4D in situ visualization of electrode morphology changes during accelerated degradation in fuel cells by X-ray computed tomography

Abstract A four-dimensional visualization approach, featuring three dimensions in space and one dimension in time, is proposed to study local electrode degradation effects during voltage cycling in fuel cells. Non-invasive in situ micro X-ray computed tomography (XCT) with a custom fuel cell fixture is utilized to track the same cathode catalyst layer domain throughout various degradation times from beginning-of-life (BOL) to end-of-life (EOL). With this unique approach, new information regarding damage features and trends are revealed, including crack propagation and catalyst layer thinning being quantified by means of image processing and analysis methods. Degradation heterogeneities as a result of local environmental variations under land and channel are also explored, with a higher structural degradation rate under channels being observed. Density and compositional changes resulting from carbon corrosion and catalyst layer collapse and thinning are observed by changes in relative X-ray attenuation from BOL to EOL, which also indicate possible vulnerable regions where crack initiation and propagation may occur. Electrochemical diagnostics and morphological features observed by micro-XCT are correlated by additionally collecting effective catalyst surface area, double layer capacitance, and polarization curves prior to imaging at various stages of degradation.

[1]  Volker Schmidt,et al.  Three-dimensional study of compressed gas diffusion layers using synchrotron X-ray imaging , 2014 .

[2]  John Banhart,et al.  Synchrotron X-ray tomography for investigations of water distribution in polymer electrolyte membrane fuel cells , 2011 .

[3]  Kateryna Artyushkova,et al.  Effects of Cathode Corrosion on Through-Plane Water Transport in Proton Exchange Membrane Fuel Cells. , 2013, Journal of the Electrochemical Society.

[4]  G. Janssen,et al.  Imaging of membrane electrode assemblies of proton exchange membrane fuel cells by X-ray computed tomography , 2011 .

[5]  R. White,et al.  3D Printed Flow Field and Fixture for Visualization of Water Distribution in Fuel Cells by X-ray Computed Tomography , 2016 .

[6]  W. Tang,et al.  Investigation of dynamic driving cycle effect on the degradation of proton exchange membrane fuel cell by segmented cell technology , 2014 .

[7]  A. Hitchcock,et al.  Carbon corrosion of proton exchange membrane fuel cell catalyst layers studied by scanning transmission X-ray microscopy , 2014 .

[8]  Erik Kjeang,et al.  Membrane degradation during combined chemical and mechanical accelerated stress testing of polymer electrolyte fuel cells , 2014 .

[9]  S. Hirai,et al.  Oblique Soft X-Ray Tomography as a Non-Destructive Method for Morphology Diagnostics in Degradation of Proton-Exchange Membrane Fuel Cell , 2014 .

[10]  A. Wokaun,et al.  Local Catalyst Support Degradation during Polymer Electrolyte Fuel Cell Start-Up and Shutdown , 2012 .

[11]  Ingo Manke,et al.  3D Imaging of Catalyst Support Corrosion in Polymer Electrolyte Fuel Cells , 2011 .

[12]  K. Beccu,et al.  Abschätzung der porenstruktur poröser elektroden aus impedanzmessungen , 1976 .

[13]  F. Büchi,et al.  Effects of Synchrotron Radiation on Fuel Cell Materials , 2011 .

[14]  H. Gasteiger,et al.  Review—Electromobility: Batteries or Fuel Cells? , 2015 .

[15]  Robert P. Dougherty,et al.  Computing Local Thickness of 3D Structures with ImageJ , 2007, Microscopy and Microanalysis.

[16]  F. Marone,et al.  Progress in In Situ X-Ray Tomographic Microscopy of Liquid Water in Gas Diffusion Layers of PEFC , 2011 .

[17]  David Harvey,et al.  A Semi-Empirical Two Step Carbon Corrosion Reaction Model in PEM Fuel Cells , 2013 .

[18]  Laetitia Dubau,et al.  Degradation heterogeneities induced by repetitive start/stop events in proton exchange membrane fuel cell: Inlet vs. outlet and channel vs. land , 2013 .

[19]  Erik Kjeang,et al.  Three-dimensional phase segregation of micro-porous layers for fuel cells by nano-scale X-ray computed tomography , 2016 .

[20]  M. Kim,et al.  Phase-change-related degradation of catalyst layers in proton-exchange-membrane fuel cells , 2013 .

[21]  Takashi Sasabe,et al.  Effects of polytetrafluoroethylene treatment and compression on gas diffusion layer microstructure using high-resolution X-ray computed tomography , 2014 .

[22]  E. Kjeang,et al.  Water sorption and expansion of an ionomer membrane constrained by fuel cell electrodes , 2015 .

[23]  S. Knights,et al.  Effect of catalyst layer defects on local membrane degradation in polymer electrolyte fuel cells , 2016 .

[24]  Kwok-Wing Chau,et al.  A new image thresholding method based on Gaussian mixture model , 2008, Appl. Math. Comput..

[25]  E. Kjeang,et al.  Stochastic microstructural modeling of fuel cell gas diffusion layers and numerical determination of transport properties in different liquid water saturation levels , 2016 .

[26]  R. Borup,et al.  Influence of the microporous layer on carbon corrosion in the catalyst layer of a polymer electrolyte membrane fuel cell , 2012 .

[27]  Mark K. Debe,et al.  Electrocatalyst approaches and challenges for automotive fuel cells , 2012, Nature.

[28]  E. Gyenge,et al.  Characterizing the Structural Degradation in a PEMFC Cathode Catalyst Layer: Carbon Corrosion , 2009 .

[29]  R. White,et al.  Communication—Effect of Micro-XCT X-ray Exposure on the Performance of Polymer Electrolyte Fuel Cells , 2016 .

[30]  E. Kjeang,et al.  Failure analysis of fuel cell electrodes using three-dimensional multi-length scale X-ray computed tomography , 2016 .

[31]  Michael Fowler,et al.  Morphological features (defects) in fuel cell membrane electrode assemblies , 2006 .

[32]  E. Kjeang,et al.  3D visualization of membrane failures in fuel cells , 2017 .

[33]  Mathias Schulze,et al.  A review of platinum-based catalyst layer degradation in proton exchange membrane fuel cells , 2009 .

[34]  Adam Z. Weber,et al.  Probing water distribution in compressed fuel-cell gas-diffusion layers using X-ray computed tomography , 2015 .