Determining Stress in Metallic Conducting Layers of Microelectronics Devices Using High Resolution Electron Backscatter Diffraction and Finite Element Analysis

Delayed failure due to stress voiding is a concern with some aging microelectronics, as these voids can grow large enough to cause an open circuit. Local measurements of stress in the metallic layers are crucial to understanding and predicting this failure, but such measurements are complicated by the fact that exposing the aluminum conducting lines will relieve most of their stress. In this study, we instead mechanically thin the device substrate and measure distortions on the thinned surface using high resolution electron backscatter diffraction (HREBSD). These measurements are then related to the stresses in the metallic layers through elastic simulations. This study found that in legacy components that had no obvious voids, the stresses were comparable to the theoretical stresses at the time of manufacture (≈300 MPa). Distortion fields in the substrate were also determined around known voids, which may be directly compared to stress voiding models. The technique presented here for stress determination, HREBSD coupled with finite element analysis to infer subsurface stresses, is a valuable tool for assessing failure in layered microelectronics devices.

[1]  J. Fundenberger,et al.  Characterization of a nanopipe dislocation in GaN by means of HR-EBSD and field dislocation mechanics analysis , 2022, Materials Characterization.

[2]  C. B. Carter,et al.  Identification of Star Defects in Gallium Nitride with HREBSD and ECCI , 2021, Microscopy and Microanalysis.

[3]  Patrick E. Leser,et al.  A digital twin feasibility study (Part I): Non-deterministic predictions of fatigue life in aluminum alloy 7075-T651 using a microstructure-based multi-scale model , 2020 .

[4]  James E. Warner,et al.  A digital twin feasibility study (Part II): Non-deterministic predictions of fatigue life using in-situ diagnostics and prognostics , 2020, Engineering Fracture Mechanics.

[5]  B. E. Dunlap,et al.  Correlating results from high resolution EBSD with TEM- and ECCI-based dislocation microscopy: Approaching single dislocation sensitivity via noise reduction. , 2019, Ultramicroscopy.

[6]  S. Roux,et al.  Estimation of elastic strain by integrated image correlation on electron diffraction patterns. , 2019, Ultramicroscopy.

[7]  J. Hochhalter,et al.  New levels of high angular resolution EBSD performance via inverse compositional Gauss-Newton based digital image correlation. , 2018, Ultramicroscopy.

[8]  J. Hoefnagels,et al.  A consistent full-field integrated DIC framework for HR-EBSD. , 2018, Ultramicroscopy.

[9]  R. Cook,et al.  Strain Mapping Using EBSD Cross Correlation and Raman Methods , 2018, Microscopy and Microanalysis.

[10]  T. Book,et al.  Identifying strain localization and dislocation processes in fatigued Inconel 718 manufactured from selective laser melting , 2018 .

[11]  W. Osborn,et al.  In-situ elastic strain mapping during micromechanical testing using EBSD. , 2018, Ultramicroscopy.

[12]  Marc De Graef,et al.  Error analysis of the crystal orientations obtained by the dictionary approach to EBSD indexing. , 2017, Ultramicroscopy.

[13]  S. F. Li,et al.  Crystal Plasticity Model Validation Using Combined High-Energy Diffraction Microscopy Data for a Ti-7Al Specimen , 2017, Metallurgical and Materials Transactions A.

[14]  R. H. Wagoner,et al.  Performance of Dynamically Simulated Reference Patterns for Cross-Correlation Electron Backscatter Diffraction , 2016, Microscopy and Microanalysis.

[15]  D. Fullwood,et al.  The effect of length scale on the determination of geometrically necessary dislocations via EBSD continuum dislocation microscopy. , 2016, Ultramicroscopy.

[16]  D. Fullwood,et al.  Analysis of traction‐free assumption in high‐resolution EBSD measurements , 2015, Journal of microscopy.

[17]  M. Vaudin,et al.  Validation of kinematically simulated pattern HR-EBSD for measuring absolute strains and lattice tetragonality , 2015 .

[18]  A. Wilkinson,et al.  The effect of pattern overlap on the accuracy of high resolution electron backscatter diffraction measurements. , 2015, Ultramicroscopy.

[19]  D. Raabe,et al.  Error analysis of the crystal orientations and disorientations obtained by the classical electron backscatter diffraction technique , 2015 .

[20]  Gavin D. R. Hall,et al.  An evaluation of accelerated failure time models of stress-migration and stress-induced voiding failures under vias , 2015, 2015 IEEE International Reliability Physics Symposium.

[21]  B. Shollock,et al.  Crystal plasticity and high-resolution electron backscatter diffraction analysis of full-field polycrystal Ni superalloy strains and rotations under thermal loading , 2014 .

[22]  D. Allman,et al.  On the distribution of stress-induced voiding failures under vias , 2014, 2014 IEEE International Reliability Physics Symposium.

[23]  C. Okoro,et al.  Nondestructive Measurement of the Residual Stresses in Copper Through-Silicon Vias Using Synchrotron-Based Microbeam X-Ray Diffraction , 2014, IEEE Transactions on Electron Devices.

[24]  Jon Alkorta,et al.  Limits of simulation based high resolution EBSD. , 2013, Ultramicroscopy.

[25]  John A. Basinger,et al.  Precision of EBSD based Orientation Measurements , 2011, Microscopy and Microanalysis.

[26]  A. Wilkinson,et al.  The effect of crystal orientation on the indentation response of commercially pure titanium: experiments and simulations , 2010, Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences.

[27]  D. Fullwood,et al.  Bragg's Law diffraction simulations for electron backscatter diffraction analysis. , 2009, Ultramicroscopy.

[28]  Paul A. Flinn,et al.  Direct observation of the growth and movement of electromigration voids under passivation , 2008 .

[29]  S. Orain,et al.  FEM-based method to determine mechanical stress evolution during process flow in microelectronics. Application to stress-voiding , 2004, 5th International Conference on Thermal and Mechanical Simulation and Experiments in Microelectronics and Microsystems, 2004. EuroSimE 2004. Proceedings of the.

[30]  M. Bruce,et al.  ABCs of Photon Emission Microscopy , 2003, EDFA Technical Articles.

[31]  S. Greco,et al.  Stress voiding in wide copper lines , 2002 .

[32]  A. Fischer,et al.  Stress-induced voiding in aluminum and copper interconnects , 2002 .

[33]  R. Keller,et al.  Local crystallography and stress voiding in Al-Si-Cu versus copper interconnects , 1999 .

[34]  Kim Y. Lee,et al.  Electromigration and stress-induced voiding in fine Al and Al-alloy thin-film lines , 1995, IBM J. Res. Dev..

[35]  F. G. Yost,et al.  Voiding due to thermal stress in narrow conductor lines , 1989 .

[36]  T. Ruggles,et al.  Characterizing Defect Structures in Am Steel Using Direct Electron Detection EBSD , 2022, SSRN Electronic Journal.

[37]  J. Kysar,et al.  Resolving geometrically necessary dislocation density onto individual dislocation types using EBSD-based continuum dislocation microscopy , 2016 .

[38]  A. D. Romig,et al.  Stress-driven diffusive voiding of aluminum conductor lines , 1989, 27th Annual Proceedings., International Reliability Physics Symposium.