP coating promotes implant osteointegration in a rat model.

[1]  D. Mao,et al.  Mechanical and histological evaluations of hydroxyapatite-coated and noncoated Ti6Al4V implants in tibia bone. , 2001, Journal of biomedical materials research.

[2]  W R Walsh,et al.  Morphometric and mechanical evaluation of titanium implant integration: comparison of five surface structures. , 2000, Journal of biomedical materials research.

[3]  D. Puleo,et al.  Understanding and controlling the bone-implant interface. , 1999, Biomaterials.

[4]  T. Bauer,et al.  The pathology of total joint arthroplasty , 1999, Skeletal Radiology.

[5]  K. Hayashi,et al.  The effect of hydroxyapatite coating on the bonding of bone to titanium implants in the femora of ovariectomised rats. , 1999, The Journal of bone and joint surgery. British volume.

[6]  C. Bünger,et al.  Improved bone anchorage of hydroxypatite coated implants compared with tricalcium-phosphate coated implants in trabecular bone in dogs. , 1999, Biomaterials.

[7]  W. Capello,et al.  Hydroxyapatite in Total Hip Arthroplasty: Clinical Results and Critical Issues , 1998, Clinical orthopaedics and related research.

[8]  T. Nishida,et al.  Comparison of osseointegration between hydroxyapatite-coated and uncoated threaded titanium dental implants placed into surgically-created bone defect in rabbit tibia. , 1998, Journal of oral science.

[9]  B. C. Wang,et al.  In vitro and in vivo mechanical evaluations of plasma-sprayed hydroxyapatite coatings on titanium implants: the effect of coating characteristics. , 1997, Journal of biomedical materials research.

[10]  D. Brunette,et al.  The effects of micromachined surfaces on formation of bonelike tissue on subcutaneous implants as assessed by radiography and computer image processing. , 1997, Journal of biomedical materials research.

[11]  D. Scott,et al.  Current Concepts Review - Total Hip Arthroplasty with Hydroxyapatite-Coated Prostheses* , 1996 .

[12]  C. Berndt,et al.  Structural changes of thermally sprayed hydroxyapatite investigated by Rietveld analysis. , 1996, Biomaterials.

[13]  D. Scott,et al.  Total hip arthroplasty with hydroxyapatite-coated prostheses. , 1996, The Journal of bone and joint surgery. American volume.

[14]  U. Pazzaglia,et al.  Thermal behaviour of hydroxyapatite intended for medical applications. , 1993, Biomaterials.

[15]  R. Bloebaum,et al.  Osteolysis from a press-fit hydroxyapatite-coated implant. A case study. , 1993, The Journal of arthroplasty.

[16]  P. Marquis,et al.  Effect of heat treatment on the microstructure of plasma-sprayed hydroxyapatite coating. , 1993, Biomaterials.

[17]  C. Klein,et al.  Plasma sprayed coatings of hydroxylapatite. , 1987, Journal of biomedical materials research.

[18]  P. Ducheyne,et al.  Effect of hydroxyapatite impregnation on skeletal bonding of porous coated implants. , 1980, Journal of biomedical materials research.