Effect of ultraviolet/ozone treatment on the surface and bulk properties of poly(dimethyl siloxane) and poly(vinylmethyl siloxane) networks

Abstract We present a comparative study aiming at comprehending the effect of ultraviolet/ozone treatment on the modification of poly(dimethyl siloxane) (PDMS) and poly(vinylmethyl siloxane) (PVMS) silicone elastomers networks (SENs). Both PDMS and PVMS SENs undergo dramatic changes in their properties when exposed to UVO. The surface chemical composition of both PDMS and PVMS at long UVO treatment times changes substantially and features a high density of hydrophilic groups. There are two major differences in behavior in the two classes of materials. First, relative to PDMS, the PVMS-based SENs get modified throughout the entire bulk. Second, the physico-chemical changes detected in PVMS take place on much shorter time scale relative to PDMS. These results are in accord with our earlier reports that indicated that when exposed to UVO, the topmost ≈5 nm of PDMS gets converted into a silica-like material, which then acts as a barrier for diffusion of atomic oxygen. In this case, the bulk of PDMS maintains its elasticity. In contrast, both the surface and bulk of PVMS films undergo substantial changes in properties when exposed to UVO. First, the surface modification of PVMS SENs takes place after only a few seconds of the UVO treatment. In addition, we register substantial modification of bulk properties, including the complete densification accompanied with increased bulk modulus. Likely, the susceptibility of the vinyl bonds to radical reactions is responsible for this effect.

[1]  R. Spontak,et al.  Extended Chemical CrossLinking of a Thermoplastic Polyimide: Macroscopic and Microscopic Property Development , 2008 .

[2]  M. Chaudhury,et al.  Modeling hydrophobic recovery of electrically discharged polydimethylsiloxane elastomers. , 2006, Journal of colloid and interface science.

[3]  Tor Orbeck,et al.  The mechanisms of hydrophobic recovery of polydimethylsiloxane elastomers exposed to partial electrical discharges , 2001 .

[4]  S. Kumagai,et al.  Electrical and environmental aging of silicone rubber used in outdoor insulation , 1999, IEEE Transactions on Dielectrics and Electrical Insulation.

[5]  J. Genzer,et al.  Poly(vinylmethylsiloxane) elastomer networks as functional materials for cell adhesion and migration studies. , 2011, Biomacromolecules.

[6]  George M. Whitesides,et al.  Ordering of Spontaneously Formed Buckles on Planar Surfaces , 2000 .

[7]  Ulf W. Gedde,et al.  Hydrophobicity Recovery of Polydimethylsiloxane after Exposure to Corona Discharges , 1998 .

[8]  A. Mata,et al.  Characterization of Polydimethylsiloxane (PDMS) Properties for Biomedical Micro/Nanosystems , 2005, Biomedical microdevices.

[9]  J. A. Crowe,et al.  Rapid formation of soft hydrophilic silicone elastomer surfaces , 2005 .

[10]  H. Hillborg,et al.  Hydrophobicity changes in silicone rubbers , 1999, IEEE Transactions on Dielectrics and Electrical Insulation.

[11]  J. Hill,et al.  A comparison of gas-phase methods of modifying polymer surfaces , 1995 .

[12]  S. Krause,et al.  Properties of dimethylsiloxane microphases in phase-separated dimethylsiloxane block copolymers , 1987 .

[13]  M. Strobel,et al.  Analysis of air-corona-treated polypropylene and poly(ethylene terephthalate) films by contact-angle measurements and X-ray photoelectron spectroscopy , 1992 .

[14]  Michael J. Owen,et al.  Hydrophobic Recovery of Polydimethylsiloxane Elastomer Exposed to Partial Electrical Discharge , 2000 .

[15]  J. Genzer,et al.  Photochromic materials with tunable color and mechanical flexibility , 2011 .

[16]  M. Chaudhury,et al.  Hydrophobicity loss and recovery of silicone HV insulation , 1999, IEEE Transactions on Dielectrics and Electrical Insulation.

[17]  M. Owen,et al.  Hydrophobic Recovery of Plasma-Treated Polydimethylsiloxane , 1995 .

[18]  J. Helmer,et al.  Supercooling of polydimethylsiloxane , 1969 .

[19]  J. Koberstein,et al.  UV–ozone induced growth of a SiOx surface layer on a cross-linked polysiloxane film: characterization and gas separation properties , 2000 .

[20]  J. Genzer,et al.  Surface modification of Sylgard-184 poly(dimethyl siloxane) networks by ultraviolet and ultraviolet/ozone treatment. , 2002, Journal of colloid and interface science.

[21]  T. Cosgrove,et al.  NMR Spin−Spin Relaxation Studies of Silicate-Filled Low Molecular Weight Poly(dimethylsiloxane)s , 2002 .

[22]  J. Genzer,et al.  Formation of silicone elastomer networks films with gradients in modulus , 2010 .

[23]  J. E. Mark,et al.  Effect of network chain length distribution and in situ precipitated silica on the low-temperature behaviour of poly(dimethylsiloxane) model networks , 1988 .

[24]  P. Mallon,et al.  Tracking the hydrophobicity recovery of PDMS compounds using the adhesive force determined by AFM force distance measurements , 2005 .

[25]  R. Hackam Outdoor HV composite polymeric insulators , 1999, IEEE Transactions on Dielectrics and Electrical Insulation.

[26]  Grant D. Smith,et al.  Crosslinked polydimethylsiloxane exposed to oxygen plasma studied by neutron reflectometry and other surface specific techniques , 2000 .

[27]  Jeffrey T. Koberstein,et al.  Conversion of Some Siloxane Polymers to Silicon Oxide by UV/Ozone Photochemical Processes , 2000 .

[28]  E. Thomas,et al.  Robust block copolymer mask for nanopatterning polymer films. , 2010, ACS nano.